Glass article

ABSTRACT

To provide a glass article suitable for a top plate for a cooker, in which a color tone of a colored layer is not impaired. A glass article is characterized by including a Li2O—Al2O3—SiO2-based crystallized glass sheet having lightness L* of 70 or greater, chromaticity a* of within ±5, and chromaticity b* of within ±5 at a thickness of 3 mm, and a colored layer formed on a back surface of the glass sheet.

TECHNICAL FIELD

The present invention relates to a glass article suitable for a top plate for a cooker.

BACKGROUND ART

A Li₂O—Al₂O₃—SiO₂-based crystallized glass substrate with a low thermal expansion coefficient is used for a top plate for a cooker such as an induction cooker, a radiant heater cooker, and a gas cooker (see Patent Literatures 1 to 3, for example). Such a glass substrate of a top plate for a cooker includes a cooking surface and a back surface located inside of the cooker.

The back surface of the glass substrate of the top plate for a cooker is generally formed with a colored layer for a purpose of improving the design and concealing a structure inside the cooker.

CITATION LIST Patent Literature

-   Patent Literature 1: JP 39-21049 B -   Patent Literature 2: JP 40-20182 B -   Patent Literature 3: JP 01-308845 A

SUMMARY OF INVENTION Technical Problem

However, the Li₂O—Al₂O₃—SiO₂-based crystallized glass is colored due to TiO₂, Fe₂O₃, and the like, and thus, there is a problem that a color tone of a colored layer is impaired, and as a result, the appearance of the top plate for a cooker is impaired.

An object of the present invention is to provide a glass article suitable for a top plate for a cooker, in which a color tone of a colored layer is not impaired.

Solution to Problem

A glass article of the present invention is characterized by including a Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet having lightness L* of 70 or greater, chromaticity a* of within ±5, and chromaticity b* of within ±5 at a thickness of 3 mm, and a colored layer formed on a back surface of the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet.

In the glass article of the present invention, the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet preferably includes, in mass %, SiO₂ from 40 to 90%, Al₂O₃ from 5 to 30%, Li₂O from 1 to 10%, TiO₂ 0 to less than 2%, SnO₂ from 0 to 20%, ZrO₂ from 1 to 20%, MgO from 0 to 10%, P₂O₅ from 0 to 10%, and Sb₂O₃+As₂O₃ from 0 to less than 2%.

In the glass article of the present invention, an appearance of the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet is preferably colorless and transparent.

In the glass article of the present invention, a transmittance at a thickness of 3 mm and a wavelength of 300 nm of the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet is preferably 10% or greater.

In the glass article of the present invention, the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet has a thermal expansion coefficient of 30×10⁻⁷/° C. or less at 30 to 380° C.

In the glass article of the present invention, the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet has a thermal expansion coefficient of 30×10⁻⁷/° C. or less at 30 to 750° C.

A top plate for a cooker of the present invention is characterized by including the glass article described above.

Advantageous Effects of Invention

According to the present invention, it is possible to provide a glass article suitable for a top plate for a cooker, in which a color tone of a colored layer is not impaired.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a schematic front cross-sectional view illustrating a glass article according to an embodiment of the present invention.

FIG. 2 shows measurement results of reflection chromaticity.

DESCRIPTION OF EMBODIMENTS

Preferred embodiments are described below. Note that the following embodiments are exemplary only, and the present invention is not limited to the following embodiments.

Glass Article 1

FIG. 1 is a schematic front cross-sectional view illustrating a glass article 1 according to an embodiment of the present invention. As illustrated in FIG. 1 , the glass article 1 includes a Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2, and a colored layer 3 formed on a back surface of the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2. The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 includes a cooking surface 2 a which is a main surface on one side, and a back surface 2 b which is a main surface on the other side. The cooking surface 2 a is a surface on which cookware such as a pot and a frying pan is placed. The back surface 2 b is a surface facing a heating device on an inner side of the cooker. Therefore, the cooking surface 2 a and the back surface 2 b are a front side and a back side, respectively.

Li₂O—Al₂O₃—SiO₂-Based Crystallized Glass Sheet 2

A Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably includes, in mass %, SiO₂ from 40 to 90%, Al₂O₃ from 5 to 30%, Li₂O from 1 to 10%, TiO₂ 0 to less than 2%, SnO₂ from 0 to 20%, ZrO₂ from 1 to 20%, MgO from 0 to 10%, P₂O₅ from 0 to 10%, and Sb₂O₃+As₂O₃ from 0 to less than 2%. Note that, in the description regarding the content of each component below, “%” means “mass %” unless otherwise indicated.

SiO₂ is a component that forms the skeleton of the glass and forms a Li₂O—Al₂O₃—SiO₂-based crystal. The content of SiO₂ is preferably from 40 to 90%, from 52 to 80%, from 55 to 75%, from 56 to 70%, from 59 to 70%, from 60 to 70%, from 60 to 69.5%, from 60.5 to 69.5%, from 61 to 69.5%, from 61.5 to 69.5%, from 62 to 69.5%, from 62.5 to 69.5%, from 63 to 69.5%, and in particular, from 63.5 to 69.5%. If the content of SiO₂ is excessively small, the thermal expansion coefficient tends to be high, and thus, it is difficult to produce crystallized glass having excellent thermal shock resistance. Further, the crystallized glass tends to have poor chemical durability. On the other hand, if the content of SiO₂ is excessively large, the meltability of the glass decreases and the viscosity of the glass melt increases. Thus, glass fining and glass forming becomes difficult, resulting in decrease in productivity. In addition, a time required for crystallization is increased, and the productivity easily decreases.

Al₂O₃ is a component that forms the skeleton of the glass and forms a Li₂O—Al₂O₃—SiO₂-based crystal. In addition, Al₂O₃ is a component that is located around a crystal nucleus and forms a core-shell structure. The presence of the core-shell structure makes it less likely to feed a crystal nucleus component from the outside of the shell, and thus, the crystal nuclei are less likely to be enlarged, and a large number of small crystal nuclei are easily formed. The content of Al₂O₃ is preferably from 5 to 30%, from 8 to 30%, from 9 to 28%, from 10 to 27%, from 12 to 27%, from 14 to 27%, from 16 to 27%, from 17 to 27%, from 18 to 27%, from 18 to 26.5%, from 18.1 to 26.5%, from 19 to 26.5%, from 19.5 to 26.5%, from 20 to 26.5%, from 20.5 to 26.5%, and in particular, from 20.8 to 25.8%. If the content of Al₂O₃ is excessively small, the thermal expansion coefficient tends to be high, and thus, it is difficult to produce crystallized glass having excellent thermal shock resistance. Further, the crystallized glass tends to have poor chemical durability. In addition, the crystal nuclei increase in size, the crystallized glass is more likely to be cloudy, and the color tone of the colored layer 3 is likely to be impaired. On the other hand, if the content of Al₂O₃ is excessively large, the meltability of the glass decreases and the viscosity of the glass melt increases. Thus, glass fining and glass forming becomes difficult, resulting in decrease in productivity. In addition, the crystal of mullite tends to be precipitated, causing devitrification of the glass. In such a case, the crystallized glass is easily breakable.

Li₂O is a component forming a Li₂O—Al₂O₃—SiO₂-based crystal, and a component having a large effect on crystallinity and reducing the viscosity of the glass to improve the meltability and the formability of glass. The content of Li₂O is preferably from 1 to 10%, from 2 to 10%, from 2 to 8%, from 2.5 to 6%, from 2.8 to 5.5%, from 2.8 to 5%, from 3 to 5%, from 3 to 4.5%, from 3 to 4.2%, and in particular, from 3.2 to 4%. If the content of Li₂O is excessively small, the crystal of mullite tends to be precipitated, causing devitrification of the glass. In addition, in crystallizing the glass, Li₂O—Al₂O₃—SiO₂-based crystal does not easily precipitate, and thus, it is difficult to obtain crystallized glass having excellent thermal shock resistance. Further, the meltability of the glass decreases and the viscosity of the glass melt increases. Thus, glass fining and glass forming becomes difficult, resulting in decrease in productivity. On the other hand, if the content of Li₂O is excessively large, crystallinity is excessively high, and thus, the glass tends to be subject to devitrification and crystallized glass becomes easily breakable.

SiO₂, Al₂O₃, and Li₂O are main constituent components of β-quartz solid solution, which is the main crystal, and Li₂O and Al₂O₃ compensate the mutual charges to dissolve into the SiO₂ skeleton. With such three components being contained in a suitable ratio, crystallization progresses efficiently to enable low-cost production. The mass ratio of (SiO₂+Al₂O₃)/Li₂O is preferably 20 or greater, 20.2 or greater, 20.4 or greater, 20.6 or greater, 20.8 or greater, and in particular, 21 or greater.

TiO₂ is a nucleating component for precipitating crystals in a crystallization step. On the other hand, if TiO₂ is contained in a large amount, the degree of coloration of the glass significantly increases, and the color tone of the colored layer 3 is likely to be impaired. In particular, a zirconia titanate-based crystal containing ZrO₂ and TiO₂ acts as a crystal nucleus, and transition of electrons from a valence band of oxygen serving a ligand to a conduction band of zirconia and titanium, which is a central metal, (LMCT transition) occurs. LMCT transition is involved in the coloration of crystallized glass. If titanium remains in a residual glass phase, the LMCT transition may occur from the valence band of a SiO₂ skeleton to the conduction band of tetravalent titanium in the residual glass phase. In trivalent titanium in the residual glass phase, a d-d transition occurs, and this transition is involved in the coloration of crystallized glass. Furthermore, when titanium and iron coexist, an ilmenite (FeTiO₃)-like coloration develops. It is also known that when titanium and tin coexist, the degree of yellowish coloration increases. Thus, the content of TiO₂ is preferably from 0 to less than 2%, from 0 to 1%, from 0 to less than 0.5%, from 0 to 0.48%, from 0 to 0.46%, from 0 to 0.44%, from 0 to 0.42%, from 0 to 0.4%, from 0 to 0.38%, from 0 to 0.36%, from 0 to 0.34%, from 0 to 0.32%, from 0 to 0.3%, from 0 to 0.28%, from 0 to 0.26%, from 0 to 0.24%, from 0 to 0.22%, from 0 to 0.2%, from 0 to 0.18%, from 0 to 0.16%, from 0 to 0.14%, from 0 to 0.12%, and in particular, from 0 to 0.1%. However, TiO₂ is easily mixed as an impurity, and thus, when it is attempted to completely remove TiO₂, the production cost tends to increase due to increase in the cost of the raw material batch. In order to suppress the increase in production cost, a lower limit of the content of TiO₂ is preferably 0.0003% or greater, 0.0005% or greater, 0.001% or greater, 0.005% or greater, 0.01% or greater, and in particular, 0.02% or greater.

SnO₂ is a component acting as a fining agent. In addition, SnO₂ is also a component necessary to efficiently precipitate crystals in a crystallization step. On the other hand, if SnO₂ is contained in large amounts, the degree of coloration of the glass significantly increases. The content of SnO₂ is preferably from 0 to 20%, from greater than 0 to 20%, from 0.05 to 20%, from 0.1 to 10%, from 0.1 to 5%, from 0.1 to 4%, from 0.1 to 3%, from 0.15 to 3%, from 0.2 to 3%, from 0.2 to 2.7%, from 0.2 to 2.4%, from 0.25 to 2.4%, from 0.3 to 2.4%, from 0.35 to 2.4%, from 0.4 to 2.4%, from 0.45 to 2.4%, from 0.5 to 2.4%, from 0.5 to 2.35%, from 0.5 to 2.3%, from 0.5 to 2.2%, from 0.5 to 2.1%, from 0.5 to 2.05%, from 0.5 to 2%, from 0.5 to 1.95%, from 0.5 to 1.93%, from 0.5 to 1.91%, from 0.5 to 1.9%, from 0.5 to 1.88%, from 0.5 to 1.85%, from 0.5 to 1.83%, from 0.5 to 1.81%, and in particular, from 0.5 to 1.8%. If the content of SnO₂ is excessively small, it is difficult to clarify the glass, and the productivity tends to decrease. Further, the crystal nuclei are not sufficiently formed, and coarse crystals may precipitate out, and the glass may possibly be cloudy or damaged. On the other hand, if the content of SnO₂ is excessively large, the coloration of the crystallized glass may be strong, and the color tone of the colored layer 3 is likely to be impaired. In addition, the amount of SnO₂ to be evaporated at melting tends to increase, and thus environmental burden tends to increase.

ZrO₂ is a nucleating component for precipitating crystals in the crystallization step. The content of ZrO₂ is preferably from 1 to 20%, from 1 to 15%, from 1 to 10%, from 1 to 5%, from 1.5 to 5%, from 1.75 to 4.5%, from 1.75 to 4.4%, from 1.75 to 4.3%, from 1.75 to 4.2%, from 1.75 to 4.1%, from 1.75 to 4%, from 1.8 to 4%, from 1.85 to 4%, from 1.9 to 4%, from 1.95 to 4%, from 2 to 4%, from 2.05 to 4%, from 2.1 to 4%, from 2.15 to 4%, from 2.2 to 4%, from 2.25 to 4%, from 2.3 to 4%, from 2.3 to 3.95%, from 2.3 to 3.9%, from 2.3 to 3.95%, from 2.3 to 3.9%, from 2.3 to 3.85%, from 2.3 to 3.8%, from greater than 2.7 to 3.8%, from 2.8 to 3.8%, from 2.9 to 3.8%, and in particular, from 3 to 3.8%. If the content of ZrO₂ is excessively small, the crystal nuclei are not sufficiently formed and coarse crystals precipitate out. In such a case, the crystallized glass tends to be cloudy, which results in impairment of the color tone of the colored layer 3, and the crystallized glass may be damaged. On the other hand, if the content of ZrO₂ is excessively large, coarse ZrO₂ crystals precipitate and the glass is easily subject to devitrification, and the crystallized glass becomes easily breakable.

TiO₂ and ZrO₂ are components that may function as a crystal nucleus. Ti and Zr are congeners, and are similar in electrical electronegativity, ion radii, and the like. Thus, it is known that, both components easily adopt a similar molecular conformation as an oxide, and in the coexistence of TiO₂ and ZrO₂, phase separation in the early stage of crystallization tends to occur. Thus, as long as an unacceptable level of coloration does not occur, the mass ratio of TiO₂/ZrO₂ is preferably from 0.0001 to 5.0, from 0.0001 to 4.0, from 0.0001 to 3.0, from 0.0001 to 2.5, from 0.0001 to 2.0, from 0.0001 to 1.5, from 0.0001 to 1.0, from 0.0001 to 0.5, from 0.0001 to 0.4, and in particular, from 0.0001 to 0.3. If TiO₂/ZrO₂ is excessively small, the production cost tends to increase due to increase in the cost of the raw material batch. On the other hand, if TiO₂/ZrO₂ is excessively large, crystal nucleation rate is decreased, and production costs may increase.

SnO₂+ZrO₂ is preferably from 1 to 30%, from 1.1 to 30%, from 1.1 to 27%, from 1.1 to 24%, from 1.1 to 21%, from 1.1 to 20%, from 1.1 to 17%, from 1.1 to 14%, from 1.1 to 11%, from 1.1 to 9%, from 1.1 to 7.5%, from 1.4 to 7.5%, from 1.8 to 7.5%, from 2.0 to 7.5%, from 2.2 to 7%, from 2.2 to 6.4%, from 2.2 to 6.2%, from 2.2 to 6%, from 2.3 to 6%, from 2.4 to 6%, from 2.5 to 6%, and in particular, from 2.8 to 6%. If SnO₂+ZrO₂ is excessively small, crystal nuclei are less likely to precipitate, and less likely to crystallize. On the other hand, if SnO₂+ZrO₂ is excessively large, the crystal nuclei increase in size, the crystallized glass is more likely to be cloudy, and the color tone of the colored layer 3 is likely to be impaired.

SnO₂ has an effect of promoting phase separation in the glass. To efficiently cause separation of phases while maintaining a liquidus temperature low (while suppressing the risk of devitrification due to primary phase precipitation) to promptly perform nucleation and crystal growth in later steps, the mass ratio of SnO₂/(SnO₂+ZrO₂) is preferably from 0.01 to 0.99, from 0.01 to 0.98, from 0.01 to 0.94, from 0.01 to 0.90, from 0.01 to 0.86, from 0.01 to 0.82, from 0.01 to 0.78, from 0.01 to 0.74, from 0.01 to 0.70, from 0.03 to 0.70, and in particular, from 0.05 to 0.70.

In addition, when SnO₂ is under a high temperature condition, a reaction of SnO₂->SnO+½O₂ occurs, and O₂ gas is released into the glass melt. Such a reaction is known as a fining mechanism by SnO₂, and the O₂ gas released during the reaction has a “defoaming effect” in which the fine bubbles existing in the glass melt are enlarged and the bubbles are released outside the glass system, and in addition, a “stirring effect” in which the glass melt is mixed. In the Li₂O—Al₂O₃—SiO₂-based crystallized glass of the present invention, the contents of SiO₂ and Al₂O₃ accounts for the majority and these components are poorly soluble, and thus, in order to efficiently form a homogeneous glass melt, these three components should be contained in suitable proportions. The mass ratio of (SiO₂+Al₂O₃)/SnO₂ is preferably 44 or greater, 44.3 or greater, 44.7 or greater, 45 or greater, 45.2 or greater, 45.4 or greater, 45.6 or greater, 45.8 or greater, and in particular, 46 or greater.

The mass ratio of Al₂O₃/(SnO₂+ZrO₂) is preferably 7.1 or less, 7.05 or less, 7.0 or less, 6.95 or less, 66.9 or less, 6.85 or less, 6.8 or less, 6.75 or less, 6.7 or less, 6.65 or less, 6.6 or less, 6.55 or less, 6.5 or less, 6.45 or less, 6.4 or less, 6.35 or less, 6.3 or less, 6.25 or less, 6.2 or less, 6.15 or less, 6.1 or less, 6.05 or less, 6.0 or less, 5.98 or less, 5.95 or less, 5.92 or less, 5.9 or less, 5.8 or less, 5.7 or less, 5.6 or less, and in particular, 5.5 or less. If Al₂O₃/(SnO₂+ZrO₂) is excessively high, nucleation does not proceed efficiently, which makes it difficult to achieve efficient crystallization. On the other hand, if Al₂O₃/(SnO₂+ZrO₂) is excessively small, the crystal nuclei increase in size, the crystallized glass is more likely to be cloudy, and the color tone of the colored layer 3 is likely to be impaired. Thus, the lower limit of Al₂O₃/(SnO₂+ZrO₂) is preferably 0.01 or greater.

MgO is a component that can be incorporated into a Li₂O—Al₂O₃—SiO₂-based crystal to form a solid solution together to increase the thermal expansion coefficient of a Li₂O—Al₂O₃—SiO₂-based crystal. The content of MgO is preferably from 0 to 10%, from 0 to 8%, from 0 to 6%, from 0 to 5%, from 0 to 4.5%, from 0 to 4%, from 0 to 3.5%, from 0.02 to 3.5%, from 0.05 to 3.5%, from 0.08 to 3.5%, from 0.1 to 3.5%, from 0.1 to 3.3%, from 0.1 to 3%, from 0.13 to 3%, from 0.15 to 3%, from 0.17 to 3%, from 0.19 to 3%, from 0.2 to 2.9%, from 0.2 to 2.7%, from 0.2 to 2.5%, from 0.2 to 2.3%, from 0.2 to 2.2%, 0.2 to 2.1%, and in particular, from 0.2 to 2%. If the content of MgO is excessively small, the thermal expansion coefficient tends to be excessively small. In addition, the amount of volume shrinkage that occurs in the crystal precipitation may be excessively large. In addition, a difference in thermal expansion coefficient between a crystal phase and a residual glass phase after crystallization becomes large, and thus, crystallized glass may become easily breakable. If the content of MgO is excessively large, crystallinity is excessively strong and the crystallized glass is easily subject to devitrification and becomes easily breakable. The thermal expansion coefficient tends to be excessively high.

P₂O₅ is a component that suppresses the precipitation of coarse ZrO₂ crystals. The content of P₂O₅ is preferably from 0 to 10%, from 0 to 8%, from 0 to 6%, from 0 to 5%, from 0 to 4%, from 0 to 3.5%, from 0.02 to 3.5%, from 0.05 to 3.5%, from 0.08 to 3.5%, from 0.1 to 3.5%, from 0.1 to 3.3%, from 0.1 to 3%, from 0.13 to 3%, from 0.15 to 3%, from 0.17 to 3%, from 0.19 to 3%, from 0.2 to 2.9%, from 0.2 to 2.7%, from 0.2 to 2.5%, from 0.2 to 2.3%, from 0.2 to 2.2%, from 0.2 to 2.1%, from 0.2 to 2%, and in particular, from 0.3 to 1.8%. If the content of P₂O₅ is excessively small, coarse ZrO₂ crystals precipitate and the glass is easily subject to devitrification, and thus, the crystallized glass may become easily breakable. On the other hand, if the content of P₂O₅ is excessively large, the amount of Li₂O—Al₂O₃—SiO₂-based crystals to precipitate decreases and the thermal expansion coefficient tends to be high.

As₂O₃ and Sb₂O₃ are highly toxic, and may pollute the environment during glass manufacturing processing, disposal of waste glass, and the like. Thus, Sb₂O₃+As₂O₃ is preferably less than 2%, 1% or less, 0.7% or less, less than 0.7%, 0.65% or less, 0.6% or less, 0.55% or less, 0.5% or less, 0.45% or less, 0.4% or less, 0.35% or less, 0.3% or less, 0.25% or less, 0.2% or less, 0.15% or less, 0.1% or less, and in particular, it is preferable that substantially no Sb₂O₃+As₂O₃ is contained (specifically, the content is preferably less than 0.1 mass %). Note that if As₂O₃ and Sb₂O₃ are contained, these components may be functioned as fining agents and nucleating agents.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass of the present invention may contain the following components in the glass composition in addition to the above components.

Na₂O is a component that can be incorporated into a Li₂O—Al₂O₃—SiO₂-based crystal to form a solid solution together, and is a component that has a significant effect on crystallinity and reduces the viscosity of the glass to improve glass meltability and formability. Na₂O is used also for adjusting the thermal expansion coefficient and the refractive index of the crystallized glass. The content of Na₂O is preferably from 0 to 10%, from 0 to 8%, from 0 to 6%, from 0 to 5%, from 0 to 4.5%, from 0 to 4%, from 0 to 3.5%, from 0 to 3%, from 0 to 2.7%, from 0 to 2.4%, from 0 to 2.1%, from 0 to 1.8%, and in particular, from 0 to 1.5%. If the content of Na₂O is excessively large, crystallinity is excessively strong and the glass is easily subject to devitrification and the resultant crystallized glass becomes easily breakable. An ionic radius of a Na cation is larger than a Li cation, a Mg cation, and the like, which are the constituent components of the main crystal, and the Na cation is not easily incorporated into the crystal, and thus, the Na cation after crystallization is likely to remain in the residual glass (glass matrix). Therefore, if the content of Na₂O is excessively large, a refractive index difference between the crystal phase and the residual glass is likely to occur, the crystallized glass is more likely to be cloudy, and the color tone of the colored layer 3 is likely to be impaired. However, Na₂O is easily mixed as an impurity, and thus, when it is attempted to completely remove Na₂O, the production cost tends to increase due to increase in the cost of the raw material batch. In order to suppress the increase in production cost, the lower limit of the content of Na₂O is preferably 0.0003% or greater, 0.0005% or greater, and in particular, 0.001% or greater.

K₂O is a component that can be incorporated into a Li₂O—Al₂O₃—SiO₂-based crystal to form a solid solution together, and is a component that has a significant effect on crystallinity and reduces the viscosity of the glass to improve glass meltability and formability. K₂O is used also for adjusting the thermal expansion coefficient and the refractive index of the crystallized glass. The content of K₂O is preferably from 0 to 10%, from 0 to 8%, from 0 to 6%, from 0 to 5%, from 0 to 4.5%, from 0 to 4%, from 0 to 3.5%, from 0 to 3%, from 0 to 2.7%, from 0 to 2.4%, from 0 to 2.1%, from 0 to 1.8%, from 0 to 1.5%, from 0 to 1.4%, from 0 to 1.3%, from 0 to 1.2%, from 0 to 1.1%, from 0 to 1%, from 0 to 0.9%, and in particular, from 0.1 to 0.8%. If the content of K₂O is excessively large, crystallinity is excessively strong and the glass is easily subject to devitrification and the crystallized glass becomes easily breakable. An ionic radius of a K cation is larger than a Li cation, a Mg cation, and the like, which are the constituent components of the main crystal, and the K cation is not easily incorporated into the crystal, and thus, the K cation after crystallization is likely to remain in the residual glass. Therefore, if the content of K₂O is excessively large, a refractive index difference between the crystal phase and the residual glass is likely to occur, the crystallized glass is more likely to be cloudy, and the color tone of the colored layer 3 is likely to be impaired. However, K₂O is easily mixed as an impurity, and thus, when it is attempted to completely remove K₂O, the production cost tends to increase due to increase in the cost of the raw material batch. In order to suppress the increase in production cost, the lower limit of the content of K₂O is preferably 0.0003% or greater, 0.0005% or greater, and in particular, 0.001% or greater.

Li₂O, Na₂O, K₂O are components that improve the meltability and the formability of the glass, but if the content of these components is excessively large, the low temperature viscosity excessively decreases, which may result in too high fluidity of the glass during crystallization. Li₂O, Na₂O, K₂O are components that may deteriorate the weather resistance, the water resistance, the chemical resistance, and the like of the glass before crystallization. If the glass before crystallization is degraded by moisture or the like, desired crystallization behavior, by extension, desired characteristics, may not be possibly obtained. On the other hand, ZrO₂ is a component that functions as a nucleating agent, and has an effect of preferential crystallization at the initial stage of crystallization to suppress the flow of residual glass. ZrO₂ has an effect of efficiently filling a void part of a glass network mainly composed of a SiO₂ skeleton and inhibiting a diffusion of protons and various chemical components in the glass network, and improves weather resistance, water resistance, chemical resistance, and the like of glass before crystallization. To obtain crystallized glass having a desired shape and properties, (Li₂O+Na₂O+K₂O)/ZrO₂ should be controlled in a suitable manner. The mass ratio of (Li₂O+Na₂O+K₂O)/ZrO₂ is preferably 2.0 or less, 1.98 or less, 1.96 or less, 1.94 or less, 1.92 or less, and in particular, 1.90 or less.

CaO is a component that reduces the viscosity of the glass and enhances the meltability and formability of the glass. CaO is used also for adjusting the thermal expansion coefficient and the refractive index of the crystallized glass. The content of CaO is preferably from 0 to 10%, from 0 to 8%, from 0 to 6%, from 0 to 5%, from 0 to 4.5%, from 0 to 4%, from 0 to 3.5%, from 0 to 3%, from 0 to 2.7%, from 0 to 2.4%, from 0 to 2.1%, from 0 to 1.8%, and in particular, from 0 to 1.5%. If the content of CaO is excessively large, the glass is easily subject to devitrification, and thus, the crystallized glass becomes easily breakable. An ionic radius of a Ca cation is larger than a Li cation, a Mg cation, and the like, which are the constituent components of the main crystal, and the Ca cation is not easily incorporated into the crystal, and thus, the Ca cation after crystallization is likely to remain in the residual glass. Therefore, if the content of CaO is excessively large, a refractive index difference between the crystal phase and the residual glass is likely to occur, the crystallized glass is more likely to be cloudy, and the color tone of the colored layer 3 is likely to be impaired. However, CaO is easily mixed as an impurity, and thus, when it is attempted to completely remove CaO, the production cost tends to increase due to increase in the cost of the raw material batch. In order to suppress the increase in production cost, the lower limit of the content of CaO is preferably 0.0001% or greater, 0.0003% or greater, and in particular, 0.0005% or greater.

SrO is a component that reduces the viscosity of the glass and enhances the meltability and formability of the glass. SrO is used also for adjusting the thermal expansion coefficient and the refractive index of the crystallized glass. The content of SrO is preferably from 0 to 10%, from 0 to 8%, from 0 to 6%, from 0 to 5%, from 0 to 4.5%, from 0 to 4%, from 0 to 3.5%, from 0 to 3%, from 0 to 2.7%, from 0 to 2.4%, from 0 to 2.1%, from 0 to 1.8%, from 0 to 1.5%, and in particular, from 0 to 1%. If the content of SrO is excessively large, the glass is easily subject to devitrification, and thus, the crystallized glass becomes easily breakable. An ionic radius of a Sr cation is larger than a Li cation, a Mg cation, and the like, which are the constituent components of the main crystal, and the Sr cation is not easily incorporated into the crystal, and thus, the Sr cation after crystallization is likely to remain in the residual glass. Therefore, if the content of SrO is excessively large, a refractive index difference between the crystal phase and the residual glass is likely to occur, the crystallized glass is more likely to be cloudy, and the color tone of the colored layer 3 is likely to be impaired. However, SrO is easily mixed as an impurity, and thus, when it is attempted to completely remove SrO, the production cost tends to increase due to increase in the cost of the raw material batch. In order to suppress the increase in production cost, the lower limit of the content of SrO is preferably 0.0001% or greater, 0.0003% or greater, and in particular, 0.0005% or greater.

BaO is a component that reduces the viscosity of the glass and enhances the meltability and formability of the glass. BaO is used also for adjusting the thermal expansion coefficient and the refractive index of the crystallized glass. The content of BaO is preferably from 0 to 10%, from 0 to 8%, from 0 to 6%, from 0 to 5%, from 0 to 4.5%, from 0 to 4%, from 0 to 3.5%, from 0 to 3%, from 0 to 2.7%, from 0 to 2.4%, from 0 to 2.1%, from 0 to 1.8%, from 0 to 1.5%, and in particular, from 0 to 1%. If the content of BaO is excessively large, crystals containing Ba precipitate, and the glass is easily subject to devitrification, and the crystallized glass becomes easily breakable. An ionic radius of a Ba cation is larger than a Li cation, a Mg cation, and the like, which are the constituent components of the main crystal, and the Ba cation is not easily incorporated into the crystal, and thus, the Ba cation after crystallization is likely to remain in the residual glass. Therefore, if the content of BaO is excessively large, a refractive index difference between the crystal phase and the residual glass is likely to occur, the crystallized glass is more likely to be cloudy, and the color tone of the colored layer 3 is likely to be impaired. However, BaO is easily mixed as an impurity, and thus, when it is attempted to completely remove BaO, the production cost tends to increase due to increase in the cost of the raw material batch. In order to suppress the increase in production cost, the lower limit of the content of BaO is preferably 0.0001% or greater, 0.0003% or greater, and in particular, 0.0005% or greater.

MgO, CaO, SrO, and BaO are components that improve the meltability and the formability of the glass, but if the content of these components is excessively high, the low temperature viscosity excessively decreases, which may result in too high fluidity of the glass during crystallization. On the other hand, ZrO₂ is a component that functions as a nucleating agent, and has an effect of preferential crystallization at the initial stage of crystallization to suppress the flow of residual glass. To obtain crystallized glass having a desired shape and properties, (MgO+CaO+SrO+BaO)/ZrO₂ should be controlled in a suitable manner. The mass ratio of (MgO+CaO+SrO+BaO)/ZrO₂ is preferably from 0 to 3, from 0 to 2.8, from 0 to 2.6, from 0 to 2.4, from 0 to 2.2, from 0 to 2.1, from 0 to 2, from 0 to 1.8, from 0 to 1.7, from 0 to 1.6, and in particular, from 0 to 1.5.

Na₂O, K₂O, CaO, SrO, and BaO are likely to remain in the residual glass after crystallization. Therefore, if the total amount of these components are excessively large, a refractive index difference between the crystal phase and the residual glass is likely to occur, and the crystallized glass is likely to be cloudy. Therefore, Na₂O+K₂O+CaO+SrO+BaO is preferably 8% or less, 7% or less, 6% or less, 5% or less, 4.5% or less, 4% or less, 3.5% or less, 3% or less, 2.7% or less, 2.42% or less, 2.415% or less, 2.410% or less, 2.405% or less, and in particular, 2.4% or less.

Li₂O, Na₂O, K₂O, MgO, CaO, SrO, and BaO are components that improve the meltability and the formability of the glass. A glass melt containing a large amount of MgO, CaO, SrO, and BaO tends to exhibit a gradual change in viscosity (viscosity curve) versus the temperature, and a glass melt containing a large amount of Li₂O, Na₂O, and K₂O tends to exhibit a steep change. If the change in the viscosity curve is excessively gradual, the glass still flows even after the glass is formed into a desired shape, and obtaining a desired shape is not easy. On the other hand, if the change in the viscosity curve is excessively steep, the glass melt solidifies during the formation, and obtaining a desired shape is not easy. Therefore, (MgO+CaO+SrO+BaO)/(Li₂O+Na₂O+K₂O) should be controlled in a suitable manner. The mass ratio of (MgO+CaO+SrO+BaO)/(Li₂O+Na₂O+K₂O) is preferably from 0 to 2, from 0 to 1.8, from 0 to 1.5, from 0 to 1.2, from 0 to 1, from 0 to 0.9, from 0 to 0.8, from 0 to 0.7, from 0 to 0.6, from 0 to 0.5, and in particular, from 0 to 0.45.

ZnO is a component that can be incorporated into a Li₂O—Al₂O₃—SiO₂-based crystal to form a solid solution together and applies a great effect on the crystallinity. ZnO is used also for adjusting the thermal expansion coefficient and the refractive index of the crystallized glass. The content of ZnO is preferably from 0 to 10%, from 0 to 8%, from 0 to 6%, from 0 to 5%, from 0 to 4.5%, from 0 to 4%, from 0 to 3.5%, from 0 to 3%, from 0 to 2.7%, from 0 to 2.4%, from 0 to 2.1%, from 0 to 1.8%, from 0 to 1.5%, and in particular, from 0 to 1%. If the content of ZnO is excessively large, crystallinity is excessively strong and the crystallized glass is more susceptible to devitrification and becomes easily breakable. However, ZnO is easily mixed as an impurity, and thus, when it is attempted to completely remove ZnO, the production cost tends to increase due to increase in the cost of the raw material batch. In order to suppress the increase in production cost, the lower limit of the content of ZnO is preferably 0.0001% or greater, 0.0003% or greater, and in particular, 0.0005% or greater.

In the Li₂O—Al₂O₃—SiO₂-based crystallized glass, a Li cation, a Mg cation, and a Zn cation are components that easily dissolve in a R-quartz solid solution, and compared with the Ba cation and the like, components that may contribute slightly to an increase in refractive index of the residual glass after crystallization. Li₂O, MgO, and ZnO function as a flux when vitrifying the raw material, and thus, it can be said that these components are important for producing colorless and transparent crystallized glass at a low temperature. Li₂O is an essential component to achieve low expansion, and is preferably contained at least 1%. A sufficient amount of Li₂O should be contained in order to achieve a desired thermal expansion coefficient and the like. However, in such a case, if the contents of MgO and ZnO are also increased correspondingly, the viscosity of the glass may decrease excessively. If the low temperature viscosity is excessively low, during firing, the fluidity of the softened glass is excessively large, and thus, crystallization into a desired shape may be difficult. If the high temperature viscosity is excessively low, the thermal load on the manufacturing equipment is reduced, but the speed of convection during heating increases, and this may result in a risk that refractories and the like are easily eroded physically. Therefore, it is preferable to control a content ratio of Li₂O, MgO, and ZnO, and in particular, it is preferable to control the total amount of MgO and ZnO relative to Li₂O that functions well as a flux. Therefore, the mass ratio of (MgO+ZnO)/Li₂O is preferably 0.394 or less, 0.393 or less, 0.392 or less, 0.391 or less, and in particular, 0.390 or less, and alternatively, 0.755 or greater, 0.756 or greater, 0.757 or greater, 0.758 or greater, and in particular, 0.759 or greater.

B₂O₃ is a component that reduces the viscosity of the glass and enhances the meltability and formability of the glass. B₂O₃ component may contribute to the likelihood of phase separation during crystal nucleus formation. The content of B₂O₃ is preferably from 0 to 10%, from 0 to 8%, from 0 to 6%, from 0 to 5%, from 0 to 4.5%, from 0 to 4%, from 0 to 3.5%, from 0 to 3%, from 0 to 2.7%, from 0 to 2.4%, from 0 to 2.1%, from 0 to 1.8%, and in particular, from 0 to 1.5%. If the content of B₂O₃ is excessively large, the amount of B₂O₃ that evaporates during melting increases, and an environmental burden increases. However, B₂O₃ is easily mixed as an impurity, and thus, when it is attempted to completely remove B₂O₃, the production cost tends to increase due to increase in the cost of the raw material batch. In order to suppress the increase in production cost, the crystallized glass may contain 0.0001% or greater, 0.0003% or greater, and in particular, 0.0005% or greater of B₂O₃.

It is known that in the Li₂O—Al₂O₃—SiO₂-based crystallized glass, phase separated regions are formed within the glass prior to crystal nucleation, and then crystal nuclei including TiO₂ and ZrO₂ are formed within the phase separated region. SnO₂, ZrO₂, P₂O₅, TiO₂, and B₂O₃ serve a vital role in the phase separation formation, and thus, SnO₂+ZrO₂+P₂O₅+TiO₂+B₂O₃ is preferably from 1.5 to 30%, from 1.5 to 26%, from 1.5 to 22%, from 1.5 to 20%, from 1.5 to 18%, from 1.5 to 16%, from 1.5 to 15%, from 1.8 to 15%, from 2.1 to 15%, from 2.4 to 15%, from 2.5 to 15%, from 2.8 to 15%, from 2.8 to 13%, from 2.8 to 12%, from 2.8 to 11%, from 2.8 to 10%, from 3 to 9.5%, from 3 to 9.2%, and in particular, from 3 to 9%, and the mass ratio of SnO₂/(SnO₂+ZrO₂+P₂O₅+TiO₂+B₂O₃) is preferably 0.06 or greater, 0.07 or greater, 0.08 or greater, 0.09 or greater, 0.1 or greater, 0.103 or greater, 0.106 or greater, 0.11 or greater, 0.112 or greater, 0.115 or greater, 0.118 or greater, 0.121 or greater, 0.124 or greater, 0.127 or greater, 0.128 or greater, in particular, 0.13 or greater. If SnO₂+ZrO₂+P₂O₅+TiO₂+B₂O₃ is excessively small, the phase separated region is not easily formed and crystallization is difficult. On the other hand, if SnO₂+ZrO₂+P₂O₅+TiO₂+B₂O₃ is excessively large, and/or SnO₂/(SnO₂+ZrO₂+P₂O₅+TiO₂+B₂O₃) is excessively small, the phase separated region becomes larger, the crystallized glass easily becomes cloudy, and the color tone of the colored layer 3 is likely to be impaired. Note that the upper limit of SnO₂/(SnO₂+ZrO₂+P₂O₅+TiO₂+B₂O₃) is not particularly limited, but realistically, 0.9 or less is preferable.

Fe₂O₃ is a component that increases the degree of coloration of the glass, and in particular, due to the interaction with TiO₂ and SnO₂, remarkably strengthens the coloration. The content of Fe₂O₃ is preferably 0.10% or less, 0.08% or less, 0.06% or less, 0.05% or less, 0.04% or less, 0.035% or less, 0.03% or less, 0.02% or less, 0.015% or less, 0.013% or less, 0.012% or less, 0.011% or less, 0.01% or less, 0.009% or less, 0.008% or less, 0.007% or less, 0.006% or less, 0.005% or less, 0.004% or less, 0.003% or less, and in particular, 0.002% or less. However, Fe₂O₃ is easily mixed as an impurity, and thus, when it is attempted to completely remove Fe₂O₃, the production cost tends to increase due to increase in the cost of the raw material batch. In order to suppress the increase in production cost, the lower limit of the content of Fe₂O₃ is preferably 0.0001% or greater, 0.0002% or greater, 0.0003% or greater, 0.0005% or greater, and in particular, 0.001% or greater.

When titanium and iron coexist, an ilmenite (FeTiO₃)-like coloration may develop. Particularly, in the Li₂O—Al₂O₃—SiO₂-based crystallized glass, titanium and iron components that do not precipitate as crystal nuclei or main crystals may remain in the residual glass after crystallization, and the development of the coloration may be promoted. It is possible to reduce the amount of such components when the composition is designed, but TiO₂ and Fe₂O₃ are easily mixed as an impurity, and thus, when it is attempted to completely remove TiO₂ and Fe₂O₃, the production cost tends to increase due to increase in the cost of the raw material batch. Therefore, in order to suppress the increase in production cost, TiO₂ and Fe₂O₃ may be contained within the above-described range, and, in the perspective of further reducing costs, both components may be contained as long as an unacceptable level of coloration does not occur. In such a case, the mass ratio of TiO₂/(TiO₂+Fe₂O₃) is preferably from 0.001 to 0.999, from 0.003 to 0.997, from 0.005 to 0.995, from 0.007 to 0.993, from 0.009 to 0.991, from 0.01 to 0.99, from 0.1 to 0.9, from 0.15 to 0.85, from 0.2 to 0.8, from 0.25 to 0.25, from 0.3 to 0.7, from 0.35 to 0.65, and in particular, from 0.4 to 0.6. This makes it easy to achieve low-cost production of crystallized glass with high level of colorless transparency.

Pt is a component that may be mixed into glass as ions, colloid, or metal, and develops coloration such as yellow to brown, which easily impairs the color tone of the colored layer 3. Such a tendency becomes prominent after crystallization. Further, after careful consideration, it was revealed that when Pt is mixed, nucleation and crystallization behavior of crystallized glass may be affected, and as a result the glass may be cloudy. Therefore, the content of the Pt is preferably 7 ppm or less, 6 ppm or less, 5 ppm or less, 4 ppm or less, 3 ppm or less, 2 ppm or less, 1.6 ppm or less, 1.4 ppm or less, 1.2 ppm or less, 1 ppm or less, 0.9 ppm or less, 0.8 ppm or less, 0.7 ppm or less, 0.6 ppm or less, 0.5 ppm or less, 0.45 ppm or less, 0.40 ppm or less, 0.35 ppm or less, and in particular, 0.30 ppm or less. It is preferable to avoid contamination of Pt where possible, but if general melting equipment is used, the use of a Pt material may be desired to obtain homogeneous glasses. Therefore, if it is attempted to completely remove Pt, the production cost tends to increase. As long as the coloration is permitted, to suppress the increase in production cost, the lower limit of the content of Pt is preferably 0.0001 ppm or greater, 0.001 ppm or greater, 0.005 ppm or greater, 0.01 ppm or greater, 0.02 ppm or greater, 0.03 ppm or greater, 0.04 ppm or greater, 0.05 ppm or greater, 0.06 ppm or greater, and in particular, 0.07 ppm or greater. In a case where coloration is permitted, similarly to ZrO₂ and TiO₂, Pt may be used as a nucleating agent that promotes precipitation of main crystals. In that case, Pt alone may be a nucleating agent, or as a complex, Pt and other components may be a nucleating agent. In a case where Pt is a nucleating agent, any form (colloid, metal crystal, and the like) may be used.

Rh is a component that may be mixed into glass as ions, colloid, or metal. Similarly to Pt, Rh tends to develop coloration such as yellow to brown and to make the crystallized glass cloudy, and as a result, the color tone of the colored layer 3 is likely to be impaired. Therefore, the content of the Rh is preferably 7 ppm or less, 6 ppm or less, 5 ppm or less, 4 ppm or less, 3 ppm or less, 2 ppm or less, 1.6 ppm or less, 1.4 ppm or less, 1.2 ppm or less, 1 ppm or less, 0.9 ppm or less, 0.8 ppm or less, 0.7 ppm or less, 0.6 ppm or less, 0.5 ppm or less, 0.45 ppm or less, 0.40 ppm or less, 0.35 ppm or less, and in particular, 0.30 ppm or less. It is preferable to avoid contamination of Rh where possible, but if general melting equipment is used, the use of a Rh material may be desired to obtain homogeneous glasses. Therefore, if it is attempted to completely remove Rh, the production cost tends to increase. As long as the coloration is permitted, to suppress the increase in production cost, the lower limit of the content of Rh is preferably 0.0001 ppm or greater, 0.001 ppm or greater, 0.005 ppm or greater, 0.01 ppm or greater, 0.02 ppm or greater, 0.03 ppm or greater, 0.04 ppm or greater, 0.05 ppm or greater, 0.06 ppm or greater, and in particular, 0.07 ppm or greater. In a case where coloration is permitted, similarly to ZrO₂ and TiO₂, Rh may be used as a nucleating agent. In that case, Rh alone may be a nucleating agent, or as a complex, Rh and other components may be a nucleating agent. In a case where Rh is a nucleating agent that promotes precipitation of main crystals, any form (colloid, metal crystal, and the like) may be used.

Pt+Rh is preferably 9 ppm or less, 8 ppm or less, 7 ppm or less, 6 ppm or less, 5 ppm or less, 4.75 ppm or less, 4.5 ppm or less, 4.25 ppm or less, 4 ppm or less, 3.75 ppm or less, 3.5 ppm or less, 3.25 ppm or less, 3 ppm or less, 2.75 ppm or less, 2.5 ppm or less, 2.25 ppm or less, 2 ppm or less, 1.75 ppm or less, 1.5 ppm or less, 1.25 ppm or less, 1 ppm or less, 0.95 ppm or less, 0.9 ppm or less, 0.85 ppm or less, 0.8 ppm or less, 0.75 ppm or less, 0.7 ppm or less, 0.65 ppm or less, 0.60 ppm or less, 0.55 ppm or less, 0.50 ppm or less, 0.45 ppm or less, 0.40 ppm or less, 0.35 ppm or less, and in particular, 0.30 ppm or less. It is preferable to avoid contamination of Pt and Rh where possible, but if general melting equipment is used, the use of a Pt material or Rh material may be desired to obtain homogeneous glasses. Therefore, if it is attempted to completely remove Pt and Rh, the production cost tends to increase. As long as the coloration is permitted, to suppress the increase in production cost, the lower limit of Pt+Rh is preferably 0.0001 ppm or greater, 0.001 ppm or greater, 0.005 ppm or greater, 0.01 ppm or greater, 0.02 ppm or greater, 0.03 ppm or greater, 0.04 ppm or greater, 0.05 ppm or greater, 0.06 ppm or greater, and in particular, 0.07 ppm or greater.

Typically, in developing glass materials, glasses having different compositions are produced using various crucibles. Therefore, there is often platinum and rhodium evaporated from the crucible inside the electric furnace used for melting. It was confirmed that the Pt and Rh present in the electric furnace are mixed into the glass. The amount of Pt and Rh to be mixed can be controlled by selecting appropriate raw materials and crucible materials. In addition, the contents of Pt and Rh in the glass can also be controlled by attaching a quartz lid to the crucible, lowering the melting temperature, shortening the time required for melting, or the like.

In addition to the above components, as long as no adverse effect is applied on the coloration, minor components, such as H₂, CO₂, CO, H₂O, He, Ne, Ar, and N₂ may be contained, and each of the minor components may be contained at up to 0.1%. An intentional addition of Ag, Au, Pd, Ir, V, Cr, Sc, Ce, Pr, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Ac, Th, Pa, U, and the like in the glass increases raw material costs, and tends to increase production costs. On the other hand, if a glass containing Ag, Au, and the like is subjected to light irradiation or heat treatment, aggregates of such components are formed, and crystallization may be promoted from such aggregates. If Pd and the like, which have various catalytic effects, are contained, it is possible to impart unique functions to the glass or the crystallized glass. In view of these circumstances, with an aim to promote crystallization or impart other functions, the crystallized glass may contain 1% or less, 0.5% or less, 0.3% or less, and 0.1% or less of each of the above components, and otherwise, it is preferable to contain 500 ppm or less, 300 ppm or less, 100 ppm or less, and in particular 10 ppm or less of each of the above components.

As long as no adverse effect is applied on the coloration, the Li₂O—Al₂O₃—SiO₂-based crystallized glass may contain up to 10% of SO₃, MnO, Cl₂, Y₂O₃, MoO₃, La₂O₃, WO₃, HfO₂, Ta₂O₅, Nd₂O₃, Nb₂O₅, RfO₂, and the like, in total. However, raw material batches of these components are costly and use of such raw material batches tends to increase production costs, and thus, unless there are special circumstances, these components may not be added. In particular, HfO₂ has a high raw material cost and Ta₂O₅ may be a conflict mineral, and thus, the total amount of these components is preferably, in mass %, 5% or less, 4% or less, 3% or less, 2% or less, 1% or less, 0.5% or less, 0.4% or less, 0.3% or less, 0.2% or less, 0.1% or less, 0.05% or less, less than 0.05%, 0.049% or less, 0.048% or less, 0.047% or less, 0.046% or less, and in particular, 0.045% or less.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a β-OH value from 0.001 to 2/mm, from 0.01 to 1.5/mm, from 0.02 to 1.5/mm, from 0.03 to 1.2/mm, from 0.04 to 1.5/mm, from 0.05 to 1/mm, from 0.06 to 1/mm, from 0.07 to 1/mm, from 0.08 to 0.9/mm, from 0.08 to 0.85/mm, from 0.08 to 0.8/mm, from 0.08 to 0.75/mm, from 0.08 to 0.7/mm, from 0.08 to 0.65/mm, from 0.08 to 0.6/mm, from 0.08 to 0.55/mm, from 0.08 to 0.54/mm, from 0.08 to 0.53/mm, from 0.08 to 0.52/mm, from 0.08 to 0.51/mm, and in particular, from 0.08 to 0.5/mm. If the β-OH value is excessively small, a crystal nucleus formation rate in the crystallization step is decreased, and a smaller number of crystal nuclei may be generated. As a result, the number of coarse crystals increases, resulting in cloudy and less transparent appearance of the crystallized glass. Such crystallized glass easily impairs the color tone of the colored layer 3. The reasons why a high β-OH value promotes crystallization is not completely known, but it is assumed that one of the reasons is that the β-OH groups weaken the bond of the glass skeleton and lower the viscosity of the glass. It is assumed that another reason is that the presence of the β-OH groups in the glass leads to increasing the mobility of components that can function as a crystal nucleus, such as Zr. On the other hand, if the β-OH value is excessively large, bubbles are likely to be generated at interface between the glass and a glass manufacturing furnace member made of metal containing Pt and the like, and a glass manufacturing furnace members including refractories, and the like, and thus, the quality of a glass product may be deteriorated. Note that the β-OH value is changed depending on the raw material, the melting atmosphere, the melting temperature, the melting time, and the like, and as necessary, these conditions can be changed to adjust the β-OH value. Note that the “β-OH value” refers to a value obtained by substituting a transmittance of glass measured by using FT-IR, in the following formula.

β-OH value=(1/X)log(T ₁ /T ₂)

-   -   X: Glass thickness (mm)     -   T₁: Transmittance (%) at a reference wavelength of 3846 cm⁻¹     -   T₂: Minimum transmittance (%) near an absorption wavelength of         hydroxyl groups of 3600 cm⁻¹

That is, a preferable composition range of the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 is: SiO₂ from 50 to 75%, Al₂O₃ from 10 to 30%, Li₂O from 1 to 8%, SnO₂ from 0 to 5%, ZrO₂ from 1 to 5%, MgO from 0 to 10%, P₂O₅ from 0 to 5%, TiO₂ from 0 to less than 1.5%, (Li₂O+Na₂O+K₂O)/ZrO₂ from 0 to 1.5, TiO₂/(TiO₂+Fe₂O₃) from 0.01 to 0.99, (MgO+ZnO)/Li₂O from 0 to 0.8, and β-OH value from 0.001 to 2/mm; preferably, SiO₂ from 50 to 75%, Al₂O₃ from 10 to 30%, Li₂O from 1 to 8%, SnO₂ from greater than 0 to 5%, ZrO₂ from 1 to 5%, MgO from 0 to 10%, P₂O₅ from 0 to 5%, TiO₂ from 0 to less than 1.5%, (Li₂O+Na₂O+K₂O)/ZrO₂ from 0 to 1.5, TiO₂/(TiO₂+Fe₂O₃) from 0.01 to 0.99, (MgO+ZnO)/Li₂O from 0 to 0.8, (MgO+CaO+SrO+BaO)/(Li₂O+Na₂O+K₂O) from 0 to 0.5, and β-OH value from 0.001 to 2/mm; more preferably, SiO₂ from 50 to 75%, Al₂O₃ from 10 to 30%, Li₂O from 1 to 8%, SnO₂ from greater than 0 to 5%, ZrO₂ from 1 to 5%, MgO from 0 to 10%, P₂O₅ from 0 to 5%, TiO₂ from 0 to less than 1.5%, (Li₂O+Na₂O+K₂O)/ZrO₂ from 0 to 1.5, TiO₂/(TiO₂+Fe₂O₃) from 0.01 to 0.99, (MgO+ZnO)/Li₂O from 0 to 0.8, (MgO+CaO+SrO+BaO)/(Li₂O+Na₂O+K₂O) from 0 to 0.5, (MgO+CaO+SrO+BaO)/ZrO₂ from 0 to 2, and β-OH value from 0.001 to 2/mm; further preferably, SiO₂ from 50 to 75%, Al₂O₃ from 10 to 30%, Li₂O from 1 to 8%, SnO₂ from greater than 0 to 5%, ZrO₂ from 1 to 5%, MgO from 0 to 10%, P₂O₅ from 0 to 5%, TiO₂ from 0 to less than 1.5%, (Li₂O+Na₂O+K₂O)/ZrO₂ from 0 to 1.5, TiO₂/(TiO₂+Fe₂O₃) from 0.01 to 0.99, (MgO+ZnO)/Li₂O from 0 to 0.8, (MgO+CaO+SrO+BaO)/(Li₂O+Na₂O+K₂O) from 0 to 0.5, (MgO+CaO+SrO+BaO)/ZrO₂ from 0 to 2, SnO₂/(SnO₂+ZrO₂+P₂O₅+TiO₂+B₂O₃) from 0.06 to 0.9, and β-OH value from 0.001 to 2/mm; further preferably, SiO₂ from 50 to 75%, Al₂O₃ from 10 to 30%, Li₂O from 1 to 8%, SnO₂ from greater than 0 to 5%, ZrO₂ from 1 to 5%, MgO from 0 to 10%, P₂O₅ from 0 to 5%, TiO₂ from 0 to less than 1.5%, (Li₂O+Na₂O+K₂O)/ZrO₂ from 0 to 1.5, TiO₂/(TiO₂+Fe₂O₃) from 0.01 to 0.99, (MgO+ZnO)/Li₂O from 0 to 0.8, (MgO+CaO+SrO+BaO)/(Li₂O+Na₂O+K₂O) from 0 to 0.5, (MgO+CaO+SrO+BaO)/ZrO₂ from 0 to 2, SnO₂/(SnO₂+ZrO₂+P₂O₅+TiO₂+B₂O₃) from 0.06 to 0.9, Pt+Rh from 0 to 5 ppm, and β-OH value from 0.001 to 2/mm; further preferably, SiO₂ from 50 to 75%, Al₂O₃ from 10 to 30%, Li₂O from 1 to 8%, SnO₂ from greater than 0 to 5%, ZrO₂ from 1 to 5%, MgO from 0 to 10%, P₂O₅ from 0 to 5%, TiO₂ from 0 to less than 1.5%, (Li₂O+Na₂O+K₂O)/ZrO₂ from 0 to 1.5, TiO₂/(TiO₂+Fe₂O₃) from 0.01 to 0.99, (MgO+ZnO)/Li₂O from 0 to 0.394, (MgO+CaO+SrO+BaO)/(Li₂O+Na₂O+K₂O) from 0 to 0.5, (MgO+CaO+SrO+BaO)/ZrO₂ from 0 to 2, SnO₂/(SnO₂+ZrO₂+P₂O₅+TiO₂+B₂O₃) from 0.06 to 0.9, Pt+Rh from 0 to 5 ppm, and β-OH value from 0.001 to 2/mm; and most preferably, SiO₂ from 50 to 75%, Al₂O₃ from 10 to 30%, Li₂O from 1 to 8%, SnO₂ from greater than 0 to 5%, ZrO₂ from 1 to 5%, MgO from 0 to 10%, P₂O₅ from 0 to 5%, TiO₂ from 0 to less than 1.5%, (Li₂O+Na₂O+K₂O)/ZrO₂ from 0 to 1.5, TiO₂/(TiO₂+Fe₂O₃) from 0.01 to 0.99, (MgO+ZnO)/Li₂O from 0 to 0.394, (MgO+CaO+SrO+BaO)/(Li₂O+Na₂O+K₂O) from 0 to 0.5, (MgO+CaO+SrO+BaO)/ZrO₂ from 0 to 2, SnO₂/(SnO₂+ZrO₂+P₂O₅+TiO₂+B₂O₃) from 0.06 to 0.9, Pt+Rh from 0 to 5 ppm, HfO₂+Ta₂O₅ from 0 to less than 0.05%, β-OH value from 0.001 to 2/mm, and Sb₂O₃+As₂O₃ less than 0.7%.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 having the above-described composition is likely to have colorless and transparent appearance and less likely to impair the color tone of the colored layer 3.

In the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2, it is preferable that a lightness L* at a thickness of 3 mm is 70% or greater, 75 or greater, 80 or greater, 85 or greater, 90 or greater, 91 or greater, 92 or greater, 93 or greater, 94 or greater, 95 or greater, 96 or greater, 96.1 or greater, 96.3 or greater, and in particular, 96.5 or greater. If the lightness L* is excessively small, the glass tends to be grayish and look dark regardless of the magnitude of chromaticity, and the color tone of the colored layer 3 is likely to be impaired.

In the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2, a chromaticity a* at a thickness of 3 mm is preferably within ±5, within ±4.5, within ±4, within ±3.6, within ±3.2, within ±2.8, within ±2.4, within ±2, within ±1.8, within ±1.6, within ±1.4, within ±1.2, within ±1, within ±0.9, within ±0.8, within ±0.7, within ±0.6, and in particular, within ±0.5. If the lightness a* is a negative value with an excessively large absolute value, the glass tends to be green, if the lightness a* is a positive value with an excessively large absolute value, the glass tends to be red, and in such cases, the color tone of the colored layer 3 is likely to be impaired.

In the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2, a chromaticity b* at a thickness of 3 mm is preferably within ±5, within ±4.5, within ±4, within ±3.6, within ±3.2, within ±2.8, within ±2.4, within ±2, within ±1.8, within ±1.6, within ±1.4, within ±1.2, within ±1, within ±0.9, within ±0.8, within ±0.7, within ±0.6, and in particular, within ±0.5. If the lightness b* is a negative value with an excessively large absolute value, the glass tends to be blue, if the lightness b* is a positive value with an excessively large absolute value, the glass tends to be yellow, and in such cases, the color tone of the colored layer 3 is likely to be impaired.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a transmittance at a thickness of 3 mm and a wavelength of 200 nm of 0% or greater, 2.5% or greater, 5% or greater, 10% or greater, 12% or greater, 14% or greater, 16% or greater, 18% or greater, 20% or greater, 22% or greater, 24% or greater, 26% or greater, 28% or greater, 30% or greater, 32% or greater, 34% or greater, 36% or greater, 38% or greater, 40% or greater, 40.5% or greater, 41% or greater, 41.5% or greater, 42% or greater, 42.5% or greater, 43% or greater, 43.5% or greater, 44% or greater, 44.5% or greater, and in particular, 45% or greater. If the transmittance at a wavelength of 200 nm is excessively low, the desired transmission performance may not be obtained, and the color tone of the colored layer 3 is likely to be impaired.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a transmittance at a thickness of 3 mm and a wavelength of 250 nm of 0% or greater, 1% or greater, 2% or greater, 3% or greater, 4% or greater, 5% or greater, 6% or greater, 7% or greater, 8% or greater, 9% or greater, 10% or greater, 10.5% or greater, 11% or greater, 11.5% or greater, 12% or greater, 12.5% or greater, 13% or greater, 13.5% or greater, 14% or greater, 14.5% or greater, 15% or greater, 15.5% or greater, and in particular, 16% or greater. If the transmittance at a wavelength of 250 nm is excessively low, the desired transmission performance may not be obtained, and the color tone of the colored layer 3 is likely to be impaired.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a transmittance at a thickness of 3 mm and a wavelength of 300 nm of 0% or greater, 2.5% or greater, 5% or greater, 10% or greater, 12% or greater, 14% or greater, 16% or greater, 18% or greater, 20% or greater, 22% or greater, 24% or greater, 26% or greater, 28% or greater, 30% or greater, 32% or greater, 34% or greater, 36% or greater, 38% or greater, 40% or greater, 40.5% or greater, 41% or greater, 41.5% or greater, 42% or greater, 42.5% or greater, 43% or greater, 43.5% or greater, 44% or greater, 44.5% or greater, and in particular, 45% or greater. If the transmittance at a wavelength of 300 nm is excessively low, the desired transmission performance may not be obtained, and the color tone of the colored layer 3 is likely to be impaired.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a transmittance at a thickness of 3 mm and a wavelength of 325 nm of 0% or greater, 2.5% or greater, 5% or greater, 10% or greater, 12% or greater, 14% or greater, 16% or greater, 18% or greater, 20% or greater, 22% or greater, 24% or greater, 26% or greater, 28% or greater, 30% or greater, 32% or greater, 34% or greater, 36% or greater, 38% or greater, 40% or greater, 42% or greater, 44% or greater, 46% or greater, 48% or greater, 50% or greater, 52% or greater, 54% or greater, 56% or greater, 57% or greater, 58% or greater, 59% or greater, 60% or greater, 61% or greater, 62% or greater, 63% or greater, 64% or greater, and in particular, 65% or greater. If the transmittance at a wavelength of 325 nm is excessively low, the desired transmission performance may not be obtained, and the color tone of the colored layer 3 is likely to be impaired.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a transmittance at a thickness of 3 mm and a wavelength of 350 nm is 0% or greater, 5% or greater, 10% or greater, 15% or greater, 20% or greater, 25% or greater, 30% or greater, 35% or greater, 40% or greater, 45% or greater, 50% or greater, 55% or greater, 60% or greater, 65% or greater, 70% or greater, 71% or greater, 72% or greater, 73% or greater, 74% or greater, 75% or greater, 76% or greater, 77% or greater, 78% or greater, 80% or greater, 81% or greater, 82% or greater, and 83% or greater. If the transmittance at a wavelength of 350 nm is excessively low, the desired transmission performance may not be obtained, and the color tone of the colored layer 3 is likely to be impaired.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a transmittance at a thickness of 3 mm and a wavelength of 380 nm of 50% or greater, 55% or greater, 60% or greater, 65% or greater, 70% or greater, 75% or greater, 78% or greater, 80% or greater, 81% or greater, 82% or greater, 83% or greater, and in particular, 84% or greater. If the transmittance at a wavelength of 380 nm is excessively low, the glass develops a strong yellow color and the transparency of the crystallized glass decreased, and as a result, the desired transmission performance may not be obtained and the color tone of the colored layer 3 is likely to be impaired.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a transmittance at a thickness of 3 mm and a wavelength of 800 nm of 50% or greater, 55% or greater, 60% or greater, 65% or greater, 70% or greater, 75% or greater, 78% or greater, 80% or greater, 81% or greater, 82% or greater, 83% or greater, 84% or greater, 85% or greater, 86% or greater, 87% or greater, and in particular, 88% or greater. If the transmittance at a wavelength of 800 nm is excessively low, the glass tends to be green and thus to impair the color tone of the colored layer 3.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a transmittance at a thickness of 3 mm and a wavelength of 1200 nm of 50% or greater, 55% or greater, 60% or greater, 65% or greater, 70% or greater, 72% or greater, 74% or greater, 76% or greater, 78% or greater, 80% or greater, 81% or greater, 82% or greater, 83% or greater, 84% or greater, 85% or greater, 86% or greater, 87% or greater, 88% or greater, and in particular, 89% or greater. If the transmittance at a wavelength of 1200 nm is excessively low, the glass tends to be green and thus to impair the color tone of the colored layer 3.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a rate of transmittance change before and after crystallization at a thickness of 3 mm and at a wavelength of 300 nm of 50% or less, 48% or less, 46% or less, 44% or less, 42% or less, 40% or less, 38% or less, 37.5% or less, 37% or less, 36.5% or less, 36% or less, 35.5% or less, and in particular, 35% or less. If the rate of transmittance change before and after crystallization is reduced, it is possible to predict and control, before the crystallization, the transmittance after crystallization, and it is easier to obtain the desired transmission performance after crystallization. It is preferable that the rate of transmittance change before and after crystallization is small not only at a wavelength of 300 nm but also over the entire wavelength range.

In the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2, in a state of the glass before crystallization, a strain point (temperature corresponding to the viscosity of the glass of about 10^(14.5) dPa·s) is preferably 600° C. or higher, 605° C. or higher, 610° C. or higher, 615° C. or higher, 620° C. or higher, 630° C. or higher, 635° C. or higher, 640° C. or higher, 645° C. or higher, 650° C. or higher, and in particular, 655° C. or higher. If the strain point is excessively low, the pre-crystallized glass becomes easily breakable when formed.

In the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2, in a state of the glass before crystallization, an annealing point (temperature corresponding to the viscosity of the glass of about 10¹³ dPa·s) is preferably 680° C. or higher, 685° C. or higher, 690° C. or higher, 695° C. or higher, 700° C. or higher, 705° C. or higher, 710° C. or higher, 715° C. or higher, 720° C. or higher, and in particular, 725° C. or higher. If the annealing point is excessively low, the pre-crystallized glass becomes easily breakable when formed.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 is easily crystallized by heat treatment, and thus, unlike general glass such soda lime glass, it is not easy to measure a softening point (temperature corresponding to the viscosity of the glass of about 10^(7.6) dPa·s). Therefore, in the Li₂O—Al₂O₃—SiO₂-based crystallized glass of the present invention, a temperature at which the slope of the thermal expansion curve of the glass before crystallization changes is used as a glass transition temperature, and is regarded as an alternative to the softening point. In the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2, in a the glass state before crystallization, the glass transition temperature is preferably 680° C. or higher, 685° C. or higher, 690° C. or higher, 695° C. or higher, 700° C. or higher, 705° C. or higher, 710° C. or higher, 715° C. or higher, 720° C. or higher, and in particular, 725° C. or higher. An excessively low glass transition temperature results in excessively high fluidity of the glass during crystallization, which makes it difficult to form the glass into a desired shape.

In the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2, a liquidus temperature is preferably 1540° C. or less, 1535° C. or less, 1530° C. or less, 1525° C. or less, 1520° C. or less, 1515° C. or less, 1510° C. or less, 1505° C. or less, 1500° C. or less, 1495° C. or less, 1490° C. or less, 1485° C. or less, 1480° C. or less, 1475° C. or less, 1470° C. or less, 1465° C. or less, 1460° C. or less, 1455° C. or less, 1450° C. or less, 1445° C. or less, 1440° C. or less, 1435° C. or less, 1430° C. or less, 1425° C. or less, 1420° C. or less, 1415° C. or less, and in particular, 1410° C. or less. If the liquidus temperature is excessively high, the glass is easily subject to devitrification during production. On the other hand, if the liquidus temperature is 1480° C. or less, it is easy to manufacture the glass by a roll method and the like, if the liquidus temperature is 1450° C. or less, it is easy to manufacture the glass by a casting method, and the like, and If the liquidus temperature is 1410° C. or less, it is easy to manufacture the glass by a fusion method and the like.

In the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2, a liquidus viscosity (logarithm of the viscosity corresponding to the liquidus temperature) is preferably 2.70 or greater, 2.75 or greater, 2.80 or greater, 2.85 or greater, 2.90 or greater, 2.95 or greater, 3.00 or greater, 3.05 or greater, 3.10 or greater, 3.15 or greater, 3.20 or greater, 3.25 or greater, 3.30 or greater, 3.35 or greater, 3.40 or greater, 3.45 or greater, 3.50 or greater, 3.55 or greater, 3.60 or greater, 3.65 or greater, and in particular, 3.70 or greater. If the liquidus viscosity is excessively low, the glass is easily subject to devitrification during production. On the other hand, if the liquidus viscosity is 3.40 or greater, it is easy to manufacture the glass by a roll method and the like, if the liquidus viscosity is 3.50 or greater, it is easy to manufacture the glass by a casting method, and the like, and If the liquidus viscosity is 3.70 or greater, it is easy to manufacture the glass by a fusion method and the like.

In the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2, a β-quartz solid solution preferably precipitates as a main crystal. If the R-quartz solid solution precipitates as the main crystal, the crystal grain easily decreases in size, and thus, the crystallized glass easily transmits visible light. As a result, transparency of the crystallized glass easily increases and the color tone of the colored layer 3 is not easily impaired. It is also possible to easily bring the thermal expansion coefficient of the glass close to zero, and during heat treatment and cooling, the glass is not easily breakable. Note that if the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 is subjected to heat treatment at a temperature higher than the crystallization conditions for precipitating the β-quartz solid solution, a β-spodumene solid solution precipitates. The crystal grain size of β-spodumene solid solution tends to be larger than that of β-quartz solid solution, and thus, generally, precipitation of β-spodumene solid solution tends to result in a cloudy appearance of the crystallized glass. However, when the glass composition and firing conditions are suitably adjusted, a refractive index difference between the crystalline phase containing β-spodumene solid solution and the residual glass phase may be small, and in such a case, the crystallized glass is less cloudy. In the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2, crystals such as β-spodumene solid solution may be contained as long as there is no adverse effect on coloration and the like.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a thermal expansion coefficient at from 30 to 380° C. of 30×10⁻⁷/° C. or less, 25×10⁻⁷/° C. or less, 20×10⁻⁷/° C. or less, 18×10⁻⁷/° C. or less, 16×10⁻⁷/° C. or less, 14×10⁻⁷/° C. or less, 13×10⁻⁷/° C. or less, 12×10⁻⁷/° C. or less, 11×10⁻⁷/° C. or less, 10×10⁻⁷/° C. or less, 9×10⁻⁷/° C. or less, 8×10⁻⁷/° C. or less, 7×10⁻⁷/° C. or less, 6×10⁻⁷/° C. or less, 5×10⁻⁷/° C. or less, 4×10⁻⁷/° C. or less, 3×10⁻⁷/° C. or less, and in particular, 2×10⁻⁷/° C. or less. Note that if dimensional stability and/or thermal shock resistance are particularly desired, the thermal expansion coefficient is preferably from −5×10⁻⁷/° C. to 5×10⁻⁷/° C., from −3×10⁻⁷/° C. to 3×10⁻⁷/° C., from −2.5×10⁻⁷/° C. to 2.5×10⁻⁷/° C., from −2×10⁻⁷/° C. to 2×10⁻⁷/° C., from −1.5×10⁻⁷/° C. to 1.5×10⁻⁷/° C., from −1×10⁻⁷/° C. to 1×10⁻⁷/° C., and in particular, from −0.5×10⁻⁷/° C. to 0.5×10⁻⁷/° C.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a thermal expansion coefficient at from 30 to 750° C. of 30×10⁻⁷/° C. or less, 25×10⁻⁷/° C. or less, 20×10⁻⁷/° C. or less, 18×10⁻⁷/° C. or less, 16×10⁻⁷/° C. or less, 14×10⁻⁷/° C. or less, 13×10⁻⁷/° C. or less, 12×10⁻⁷/° C. or less, 11×10⁻⁷/° C. or less, 10×10⁻⁷/° C. or less, 9×10⁻⁷/° C. or less, 8×10⁻⁷/° C. or less, 7×10⁻⁷/° C. or less, 6×10⁻⁷/° C. or less, 5×10⁻⁷/° C. or less, 4×10⁻⁷/° C. or less, and in particular, 3×10⁻⁷/° C. or less. Note that if dimensional stability and/or thermal shock resistance are particularly desired, the thermal expansion coefficient is preferably from −15×10⁻⁷/° C. to 15×10⁻⁷/° C., from −12×10⁻⁷/° C. to 12×10⁻⁷/° C., from −10×10⁻⁷/° C. to 10×10⁻⁷/° C., from −8×10⁻⁷/° C. to 8×10⁻⁷/° C., from −6×10⁻⁷/° C. to 6×10⁻⁷/° C., from −5×10⁻⁷/° C. to 5×10⁻⁷/° C., from −4.5×10⁻⁷/° C. to 4.5×10⁻⁷/° C., from −4×10⁻⁷/° C. to 4×10⁻⁷/° C., from −3.5×10⁻⁷/° C. to 3.5×10⁻⁷/° C., from −3×10⁻⁷/° C. to 3×10⁻⁷/° C., from −2.5×10⁻⁷/° C. to 2.5×10⁻⁷/° C., from −2×10⁻⁷/° C. to 2×10⁻⁷/° C., from −1.5×10⁻⁷/° C. to 1.5×10⁻⁷/° C., from −1×10⁻⁷/° C. to 1×10⁻⁷/° C., and in particular, from −0.5×10⁻⁷/° C. to 0.5×10⁻⁷/° C.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a Young's modulus of from 60 to 120 GPa, from 70 to 110 GPa, from 75 to 110 GPa, from 75 to 105 GPa, from 80 to 105 GPa, and in particular, from 80 to 100 GPa. If the Young's modulus is excessively low or high, the mechanical strength of the glass article 1 is likely to decrease.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a modulus of rigidity of from 25 to 50 GPa, from 27 to 48 GPa, from 29 to 46 GPa, and in particular, from 30 to 45 GPa. If the modulus of rigidity is excessively low or high, the mechanical strength of the glass article 1 is likely to decrease.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a Poisson's ratio of 0.35 or less, 0.32 or less, 0.3 or less, 0.28 or less, 0.26 or less, and in particular, 0.25 or less. If the Poisson's ratio is excessively large, the mechanical strength of the glass article 1 is likely to decrease.

The crystallizable glass before crystallization of the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 preferably has a density of from 2.30 to 2.60 g/cm³, from 2.32 to 2.58 g/cm³, from 2.34 to 2.56 g/cm³, from 2.36 to 2.54 g/cm³, from 2.38 to 2.52 g/cm³, from 2.39 to 2.51 g/cm³, and in particular, from 2.40 to 2.50 g/cm³. If the density of the crystallizable glass is excessively small, the gas permeability before crystallization deteriorates, and the glass may be contaminated during storage. On the other hand, if the density of the crystallizable glass is excessively large, the weight per unit area increases, and this makes it difficult to handle such glass.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 (after crystallization) preferably has a density of from 2.40 to 2.80 g/cm³, from 2.42 to 2.78 g/cm³, from 2.44 to 2.76 g/cm³, from 2.46 to 2.74 g/cm³, and in particular, from 2.47 to 2.73 g/cm³. If the density of crystallized glass is excessively small, the gas permeability of the crystallized glass may deteriorate and the colored layer may be contaminated. On the other hand, if the density of the crystallized glass is excessively large, the weight per unit area increases, which makes it difficult to handle the crystallized glass. The density of crystallized glass (after crystallization) is an index for determining whether the glass is sufficiently crystallized. Specifically, if the same glasses are compared, a higher density (larger difference in density between raw glass and the crystallized glass) indicates that crystallization is further advanced.

A rate of density change of the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 is defined by {(density after crystallization (g/cm³)—density before crystallization (g/cm³))/density before crystallization (g/cm³)}×100(%), where the density before crystallization is a density obtained after holding a melted glass at 700° C. for 30 minutes and cooling the glass to room temperature at 3° C./min, and the density after crystallization is a density obtained after crystallization treatment under a predetermined condition. The rate of density change is preferably from 0.01 to 10%, from 0.05 to 8%, from 0.1 to 8%, from 0.3 to 8%, from 0.5 to 8%, from 0.9 to 8%, from 1 to 7.8%, from 1 to 7.4%, from 1 to 7%, from 1.2 to 7%, from 1.6 to 7%, from 2 to 7%, from 2 to 6.8%, from 2 to 6.5%, from 2 to 6.3%, from 2 to 6.2%, from 2 to 6.1%, from 2 to 6%, from 2.5 to 5%, from 2.6 to 4.5%, and from 2.8 to 3.8%. If the rate of density change before and after crystallization is reduced, it is possible to reduce a breakage rate after crystallization, and it is possible to reduce scattering of glass and a glass matrix, and as a result it is possible to obtain crystallized glass with high transmittance. In particular, in a region where the content of TiO₂ is less than 2.0% (in particular, less than 0.5%), in order to reduce a coloration factor other than absorption of TiO₂ and the like, it is possible to significantly reduce scattering and possible to contribute to improving the transmittance.

The Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 may be subject to chemical strengthening and the like. As a treatment condition of the chemical strengthening treatment, an appropriate treatment time and an appropriate treatment temperature may be chosen in consideration of the glass composition, the crystallinity, the type of the molten salt, and the like. For example, in order to facilitate chemical strengthening after crystallization, a glass composition containing a large amount of Na₂O that may be contained in the residual glass may be selected, and the crystallinity may be intentionally lowered. A molten salt may include an alkali metal such as Li, Na, K alone or in combination thereof. In addition, instead of normal one-step strengthening, multistep chemical strengthening may be selected. Besides, if the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 is subject to chemical strengthening and the like before crystallization, it is possible to reduce the content of Li₂O on a surface of a sample compared to the content of LiO₂ inside the sample. When such glass is crystallized, the crystallinity of the surface of the sample is lower than that inside the sample and the thermal expansion coefficient of the surface of the sample is relatively high, it is possible to introduce compressive stress resulting from a difference in thermal expansion into the surface of the sample. If the crystallinity of the surface of the sample is low, the glass phase increases at the surface, and depending on the selection of glass composition, it is possible to improve chemical resistance and gas barrier properties.

Next, a method of manufacturing the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 will be described.

Firstly, a raw material batch prepared to be glass having the composition described above is charged into a glass melting furnace, melted at from 1500 to 1750° C., and then, formed. Note that a flame melting method using a burner and the like, an electric melting method by electric heating, and the like may be used during the glass melting. In addition, melting by laser irradiation and melting by plasma may also be used.

Next, the obtained crystallizable glass (glass that can be crystallized but not yet crystallized) is heat-treated to crystallize. As the crystallization condition, firstly, nucleation is performed at from 700 to 950° C. (preferably from 750 to 900° C.) for 0.1 to 100 hours (preferably from 1 to 60 hours), and subsequently, crystal growth is performed at from 800 to 1050° C. (preferably from 800 to 1000° C.) for 0.1 to 50 hours (preferably from 0.2 to 10 hours). As a result, it is possible to obtain transparent Li₂O—Al₂O₃—SiO₂-based crystallized glass (thickness: 1 to 10 mm) in which β-quartz solid solution crystals were precipitated as main crystals. Note that heat treatment may be performed only at a certain temperature, stepwise heat treatment including holding the glass at two or more temperature levels may be performed, and heating may be performed while providing a temperature gradient.

A sound wave or electromagnetic wave may be applied to promote the crystallization. Further, the crystallized glass at a high-temperature may be cooled at a rate according to a certain temperature gradient, or may be cooled according to a temperature gradient of two or more levels. If it is preferable to obtain sufficient thermal shock resistance, it is desired to sufficiently relax the structure of the residual glass phase by controlling the cooling rate. In an inner portion of the crystallized glass in the thickness direction, which is farthest from the surface, an average cooling rate from 800° C. to 25° C. is preferably 3000° C./min, 1000° C./min or less, 500° C./min or less, 400° C./min or less, 300° C./min or less, 200° C./min or less, 100° C./min or less, 50° C./min or less, 25° C./min or less, 10° C./min or less, and in particular, 5° C./min or less. If it is desired to obtain a long-term dimensional stability, the average cooling rate is further preferably 2.5° C./min or less, 1° C./min or less, 0.5° C./min or less, 0.1° C./min or less, 0.05° C./min or less, 0.01° C./min or less, 0.005° C./min or less, 0.001° C./min or less, 0.0005° C./min or less, and in particular, 0.0001° C./min or less. Except for a case of physical strengthening treatment by air cooling, water cooling, and the like, as to the cooling rate of the crystallized glass, it is desirable to minimize a difference between the cooling rate at the surface of the glass and the cooling rate in the inner portion in the thickness direction, which is furthest from the surface of the glass. A value obtained by dividing the cooling rate in the inner portion in the thickness direction, which is furthest from the surface, by the cooling rate at the surface is preferably from 0.0001 to 1, from 0.001 to 1, from 0.01 to 1, from 0.1 to 1, from 0.5 to 1, from 0.8 to 1, from 0.9 to 1, and in particular, 1. When the value is close to 1, in all positions of the crystallized glass sample, residual strain is difficult to occur, and it is easy to obtain a long-term dimensional stability. Note that it is possible to estimate the cooling rate at the surface by using a contact temperature measurement or a radiation thermometer. The internal temperature can be estimated by placing the crystallized glass at a high temperature in a cooling medium, measuring a heat quantity and a heat quantity change rate of the cooling medium, estimating the internal temperature based on numerical data obtained in the measurement, specific heat and thermal conductivity of the crystallized glass and the cooling medium, and the like.

Colored Layer 3

The colored layer 3 preferably contains a silicone resin, a color pigment, and an extender pigment. From the perspective of dispersibility, heat resistance, in the colored layer 3, the content ratio of the color pigment to the extender pigment (color pigment/extender pigment) is preferably from 1 to 6, in particular from 1.5 to 5.

The silicone resin contained in the colored layer 3 preferably has high heat resistance. For example, the silicone resin contained in the colored layer 3 is preferably a silicone resin in which a functional group directly bonded to a silicon atom is at least one of a methyl group and a phenyl group. In these cases, the color change of the colored layer 3 is easily suppressed when the glass article 1 reaches a high temperature.

The content of the silicone resin in the colored layer 3 is preferably from 20 to 70 mass %, in particular from 30 mass to 60 mass %. If the content of the silicone resin is excessively small, the heat resistance and the impact resistance of the glass article 1 are likely to decrease. On the other hand, if the content of the silicone resin is excessively large, the mechanical strength of the glass article 1 is likely to decrease. Note that the content of the silicone resin is a content relative to the total amount of all materials included in the colored layer 3, which corresponds to 100 mass %.

The color pigment contained in the colored layer 3 is not particularly limited as long as a colored inorganic material is used. Examples of the color pigments include, but are not limited to, a white pigment powder such as a TiO₂ powder, a ZrO₂ powder and a ZrSiO₄ powder, a blue inorganic pigment powder containing Co, a green inorganic pigment powder containing Co, a Ti—Sb—Cr-based or Ti—Ni-based yellow inorganic pigment powder, a Co—Si-based red inorganic pigment powder, a brown inorganic pigment powder containing Fe, and a black inorganic pigment powder containing Cu.

Specific examples of the blue inorganic pigment powder containing Co may include, but are not limited to, a Co—Al or Co—Al—Ti based inorganic pigment powder. Specific examples of the Co—Al-based inorganic pigment powder include, but are not limited to, a CoAl₂O₄ powder. Specific examples of the Co—Al—Ti-based inorganic pigment powders include, but are not limited to, a CoAl₂O₄—TiO₂—Li₂O powder.

Specific examples of the green inorganic pigment powder containing Co include, but are not limited to, a Co—Al—Cr-based or Co—Ni—Ti—Zn-based inorganic pigment powder. Specific examples of the Co—Al—Cr-based inorganic pigment powder include, but are not limited to, a Co(Al,Cr)₂O₄ powder. Specific examples of the Co—Ni—Ti—Zn-based inorganic pigment powder include, but are not limited to, a (Co,Ni,Zn)₂TiO₄ powder.

Specific examples of the brown inorganic pigment powder containing Fe include, but are not limited to, a Fe—Zn-based inorganic pigment powder. Specific examples of the Fe—Zn-based inorganic pigment powder include, but are not limited to, a (Zn,Fe)Fe₂O₄ powder.

Specific examples of the black inorganic pigment powder containing Cu include, but are not limited to, a Cu—Cr-based inorganic pigment powder and a Cu—Fe-based inorganic pigment powder. Specific examples of the Cu—Cr-based inorganic pigment powder include, but are not limited to, a Cu(Cr,Mn)₂O₄ powder and a Cu—Cr—Mn powder. Specific examples of the Cu—Fe-based inorganic pigment powder include, but are not limited to, a Cu—Fe—Mn powder.

Such color pigments may be used alone or as a combination of one or more types thereof.

The content of the color pigment in the colored layer 3 is preferably from 10 to 60 mass %, in particular, from 15 to 50 mass %. If the content of the color pigment is excessively small, the light shielding property and the design property of the glass article 1 are likely to be impaired. On the other hand, if the content of the color pigment is excessively large, the heat resistance and the impact resistance of the glass article 1 are likely to decrease. Note that the content of the color pigment is a content relative to the total amount of all materials included in the colored layer 3, which corresponds to 100 mass %.

An average particle size of the color pigment is preferably from 0.05 to 0.4 μm or greater, in particular, from 0.1 to 0.3 μm. If the average particle size of the color pigment is excessively small, a paste tends to have a high viscosity in a manufacturing method described below, and the printability tends to deteriorate. On the other hand, if the average particle size of the color pigment is excessively large, the heat resistance and the impact resistance are likely to deteriorate. Note that the average particle size refers to an average particle size calculated based on a volume base distribution determined by using laser diffraction.

An extender pigment contained in the colored layer 3 is an inorganic pigment powder different from the color pigment. The extender pigment is not particularly limited, but examples thereof may include talc and mica.

Such extender pigments may be used alone or as a combination of one or more types thereof.

The content of the extender pigment in the colored layer 3 is preferably from 5 to 60 mass %, and in particular from 10 to 40 mass %. If the content of the extender pigment is excessively small, the mechanical strength of the glass article 1 is likely to be deteriorate. On the other hand, if the content of the extender pigment is excessively large, the heat resistance and the impact resistance of the glass article 1 are likely to deteriorate. Note that the content of the extender pigment is a content relative to the total amount of all materials included in the colored layer 3, which corresponds to 100 mass %.

An average particle size of the extender pigment is preferably from 5 to 50 μm, and in particular from 10 to 45 μm. If the average particle size of the extender pigment is excessively small, a paste tends to have a high viscosity in a manufacturing method described below, and the printability is likely to deteriorate. On the other hand, if the average particle size of the extender pigment is excessively large, the heat resistance and the impact resistance are likely to deteriorate.

The total content of the color pigment and the extender pigment in the colored layer 3 is preferably from 15 to 70 mass %, and in particular from 25 to 60 mass %. If the total content of the color pigment and the extender pigment is excessively small, the design property and the mechanical strength of the glass article 1 are likely to deteriorate. On the other hand, if the total content of the color pigment and the extender pigment is excessively large, the heat resistance and the impact resistance of the glass article 1 are likely to deteriorate. Note that the total content of the color pigment and the extender pigment is a content relative to the total amount of all materials included in the colored layer 3, which corresponds to 100 mass %.

A thickness of the colored layer 3 is not particularly limited. The thickness of the colored layer 3 may be appropriately set depending on the light transmittance of the colored layer 3 or the like. The thickness of the colored layer 3 may be, for example, from 1 to 15 μm.

Manufacturing Method of Glass Article 1

The glass article 1 may be manufactured, for example, by the following manufacturing method.

Firstly, paste containing a silicone resin, a color pigment powder, and an extender pigment powder is prepared. The paste is prepared such that the content ratio of the color pigment powder to the extender pigment powder (color pigment/extender pigment) in the paste is greater than 1 to 6. Next, the prepared paste is directly applied on the back surface 2 b of the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet 2 and dried. As a result, it is possible to manufacture the glass article 1. Note that depending on the composition of the colored layer 3, the glass article 1 may be obtained by performing firing after the drying.

Note that the glass article 1 may include an image display portion, a video display portion, a stereoscopic image display portion, a stereoscopic video display portion, a radio wave reception portion, a radio wave transmission portion, and a sound wave generation portion.

The glass article 1 as described above is suitable for a top plate.

Example 1

The present invention will now be described based on Examples below, but the present invention is not limited to Examples. Tables 1 to 30 list Examples of the present invention (Sample Nos. 1 to 98) and Comparative Example (Sample No. 99).

TABLE 1 No. 1 No. 2 No. 3 No. 4 No. 5 Composition SiO₂ 65.9 64.7 65.6 65.6 65.1 [wt %] Al₂O₃ 22.3 21.9 22.2 22.2 22.0 B₂O₃ 0.00 0.00 0.00 0.00 0.01 P₂O₅ 1.40 1.38 1.38 1.38 1.38 Li₂O 3.71 3.64 3.70 3.70 4.10 Na₂O 0.40 0.39 0.39 0.39 0.39 K₂O 0.30 0.30 0.30 0.30 0.30 MgO 0.70 0.69 0.20 0.20 0.40 CaO 0.00 0.00 0.00 0.00 0.00 SrO 0.00 0.00 0.00 0.00 0.00 BaO 1.20 1.18 1.18 1.18 1.18 ZnO 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.0023 0.0044 0.0009 0.0015 0.0030 SnO₂ 0.69 1.81 1.40 1.40 1.40 ZrO₂ 3.39 4.06 3.70 3.70 3.70 Fe₂O₃ 0.0153 0.0149 0.0154 0.0152 0.0151 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 0.00 Composition Pt 0.03 0.03 0.03 0.03 0.03 [ppm] Rh 0.02 0.02 0.02 0.02 0.02 Pt + Rh 0.05 0.05 0.05 0.05 0.05 Sn/(P + B + Zr + Ti + Sn) 0.126 0.249 0.216 0.216 0.216 Al/(Zr + Sn) 5.46 3.72 4.35 4.35 4.31 (Mg + Zn)/Li 0.189 0.189 0.054 0.054 0.098 Sn/(Zr + Sn) 0.17 0.31 0.27 0.27 0.27 (Si + Al)/Li 23.76 23.76 23.73 23.73 21.24 (Si + Al)/Sn 127.74 47.90 62.71 62.71 62.21 (Li + Na + K)/Zr 1.30 1.07 1.19 1.19 1.29 Ti/Zr 0.0007 0.0011 0.0002 0.0004 0.0008 Ti/(Ti + Fe) 0.131 0.228 0.055 0.090 0.166 Na + K + Ca + Sr + Ba 1.91 1.87 1.87 1.87 1.87 (Mg + Ca + Sr + Ba)/Zr 0.56 0.46 0.37 0.37 0.43 (Mg + Ca + Sr + Ba)/(Li + Na + K) 0.43 0.43 0.31 0.31 0.33 Sb + As 0.00 0.00 0.00 0.00 0.00 Before crystallization Transmittance  200 nm Not measured 44.9 54.1 54.1 53.9 [%] 3 mm  250 nm Not measured 17.0 19.5 19.5 19.8 thickness  300 nm Not measured 24.1 29.9 29.9 32.3  325 nm Not measured 65.6 69.6 69.6 70.9  350 nm Not measured 84.4 86.1 86.1 86.2  380 nm Not measured 89.5 90.3 90.3 90.2  800 nm Not measured 91.5 91.8 91.8 91.7 1200 nm Not measured 91.7 91.9 91.9 91.7 L* Not measured 96.6 96.7 96.7 96.6 a* Not measured −0.1 −0.1 −0.1 −0.1 b* Not measured 0.2 0.2 0.2 0.2 Low Strain point [° C.] Not measured Not measured Not measured Not measured Not measured temperature Annealing point [° C.] Not measured Not measured Not measured Not measured Not measured viscosity Glass transition point [° C.] Not measured Not measured Not measured Not measured Not measured High 10{circumflex over ( )}4[° C.] Not measured Not measured Not measured Not measured Not measured temperature 10{circumflex over ( )}3[° C.] Not measured Not measured Not measured Not measured Not measured viscosity 10{circumflex over ( )}2.5[° C.] Not measured Not measured Not measured Not measured Not measured 10{circumflex over ( )}2[° C.] Not measured Not measured Not measured Not measured Not measured Liquidus temperature (° C.) Not measured Not measured Not measured Not measured Not measured Liquidus viscosity [—] Not measured Not measured Not measured Not measured Not measured α[×10⁻⁷/° C.] 30-380° C. Not measured 39.6 Not measured Not measured Not measured Density [g/cm3] Not measured Not measured Not measured Not measured Not measured β-OH[/mm] 0.12 0.12 0.12 0.12 0.12

TABLE 2 No. 1 No. 2 No. 3 No. 4 No. 5 After crystallization Crystallization 810° C.-60 h 810° C.-60 h 810° C.-10 h 810° C.-20 h 810° C.-20 h condition 920° C.-3 h  920° C.-3 h  920° C.-3 h  920° C.-3 h  920° C.-3 h  Transmittance 200 nm 26.0 27.0 29.9 35.0 27.0 [%] 250 nm 26.0 14.0 17.3 20.0 14.0 3 mm 300 nm 36.5 15.9 20.8 22.8 17.1 thickness 325 nm 55.1 53.5 62.0 63.7 58.3 350 nm 55.1 77.6 80.6 81.7 78.3 380 nm 69.7 84.4 85.7 86.4 84.2 800 nm 89.0 91.1 91.3 91.4 91.1 1200 nm  90.9 91.1 91.6 91.4 91.2 L* 94.4 95.8 95.8 96.1 95.8 a* −0.1 −0.1 −0.1 0.0 −0.1 b* 3.4 1.3 1.4 1.0 1.3 Precipitated β-Q β-Q β-Q β-Q β-Q crystal Average crystallite Not Not Not 45 Not size [nm] measured measured measured measured α[×10⁻⁷/° C.] 30-380° C. −0.9 −0.4 Not Not Not measured measured measured α[×10⁻⁷/° C.] 30-750° C. 0.9 0.9 Not Not Not measured measured measured Density Not Not Not Not Not [g/cm3] measured measured measured measured measured Young's Modulus 92 93 Not Not Not [GPa] measured measured measured Modulus of rigidity 37 38 Not Not Not [GPa] measured measured measured Poisson's 0.23 0.22 Not Not Not ratio measured measured measured Appearance Colorless and Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm Not 39.8 44.7 35.4 49.9 measured 250 nm Not 17.6 11.3 −3.0 29.4 measured 300 nm Not 34.2 30.3 23.7 47.1 measured 325 nm Not 18.6 11.0 8.4 17.8 measured 350 nm Not 8.0 6.3 5.1 9.2 measured 380 nm Not 5.8 5.0 4.2 6.6 measured 800 nm Not 0.4 0.5 0.4 0.6 measured 1200 nm  Not 0.4 0.5 0.4 0.6 measured

TABLE 3 No. 6 No. 7 No. 8 No. 9 No. 10 No. 11 No. 12 Composition SiO₂ 66.0 66.1 66.2 66.7 63.5 66.6 66.8 [wt %] Al₂O₃ 22.4 22.4 22.4 22.2 23.5 22.3 21.8 B₂O₃ 0.00 0.00 0.00 0.82 0.00 0.00 0.00 P₂O₅ 1.42 1.42 1.39 0.00 2.51 1.40 1.37 Li₂O 3.73 3.73 3.74 2.20 2.92 3.74 3.54 Na₂O 0.08 0.36 0.38 0.01 0.80 0.00 0.39 K₂O 0.30 0.00 0.00 0.01 0.05 0.00 0.00 MgO 0.69 0.69 0.69 0.00 1.14 0.69 0.77 CaO 0.01 0.01 0.00 0.02 0.01 0.01 0.01 SrO 0.00 0.00 0.01 0.34 0.00 0.00 0.00 BaO 0.00 0.00 0.00 0.48 0.12 0.01 0.00 ZnO 0.00 0.00 0.00 1.66 0.00 0.01 0.00 TiO₂ 0.0065 0.0042 0.0031 0.0000 0.1990 0.0055 0.0049 SnO₂ 1.42 1.43 1.34 1.63 1.75 1.40 1.27 ZrO₂ 3.85 3.83 3.84 3.90 3.72 3.81 2.96 Fe₂O₃ 0.0068 0.0087 0.0099 0.0284 0.0081 0.0084 0.0075 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Composition Pt 1.5 1.5 1.5 Not 1.5 1.5 1.5 [ppm] measured Rh 0.02 0.02 0.02 Not 0.02 0.02 0.02 measured Pt + Rh 1.52 1.52 1.52 Not 1.52 1.52 1.52 measured Sn/(P + B + 0.212 0.214 0.204 0.257 0.214 0.212 0.227 Zr + Ti + Sn) Al/(Zr + Sn) 4.25 4.26 4.32 4.01 4.30 4.28 5.15 (Mg + Zn)/Li 0.185 0.185 0.184 0.755 0.390 0.187 0.218 Sn/(Zr + Sn) 0.27 0.27 0.26 0.29 0.32 0.27 0.30 (Si + Al)/Li 23.70 23.73 23.69 40.41 29.79 23.77 25.03 (Si + Al)/Sn 62.25 61.89 66.12 54.54 49.71 63.50 69.76 (Li + Na + 1.07 1.07 1.07 0.57 1.01 0.98 1.33 K)/Zr Ti/Zr 0.0017 0.0011 0.0008 0.0000 0.0535 0.0014 0.0017 Ti/(Ti + Fe) 0.489 0.326 0.238 0.000 0.961 0.396 0.395 Na + K + Ca + 0.39 0.37 0.39 0.86 0.98 0.02 0.40 Sr + Ba (Mg + Ca + 0.18 0.18 0.18 0.21 0.34 0.19 0.26 Sr + Ba)/Zr (Mg + Ca + 0.17 0.17 0.17 0.38 0.34 0.19 0.20 Sr + Ba)/(Li + Na + K) Sb + As 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Before crystallization Transmittance 200 nm 65.9 67.4 65.7 Not Not 77.2 80.7 [%] measured measured 3 mm 250 nm 21.2 21.3 21.3 Not Not 22.3 22.8 thickness measured measured 300 nm 30.4 30.1 30.3 Not Not 29.1 32.0 measured measured 325 nm 69.0 68.8 69.0 Not Not 67.8 69.2 measured measured 350 nm 85.4 85.2 85.3 Not Not 85.0 85.2 measured measured 380 nm 89.8 89.7 89.8 Not Not 89.7 89.8 measured measured 800 nm 91.6 91.6 91.6 Not Not 91.6 91.6 measured measured 1200 nm  91.6 91.6 91.6 Not Not 91.5 91.6 measured measured L* 96.6 96.6 96.6 Not Not 96.6 96.7 measured measured a* −0.1 −0.1 −0.1 Not Not −0.1 −0.1 measured measured b* 0.3 0.3 0.3 Not Not 0.3 0.4 measured measured Low Strain point 687 683 684 Not Not Not Not temperature [° C.] measured measured measured measured viscosity Annealing point 745 741 742 Not Not Not Not [° C.] measured measured measured measured Glass transition 728 730 728 Not Not 745 740 point [° C.] measured measured High 10{circumflex over ( )}4[° C.] 1353 1351 1352 Not Not 1358 1368 temperature measured measured viscosity 10{circumflex over ( )}3[° C.] 1530 1528 1531 Not Not 1537 1549 measured measured 10{circumflex over ( )}2.5[° C.]   1643 1641 1644 Not Not 1650 1662 measured measured 10{circumflex over ( )}2[° C.] 1780 1777 1780 Not Not 1786 1795 measured measured Liquidus 1489 1486 1489 Not Not Not Not temperature (° C.) measured measured measured measured Liquidus 3.20 3.21 3.21 Not Not Not Not viscosity [—] measured measured measured measured α[×10⁻⁷/° C.] 30-380° C. 38.2 38.7 38.6 Not Not 36.4 37.5 measured measured Density 2.442 2.442 2.441 Not Not 2.441 2.444 [g/cm3] measured measured β-OH[/mm] 0.15 0.15 0.15 0.15 015 0.15 0.15

TABLE 4 No. 6 No. 7 No. 8 No. 9 No. 10 No. 11 No. 12 After crystallization Crystallization 840° C.-3 h 840° C.-3 h 840° C.-3 h 810° C.-30 h 825° C.-30 h 840° C.-3 h 810° C.-3 h condition 890° C.-1 h 890° C.-1 h 890° C.-1 h 890° C.-3 h  905° C.-3 h  890° C.-1 h 920° C.-1 h Transmittance 200 nm 26.8 25.4 22.7 Not Not 26.5 35.3 [%] measured measured 3 mm 250 nm 12.1 1

.5 11.7 Not Not 12.1 16.1 thickness measured measured 300 nm 26.8 25.4 22.7 Not Not 26.5 35.3 measured measured 325 nm 56.4 54.

55.7 Not Not 52.7 59.2 measured measured 350 nm 77.2 75.5 76.7 Not Not 75.3 74.4 measured measured 380 nm 83.2 8

.8 82.9 Not Not 82.1 79.6 measured measured 800 nm 90.7 90.5 90.6 Not Not 90.5 89.9 measured measured 1200 nm  90.8 90.7 90.9 Not Not 90.6 90.7 measured measured L* 95.5 95.2 95.4 Not Not 95.3 94.7 measured measured a* 0.1 0.1 0.1 Not Not 0.1 0.1 measured measured b* 1.6 1.9 1.7 Not Not 1.7 2.3 measured measured Precipitated β-Q β-Q β-Q β-Q β-Q β-Q β-Q crystal Average crystallite Not Not 45 Not Not Not Not size [nm] measured measured measured measured measured measured α[×10⁻⁷/° C.] 30-380° C. −5.2 −5.1 −5.0 Not Not −4.0 −2.5 measured measured α[×10⁻⁷/° C.] 30-750° C. −3.7 −3.6 −3.6 Not Not −3.7 −1.7 measured measured Density 2.531 2.534 2.534 Not Not 2.542 2.535 [g/cm3] measured measured Young's Modulus Not Not Not Not Not Not Not [GPa] measured measured measured measured measured measured measured Modulus of rigidity Not Not Not Not Not Not Not [GPa] measured measured measured measured measured measured measured Poisson's Not Not Not Not Not Not Not ratio measured measured measured measured measured measured measured Appearance Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm 59.3 62.3 65.5 Not Not 65.7 56.2 measured measured 250 nm 43.0 46.1 44.8 Not Not 45.5 29.4 measured measured 300 nm 11.7 15.7 25.1 Not Not 8.9 −10.5 measured measured 325 nm 18.3 2

.3 19.3 Not Not 22.3 14.4 measured measured 350 nm 9.6 1

.4 10.0 Not Not 11.3 12.6 measured measured 380 nm 7.3 8.8 7.7 Not Not 8.5 11.4 measured measured 800 nm 1.0 1.2 1.1 Not Not 1.2 1.9 measured measured 1200 nm  0.9 1.0 0.7 Not Not 0.9 1.0 measured measured

indicates data missing or illegible when filed

TABLE 5 No. 13 No. 14 No. 15 No. 16 No. 17 No. 18 No. 19 Composition SiO₂ 65.7 65.9 67.2 65.5 65.5 66.0 65.8 [wt %] Al₂O₃ 21.7 22.2 21.6 22.0 22.0 22.3 22.1 B₂O₃ 0.001 0.00 0.00 0.00 0.00 0.00 0.00 P₂O₅ 1.37 1.40 1.41 1.39 1.42 1.42 1.38 Li₂O 3.63 4.02 3.30 3.67 3.67 3.70 3.70 Na₂O 0.87 0.37 0.37 0.01 0.37 0.39 0.09 K₂O 0.10 0.00 0.00 0.30 0.00 0.30 0.001 MgO 0.68 1.52 1.23 0.65 0.68 0.68 0.68 CaO 0.00 0.35 0.00 0.01 0.01 0.01 0.01 SrO 0.01 0.001 0.00 0.00 0.00 0.00 0.00 BaO 1.18 0.00 0.30 1.18 1.18 0.001 1.17 ZnO 0.00 0.01 0.01 0.001 0.00 0.00 0.00 TiO₂ 0.0175 0.0080 0.1560 0.0782 0.0095 0.0014 0.0147 SnO₂ 1.17 0.45 1.18 1.39 1.39 1.41 1.31 ZrO₂ 2.93 3.90 1.89 3.75 3.73 3.80 3.77 Fe₂O₃ 0.0045 0.0033 0.0021 0.0005 0.0072 0.0085 0.0093 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Composition Pt 1.4 0.2 1.4 1.5 1.5 1.5 1.5 [ppm] Rh 0.03 0.03 0.03 0.02 0.02 0.02 0.02 Pt + Rh 1.43 0.23 1.43 1.52 1.52 1.52 1.52 Sn/(P + B + 0.213 0.078 0.255 0.210 0.212 0.213 0.202 Zr + Ti + Sn) Al/(Zr + Sn) 5.29 5.10 7.04 4.28 4.30 4.28 4.35 (Mg + Zn)/Li 0.187 0.381 0.377 0.177 0.185 0.184 0.184 Sn/(Zr + Sn) 0.29 0.10 0.38 0.27 0.27 0.27 0.26 (Si + Al)/Li 24.08 21.92 26.91 23.84 23.84 23.86 23.76 (Si + Al)/Sn 74.70 195.78 75.25 62.95 62.95 62.62 67.10 (Li + Na + 1.57 1.13 1.94 1.06 1.08 1.16 1.01 K)/Zr Ti/Zr 0.0060 0.0021 0.0825 0.0209 0.0025 0.0004 0.0039 Ti/(Ti + Fe) 0.795 0.708 0.987 0.994 0.569 0.141 0.613 Na + K + Ca + 2.16 0.72 0.67 1.50 1.56 0.70 1.27 Sr + Ba (Mg + Ca + 0.64 0.48 0.81 0.49 0.50 0.18 0.49 Sr + Ba)/Zr (Mg + Ca + 0.41 0.43 0.42 0.46 0.46 0.16 0.49 Sr + Ba)/(Li + Na + K) Sb + As 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Before crystallization Transmittance 200 nm 79.6 Not Not 62.3 61.1 62.8 69.0 [%] measured measured 3 mm 250 nm 22.3 Not Not 20.7 20.6 20.9 21.7 thickness measured measured 300 nm 33.5 Not Not 30.7 30.0 30.3 30.4 measured measured 325 nm 71.2 Not Not 68.9 68.7 69.2 67.9 measured measured 350 nm 86.1 Not Not 85.0 85.1 85.4 84.5 measured measured 380 nm 90.2 Not Not 89.5 89.6 89.8 89.3 measured measured 800 nm 91.7 Not Not 91.6 91.5 91.5 91.5 measured measured 1200 nm  91.7 Not Not 91.6 91.5 91.6 91.6 measured measured L* 96.7 Not Not 96.6 96.6 96.6 96.5 measured measured a* −0.1 Not Not −0.1 −0.1 −0.1 −0.1 measured measured b* 0.3 Not Not 0.4 0.4 0.3 0.4 measured measured Low Strain point Not Not Not 679 682 682 687 temperature [° C.] measured measured measured viscosity Annealing point Not Not Not 738 741 740 745 [° C.] measured measured measured Glass transition Not Not Not 727 728 726 730 point [° C.] measured measured measured High 10{circumflex over ( )}4[° C.] Not Not Not 1350 1348 1351 1350 temperature measured measured measured viscosity 10{circumflex over ( )}3[° C.] Not Not Not 1528 1525 1531 1527 measured measured measured 10{circumflex over ( )}2.5[° C.]   Not Not Not 1639 1636 1642 1640 measured measured measured 10{circumflex over ( )}2[° C.] Not Not Not 1772 1769 1773 1774 measured measured measured Liquidus Not Not 1378 1492 1488 1491 1479 temperature (° C.) measured measured Liquidus Not Not Not 3.18 3.19 3.20 3.24 viscosity [—] measured measured measured α[×10⁻⁷/° C.] 30-380° C. Not Not Not 39.2 39.7 39.4 38.4 measured measured measured Density 2.443 Not Not 2.462 2.461 2.440 2.461 [g/cm3] measured measured β-Cl—[/mm] 0.13 0.13 0.13 0.13 0.13 0.13 0.13

TABLE 6 No. 13 No. 14 No. 15 No. 16 No. 17 No. 18 No. 19 After crystallization Crystallization 780° C.-3 h 780° C.-3 h 780° C.-12 h 855° C.-3 h 840° C.-3 h 855° C.-3 h 840° C.-3 h condition 905° C.-1 h 890° C.-1 h 890° C.-1 h  920° C.-1 h 890° C.-1 h 920° C.-1 h 890° C.-1 h Transmittance 200 nm 37.2 Not Not 28.9 23.5 30.0 26.1 [%] measured measured 3 mm 250 nm 19.0 Not Not 15.2 13.8 15.3 13.9 thickness measured measured 300 nm 37.2 Not Not 28.9 23.5 30.0 26.1 measured measured 325 nm 64.4 Not Not 59.8 58.1 49.8 53.3 measured measured 350 nm 80.2 Not Not 77.0 76.8 67.1 74.3 measured measured 380 nm 85.1 Not Not 82.3 82.5 74.3 80.8 measured measured 800 nm 90.9 Not Not 90.4 90.5 90.2 90.2 measured measured 1200 nm  91.2 Not Not 90.6 90.9 90.8 90.6 measured measured L* 95.8 Not Not 95.3 95.3 95.3 95.4 measured measured a* 0.0 Not Not 0.1 0.1 0.1 0.0 measured measured b* 1.2 Not Not 1.8 1.8 1.8 1.9 measured measured Precipitated β-Q β-Q β-Q β-Q β-Q β-Q β-Q crystal Average crystallite Not Not Not Not Not Not Not size [nm] measured measured measured measured measured measured measured α[×10⁻⁷/° C.] 30-380° C. −3.0 −1.3 −0.8 −3.4 −3.5 −3.7 −5.0 α[×10⁻⁷/° C.] 30-750° C. −2.7 −0.8 −0.5 −1.8 −1.9 −2.0 −3.5 Density 2.530 Not 2.521 2.544 2.544 2.521 2.551 [g/cm3] measured Young's Modulus Not Not Not Not Not Not Not [GPa] measured measured measured measured measured measured measured Modulus of rigidity Not Not Not Not Not Not Not [GPa] measured measured measured measured measured measured measured Poisson's Not Not Not Not Not Not Not ratio measured measured measured measured measured measured measured Appearance Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm 53.2 Not Not 53.7 61.5 52.2 62.2 measured measured 250 nm 16.8 Not Not 26.7 33.3 26.4 36.0 measured measured 300 nm −11.2 Not Not 6.1 21.5 0.8 14.3 measured measured 325 nm 9.5 Not Not 13.3 15.4 28.0 21.5 measured measured 350 nm 6.9 Not Not 9.5 9.7 21.4 12.0 measured measured 380 nm 5.6 Not Not 8.1 8.0 17.3 9.5 measured measured 800 nm 0.8 Not Not 1.3 1.1 1.5 1.3 measured measured 1200 nm  0.6 Not Not 1.1 0.7 0.8 1.0 measured measured

TABLE 7 No. 20 No. 21 No. 22 No. 23 No. 24 No. 25 No. 26 Composition SiO₂ 66.6 65.0 66.1 67.1 68.0 65.7 67.0 [wt %] Al₂O₃ 21.9 22.0 21.7 22.2 22.6 21.9 22.1 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.60 0.00 P₂O₅ 1.39 1.38 1.36 1.41 0.00 2.55 1.40 Li₂O 3.66 3.67 3.63 3.69 3.74 3.64 3.62 Na₂O 0.40 0.40 0.41 0.07 0.09 0.07 0.37 K₂O 0.00 0.30 0.02 0.00 0.00 0.00 0.00 MgO 0.68 0.69 0.68 1.23 0.40 1.23 1.23 CaO 0.01 0.00 0.03 0.01 0.02 0.01 0.00 SrO 0.00 0.00 0.43 0.00 0.00 0.00 0.01 BaO 1.17 1.19 1.16 0.00 0.00 0.00 0.00 ZnO 0.00 0.00 0.00 0.00 0.90 0.00 0.00 TiO₂ 0.0210 0.3630 0.0235 0.0001 0.0141 0.0385 0.0720 SnO₂ 1.23 1.36 1.21 1.41 1.22 1.25 1.29 ZrO₂ 2.81 3.71 3.01 3.02 3.06 3.06 3.01 Fe₂O₃ 0.0039 0.0000 0.0131 0.0088 0.0003 0.0091 0.0029 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Composition Pt 1.5 0.01 1.5 1.4 1.4 1.4 1.4 [ppm] Rh 0.02 0.01 0.02 0.02 0.03 0.03 0.03 Pt + Rh 1.52 0.02 1.52 1.42 1.43 1.43 1.43 Sn/(P + B + 0.226 0.200 0.216 0.24 0.284 0.167 0.223 Zr + Ti + Sn) Al/(Zr + Sn) 5.42 4.33 5.14 5.0 5.28 5.08 5.14 (Mg + Zn)/Li 0.186 0.188 0.187 0.333 0.348 0.338 0.340 Sn/(Zr + Sn) 0.30 0.27 0.29 0.32 0.29 0.29 0.30 (Si + Al)/Li 24.18 23.69 24.19 24.20 24.22 24.07 24.61 (Si + Al)/Sn 71.95 63.93 72.56 63.33 74.26 70.08 69.07 (Li + Na + 1.44 1.18 1.35 1.25 1.25 1.21 1.33 K)/Zr Ti/Zr 0.0075 0.0978 0.0078 0.0000 0.0046 0.0126 0.0239 Ti/(Ti + Fe) 0.843 1.000 0.642 0.011 0.979 0.809 0.961 Na + K + Ca + 4.75 4.76 5.18 5.00 4.25 4.95 5.23 Sr + Ba (Mg + Ca + 0.66 0.51 0.76 0.41 0.14 0.41 0.41 Sr + Ba)/Zr (Mg + Ca + 0.46 0.43 0.57 0.33 0.11 0.34 0.31 Sr + Ba)/(Li + Na + K) Sb + As 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Before crystallization Transmittance 200 nm 80 Not 70 81 78 80 82 [%] measured 3 mm 250 nm 23 Not 19 24 23 24 24 thickness measured 300 nm 35 Not 19 34 33 30 34 measured 325 nm 71 Not 56 72 71 67 71 measured 350 nm 86 Not 80 86 86 85 86 measured 380 nm 90 Not 88 90 90 90 90 measured 800 nm 92 Not 91 92 92 91 92 measured 1200 nm  92 Not 91 92 92 92 92 measured L* 96.7 Not 96.6 96.7 96.7 96.6 96.6 measured a* −0.1 Not −0.1 0.0 0.0 0.0 0.0 measured b* 0.3 Not 0.4 0.3 0.3 0.3 0.3 measured Low Strain point 683 Not 683 Not Not Not Not temperature [° C.] measured measured measured measured measured viscosity Annealing point 742 Not 742 Not Not Not Not [° C.] measured measured measured measured measured Glass transition 737 Not 731 738 743 731 Not point [° C.] measured measured High 10{circumflex over ( )}4[° C.] 1362 Not 1362 1356 1352 1357 1358 temperature measured viscosity 10{circumflex over ( )}3[° C.] 1544 Not 1544 1537 1532 1538 1538 measured 10{circumflex over ( )}2.5[° C.]   1658 Not 1656 1649 1645 1650 1653 measured 10{circumflex over ( )}2[° C.] 1793 Not 1789 1778 1778 1780 1790 measured Liquidus 1423 Not 1442 Not Not Not Not temperature (° C.) measured measured measured measured measured Liquidus 3.63 Not 3.53 Not Not Not Not viscosity [—] measured measured measured measured measured α[×10⁻⁷/° C.] 30-380° C. 39.2 Not 39.3 36.6 36.9 36.5 36.9 measured Density 2.441 Not 2.445 2.431 2.438 2.420 2.430 [g/cm3] measured β-OH[/mm] 0.18 0.18 0.18 0.18 0.18 0.18 0.18

TABLE 8 No. 20 No. 21 No. 22 No. 23 No. 24 No. 25 No. 26 After crystallization Crystallization 840° C.-3 h 810° C.-20 h 810° C.-3 h 780° C.-3 h 780° C.-3 h 780° C.-3 h 780° C.-3 h condition 890° C.-1 h 920° C.-3 h  920° C.-1 h 890° C.-1 h 890° C.-1 h 890° C.-1 h 890° C.-1 h Transmittance 200 nm 41 Not 34 30 26 29 33 [%] measured 3 mm 250 nm 17 Not 10 14 13 11 13 thickness measured 300 nm 41 Not 34 30 26 29 33 measured 325 nm 54 Not 44 56 55 55 61 measured 350 nm 69 Not 66 76 75 76 79 measured 380 nm 74 70 76 82 81 83 84 800 nm 90 91 90 91 91 91 91 1200 nm  91 Not 90 91 91 91 91 measured L* 93.9 Not 94.8 95.4 95.3 95.6 95.6 measured a* 0.2 Not 0.0 0.1 0.0 0.0 0.1 measured b* 3.4 Not 2.7 1.7 1.9 1.5 1.4 measured Precipitated β-Q β-Q β-Q β-Q β-Q β-Q β-Q crystal Average crystallite Not Not Not Not Not Not Not size [nm] measured measured measured measured measured measured measured α[×10⁻⁷/° C.] 30-380° C. −5.4 −0.2 −5.0 −2.8 −2.5 −2.4 −1.1 α[×10⁻⁷/° C.] 30-750° C. −4.0 −0.9 −3.4 −2.6 −1.9 −2.5 −0.8 Density 2.520 Not 2.529 2.529 2.534 2.527 2.523 [g/cm3] measured Young's Modulus Not Not Not Not Not Not Not [GPa] measured measured measured measured measured measured measured Modulus of rigidity Not Not Not Not Not Not Not [GPa] measured measured measured measured measured measured measured Poisson's Not Not Not Not Not Not Not ratio measured measured measured measured measured measured measured Appearance Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm 49.3 Not 51.1 62.8 66.5 64.5 59.8 measured 250 nm 24.3 Not 47.7 41.5 42.8 54.3 43.9 measured 300 nm −16.4 Not −76.5 12.6 21.0 4.2 2.2 measured 325 nm 23.8 Not 22.2 21.6 22.4 19.0 13.6 measured 350 nm 20.1 Not 18.1 12.0 12.8 9.6 8.2 measured 380 nm 17.3 Not 13.7 8.9 9.6 7.1 6.6 measured 800 nm 2.1 Not 1.3 1.3 1.1 0.8 1.0 measured 1200 nm  1.0 Not 1.4 0.9 0.9 0.6 0.9 measured

TABLE 9 No. 27 No. 28 No. 29 No. 30 No. 31 No. 32 No. 33 Composition SiO₂ 66.5 67.4 [wt %] Al₂O₃ 21.8 22.3 B₂O₃ 0.00 0.00 P₂O₅ 1.40 1.33 Li₂O 3.63 3.68 Na₂O 0.41 0.37 K₂O 0.00 0.00 MgO 0.69 1.24 CaO 0.00 0.00 SrO 0.00 0.00 BaO 1.18 0.00 ZnO 0.01 0.00 TiO₂ 0.0182 0.0145 SnO₂ 1.36 1.13 ZrO₂ 2.95 2.62 Fe₂O₃ 0.0018 0.0064 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Composition Pt 0 0.03 0.16 0.30 0.49 0.71 0.03 [ppm] Rh 0 0.02 0.09 0.06 0.07 0.10 0.22 Pt + Rh 0 0.05 0.25 0.36 0.56 0.81 0.25 Sn/(P + B + 0.237 0.222 Zr + Ti + Sn) Al/(Zr + Sn) 505 5.95 (Mg + Zn)/Li 0.194 0.337 Sn/(Zr + Sn) 0.32 0.30 (Si + Al)/Li 24.33 24.38 (Si + Al)/Sn 64.93

9.38 (Li + Na + 1.37 1.55 K)/Zr Ti/Zr 0.0052 0.0055 Ti/(Ti + Fe) 0.910 0.694 Na + K + Ca + 4.73 5.28 Sr + Ba (Mg + Ca + 0.64 0.47 Sr + Ba)/Zr (Mg + Ca + 0.47 0.31 Sr + Ba)/(Li + Na + K) Sb + As 0.00 0.00 Before crystallization Transmittance 200 nm 72.0 83.4 Not Not Not Not Not [%] measured measured measured measured measured 3 mm 250 nm 22.1 24.6 Not Not Not Not Not thickness measured measured measured measured measured 300 nm 35.3 45.9 Not Not Not Not Not measured measured measured measured measured 325 nm 72.6 76.6 Not Not Not Not Not measured measured measured measured measured 350 nm 86.8 87.5 Not Not Not Not Not measured measured measured measured measured 380 nm 90.4 90.3 Not Not Not Not Not measured measured measured measured measured 800 nm 91.6 91.7 Not Not Not Not Not measured measured measured measured measured 1200 mm  91.6 91.7 Not Not Not Not Not measured measured measured measured measured L* 96.7 96.6 Not Not Not Not Not measured measured measured measured measured a* 0.0 −0.1 Not Not Not Not Not measured measured measured measured measured b* 0.2 0.4 Not Not Not Not Not measured measured measured measured measured Low Strain point 683 Not Not Not Not Not Not temperature [° C.] measured measured measured measured measured measured viscosity Annealing point 742 Not Not Not Not Not Not [° C.] measured measured measured measured measured measured Glass transition 731 737 Not Not Not Not Not point [° C.] measured measured measured measured measured High 10{circumflex over ( )}4[° C.] 1362 1362 Not Not Not Not Not temperature measured measured measured measured measured viscosity 10{circumflex over ( )}3[° C.] 1544 1542 Not Not Not Not Not measured measured measured measured measured 10{circumflex over ( )}2.5[° C.]   1656 1655 Not Not Not Not Not measured measured measured measured measured 10{circumflex over ( )}2[° C.] 1789 1789 Not Not Not Not Not measured measured measured measured measured Liquidus 1442 1401 Not Not Not Not Not temperature (° C.) measured measured measured measured measured Liquidus 3.53 3.72 Not Not Not Not Not viscosity [—] measured measured measured measured measured α[×10⁻⁷/° C.] 30-380° C. 39.3 37.8 Not Not Not Not Not measured measured measured measured measured Density 2.444 2.422 Not Not Not Not Not [g/cm3] measured measured measured measured measured β-OH[/mm] 0.12 0.12 0.12 0.12 0.12 0.12 0.12

indicates data missing or illegible when filed

TABLE 10 No. 27 No. 28 No. 29 No. 30 No. 31 No. 32 No. 33 After crystallization Crystallization 780° C.-3 h 780° C.-3 h 780° C.-3 h 780° C.-3 h 780° C.-3 h 780° C.-3 h 780° C.-3 h condition 905° C.-1 h 890° C.-1 h 890° C.-1 h 890° C.-1 h 890° C.-1 h 890° C.-1 h 890° C.-1 h Transmittance 200 nm 34.9 30.6 37.5 36.7 36.7 35.9 30.6 [%] 250 nm 17.0 12.1 18.9 19.0 18.9 18.7 12.1 3 mm 300 nm 34.9 30.6 20.6 23.0 22.9 23.1 30.6 thickness 325 nm 69.9 61.9 59.7 62.2 60.7 60.5 61.9 350 nm 85.3 81.7 78.7 79.7 77.6 77.2 81.7 380 nm 88.9 87.0 91.1 91.1 90.8 90.7 87.0 800 nm 91.4 91.4 91.1 91.1 90.8 90.7 91.4 1200 nm  91.2 91.3 91.0 90.9 90.8 90.8 91.3 L* 96.3 96.2 95.9 95.9 95.6 95.5 96.2 a* 0.1 0.0 −0.1 −0.1 −0.1 −0.1 0.0 b* 0.4 0.7 1.2 1.1 1.5 1.6 0.7 Diffuse 600 nm Not 0.10 Not Not Not 0.53 Not transmittance measured measured measured measured measured [%] 800 nm Not 0.04 Not Not Not 0.23 Not 3 mm measured measured measured measured measured thickness 1200 nm  Not 0.03 Not Not Not 0.06 Not measured measured measured measured measured Precipitated β-Q β-Q β-Q β-Q β-Q β-Q β-Q crystal Average crystallite 38 Not Not Not Not Not Not size [nm] measured measured measured measured measured measured α[×10⁻⁷/° C.] 30-380° C. −5.0 −2.7 Not Not Not Not Not measured measured measured measured measured α[×10⁻⁷/° C.] 30-750° C. −3.4 −1.7 Not Not Not Not Not measured measured measured measured measured Density 2.530 2.515 Not Not Not Not Not [g/cm3] measured measured measured measured measured Young's Modulus Not Not Not Not Not Not Not [GPa] measured measured measured measured measured measured measured Modulus of rigidity Not Not Not Not Not Not Not [GPa] measured measured measured measured measured measured measured Poisson's Not Not Not Not Not Not Not ratio measured measured measured measured measured measured measured Appearance Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm 51.5 63.3 Not Not Not Not Not measured measured measured measured measured 250 nm 22.9 50.6 Not Not Not Not Not measured measured measured measured measured 300 nm 1.1 33.3 Not Not Not Not Not measured measured measured measured measured 325 nm 3.8 19.3 Not Not Not Not Not measured measured measured measured measured 350 nm 1.7 6.6 Not Not Not Not Not measured measured measured measured measured 380 nm 1.7 3.6 Not Not Not Not Not measured measured measured measured measured 800 nm 0.2 0.3 Not Not Not Not Not measured measured measured measured measured 1200 nm  0.4 0.5 Not Not Not Not Not measured measured measured measured measured

TABLE 11 No. 34 No. 35 No. 36 No. 37 No. 38 No. 39 No. 40 No. 41 No. 42 No. 43 Composition SiO₂ 66.5 66.2 [wt %] Al₂O₃ 22.0 22.2 B₂O₃ 0.00 0.00 P₂O₅ 1.42 1.40 Li₂O 3.50 2.35 Na₂O 0.40 0.40 K₂O 0.00 0.30 MgO 1.20 1.20 CaO 0.00 0.00 SrO 0.01 0.00 BaO 0.00 1.20 ZnO 0.00 0.00 TiO₂ 0.0058 0.0072 SnO₂ 1.33 1.30 ZrO₂ 3.00 2.99 Fe₂O₃ 0.0057 0.0066 Sb₂O₃ 0.00 0.00 As₂O₃ 0.00 0.00 Composition Pt 0.01 0.00 1.90 [ppm] Rh 0.03 0.00 0.05 Pt + Rh 0.04 0.00 1.95 Sn/(P + B + 0.231 0.228 Zr + Ti + Sn) Al/(Zr + Sn) 5.08 5.17 (Mg + Zn)/Li 0.343 0.511 Sn/(Zr + Sn) 0.31 0.30 (Si + Al)/Li 25.29 37.62 (Si + Al)/Sn 66.54 68.00 (Li + Na + 1.30 1.02 K)/Zr Ti/Zr 0.0019 0.0024 Ti/(Ti + Fe) 0.504 0.522 Na + K + Ca + 0.41 1.90 Sr + Ba (Mg + Ca + 0.40 0.80 Sr + Ba)/Zr (Mg + Ca + 0.31 0.79 Sr + Ba)/(Li + Na + K) Sb + As 0.00 0.00 Before crystallization Transmittance 200 nm 82.2 Not 81.5 [%] measured 3 mm 250 nm 25.0 Not 23.7 thickness measured 300 nm 36.2 Not 30.6 measured 325 nm 72.5 Not 68.1 measured 350 nm 86.3 Not 85.0 measured 380 nm 90.0 Not 89.9 measured 800 nm 91.6 Not 91.6 measured 1200 nm  91.7 Not 91.6 measured L* 96.6 Not 96.6 measured a* 0.0 Not −0.1 measured b* 0.3 Not 0.4 measured Low Strain point Not Not 695 temperature [° C.] measured measured viscosity Annealing point Not Not 754 [° C.] measured measured Glass transition 742 Not Not point [° C.] measured measured High 10{circumflex over ( )}4[° C.] Not Not 1364 temperature measured measured viscosity 10{circumflex over ( )}3[° C.] Not Not 1542 measured measured 10{circumflex over ( )}2.5[° C.]   Not Not 1658 measured measured 10{circumflex over ( )}2[° C.] Not Not Not measured measured measured Liquidus Not Not 1440 temperature (° C.) measured measured Liquidus Not Not 3.53 viscosity [—] measured measured α[×10⁻⁷/° C.] 30-380° C. 37.1 Not measured Density 2.431 2.460 [g/cm3] β-OH[/mm] 0.19 0.19

TABLE 12 No. 34 No. 35 No. 36 No. 37 No. 38 No. 39 No. 40 No. 41 No. 42 No. 43 After crystallization Crystallization 780° C.- 780° C.- 810° C.- 810° C.- 825° C.- 825° C.- 810° C.- 810° C.- 810° C.- 840° C.- condition 3 h 3 h 0.75 h 0.75 h 0.75 h 0.75 h 1.5 h 1.5 h 1.5 h 1.5 h 890° C.- 920° C.- 920° C.- 835° C.- 835° C.- 935° C.- 920° C.- 935° C.- 950° C.- 920° C.- 1 h 1 h 0.25 h 0.25 h 0.25 h 0.25 h 1 h 1 h 1 h 1 h Transmittance 200 nm 35.5 30.2 32.9 31.4 38.1 Not Not Not Not Not [%] measured measured measured measured measured 3 mm 250 nm 15.8 14.5 15.9 15.0 18.9 Not Not Not Not Not thickness measured measured measured measured measured 300 nm 35.5 22.0 23.4 23.9 23.2 23.2 23.2 24.3 23.5 20.2 325 nm 67.7 66.5 64.4 65.4 60.8 Not 60.8 47.1 50.1 45.7 measured 350 nm 84.5 83.8 81.5 81.9 78.2 Not 78.2 59.5 64.0 60.7 measured 380 nm 88.6 88.1 86.6 86.9 84.4 Not Not Not Not Not measured measured measured measured measured 800 nm 91.4 91.4 91.4 91.4 91.3 Not Not Not Not Not measured measured measured measured measured 1200 nm  91.3 91.3 91.3 91.3 91.5 Not Not Not Not Not measured measured measured measured measured L* 96.3 96.3 96.2 96.2 96.0 Not Not Not Not Not measured measured measured measured measured a* 0.0 0.0 0.0 0.0 0.1 Not Not Not Not Not measured measured measured measured measured b* 0.5 0.6 0.8 0.8 1.2 Not Not Not Not Not measured measured measured measured measured Precipitated β-Q β-Q β-Q β-Q β-Q β-Q β-Q β-Q β-Q β-Q crystal Average 41 Not Not Not Not Not Not Not Not Not crystallite measured measured measured measured measured measured measured measured measured size [nm] α[×10⁻⁷/° C.] 30-380° C. −1.7 −1.6 −1.7 Not Not Not 12.2 13.6 15.4 12.0 measured measured measured α[×10⁻⁷/° C.] 30-750° C. −1.1 −1.0 −1.1 Not Not Not Not Not Not Not measured measured measured measured measured measured measured Density 2.521 Not Not Not 2.521 2.514 Not Not Not Not [g/cm3] measured measured measured measured measured measured measured Young's Not Not Not Not Not Not Not Not Not Not Modulus measured measured measured measured measured measured measured measured measured measured [GPa] Modulus Not Not Not Not Not Not Not Not Not Not of rigidity measured measured measured measured measured measured measured measured measured measured [GPa] Poisson's Not Not Not Not Not Not Not Not Not Not ratio measured measured measured measured measured measured measured measured measured measured Appearance Colorless and Colorless and transparent transparent Rate of change before and after crystallization [%] Transmittance 200 nm 56.8 63.3 59.9 61.8 53.6 53.6 Not Not Not Not 3 mm measured measured measured measured thickness 250 nm 36.7 42.1 36.6 36.1 24.6 24.6 Not Not Not Not measured measured measured measured 300 nm 2.0 39.1 35.4 33.9 35.8 35.8 7.3 6.3 7.0 10.3 325 nm 6.6 8.3 11.1 9.8 16.1 16.1 7.3 21.0 18.0 22.4 350 nm 2.1 3.0 5.6 5.1 9.4 9.4 6.8 25.5 21.1 24.4 380 nm 1.8 2.1 3.8 3.5 6.2 6.2 Not Not Not Not measured measured measured measured 800 nm 0.1 0.2 0.1 0.2 0.2 0.2 Not Not Not Not measured measured measured measured 1200 nm  D. 0.5 0.5 0.5 0.2 0.2 Not Not Not Not measured measured measured measured

TABLE 13 No. 44 No. 45 No. 46 No. 47 No. 48 No. 49 No. 50 Composition SiO₂ 66.60 64.4 67.0 66.9 66.9 66.7 67.0 [wt %] Al₂O₃ 22.3 24.0 22.3 22.4 22.5 22.2 22.3 B₂O₃ 0.00 0.00 0.02 0.00 0.00 0.00 0.00 P₂O₅ 1.42 1.61 1.33 1.34 1.34 1.41 1.36 Li₂O 3.65 3.85 3.59 3.64 3.61 3.60 3.68 Na₂O 0.65 0.62 0.39 0.40 0.39 0.38 0.39 K₂O 0.01 0.01 0.005 0.007 0.001 0.0001 0.0032 MgO 1.05 1.38 1.26 1.31 1.32 1.32 1.17 CaO 0.00 0.00 0.002 0.01 0.00 0.0007 0.00 SrO 0.00 0.00 0.00 0.0012 0.01 0.00 0.00 BaO 0.45 0.00 0.03 0.00 0.01 0.01 0.0008 ZnO 0.0000 0.00 0.00 0.00 0.02 0.0001 0.00 TiO₂ 0.0181 0.0147 0.0044 0.0048 0.0132 0.0222 0.0058 SnO₂ 1.19 1.20 1.20 1.18 1.15 1.28 1.19 ZrO₂ 2.57 2.69 2.57 2.61 2.62 2.94 2.73 Fe₂O₃ 0.0132 0.0112 0.0085 0.0093 0.0095 0.0110 0.0082 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Composition Pt 0.01 0.00 0.15 0.15 0.15 0.15 0.15 [ppm] RF 0.02 0.01 0.05 0.05 0.05 0.05 0.05 Pt + Rh 0.03 0.01 0.20 0.20 0.20 0.20 0.20 Sn/(P + B + 0.229 0.218 0.234 0.230 0.224 0.226 0.225 Zr + Ti + Sn) Al/(Zr + Sn) 5.93 6.17 5.92 5.91 5.97 5.26 5.69 (Mg + Zn)/Li 0.288 0.358 0.351 0.360 0.372 0.367 0.318 Sn/(Zr + Sn) 0.32 0.31 0.32 0.31 0.31 0.30 0.30 (Si + Al)/Li 24.36 22.96 24.87 24.53 24.76 24.69 24.27 (Si + Al)/Sn 74.71 73.67 74.42 75.68 77.74 69.45 75.04 (Li + Na + K)/Zr 1.68 1.67 1.55 1.55 1.53 1.35 1.49 Ti/Zr 0.0070 0.0055 0.0017 0.0018 0.0050 0.0076 0.0021 Ti/(Ti + Fe) 0.578 0.568 0.341 0.340 0.581 0.669 0.414 Na + K + Ca + 1.11 0.63 0.43 0.42 0.41 0.39 0.39 Sr + Ba (Mg + Cu + 0.58 0.51 0.50 0.51 0.51 0.45 0.43 Sr +Ba)/Zr (Mg + Ca + 0.35 0.31 0.32 0.33 0.33 0.33 0.29 Sr + Ba)/(Li + Na + K) Sb + As 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Before crystallization Transmittance 200 nm Not Not Not Not Not Not Not [%] measured measured measured measured measured measured measured 3 mm 250 nm Not Not Not Not Not Not Not thickness measured measured measured measured measured measured measured 300 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 325 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 350 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 380 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 800 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 1200 nm  Not Not Not Not Not Not Not measured measured measured measured measured measured measured L* Not Not Not Not Not Not Not measured measured measured measured measured measured measured a* Not Not Not Not Not Not Not measured measured measured measured measured measured measured b* Not Not Not Not Not Not Not measured measured measured measured measured measured measured Low Strain point Not Not Not Not Not Not Not temperature [° C.] measured measured measured measured measured measured measured viscosity Annealing point Not Not Not Not Not Not Not [° C.] measured measured measured measured measured measured measured Glass Not Not Not Not Not Not Not transition measured measured measured measured measured measured measured point [° C.] High 10{circumflex over ( )}4[° C.] Not Not Not Not Not Not Not temperature measured measured measured measured measured measured measured viscosity 10{circumflex over ( )}3[° C.] Not Not Not Not Not Not Not measured measured measured measured measured measured measured 10{circumflex over ( )}2.5[° C.]   Not Not Not Not Not Not Not measured measured measured measured measured measured measured 10{circumflex over ( )}2[° C.] Not Not Not Not Not Not Not measured measured measured measured measured measured measured Liquidus Not Not Not Not Not Not Not temperature measured measured measured measured measured measured measured (° C.) Liquidus Not Not Not Not Not Not Not viscosity measured measured measured measured measured measured measured [—] α[×10⁻⁷/° C.] 30-380° C. Not Not Not Not Not Not Not measured measured measured measured measured measured measured Density Not Not 2.427 2.4275 2.429 2.435 Not [g/cm3] measured measured measured β —OH[/mm] 0.11 0.11 0.11 0.11 0.11 0.11 0.11

TABLE 14 No. 44 No. 45 No. 46 No. 47 No. 48 No. 49 No. 50 After crystallization Crystallization 795° C.- 795° C.- 780° C.- 780° C.- 780° C.- 780° C.- 780° C.- condition 3 h 3 h 3 h 3 h 3 h 3 h 3 h 890° C.- 890° C.- 890° C.- 890° C.- 890° C.- 890° C.- 890° C.- 1 h 1 h 1 h 1 h 1 h 1 h 1 h Transmittance 200 nm Not Not Not Not Not Not Not [%] measured measured measured measured measured measured measured 3 mm 250 nm Not Not Not Not Not Not Not thickness measured measured measured measured measured measured measured 300 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 325 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 350 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 380 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 800 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 1200 nm  Not Not Not Not Not Not Not measured measured measured measured measured measured measured L* Not Not Not Not Not Not Not measured measured measured measured measured measured measured a* Not Not Not Not Not Not Not measured measured measured measured measured measured measured b* Not Not Not Not Not Not Not measured measured measured measured measured measured measured Precipitated β-Q β-Q β-Q β-Q β-Q β-Q β-Q crystal Average Not Not Not Not Not Not Not crystallite measured measured measured measured measured measured measured size [nm] α[×10⁻⁷/° C.] 30-380° C. Not Not −1.5 −2.1 −1.0 −0.7 Not measured measured measured α[×10⁻⁷/° C.] 30-750° C. Not Not −0.8 −0.9 −0.1 0.1 Not measured measured measured Density Not Not 2.514 2.513 2.513 2.527 Not [g/cm3] measured measured measured Young's Not Not Not Not Not Not 93 Modulus measured measured measured measured measured measured [GPa] Modulus Not Not Not Not Not Not 38 of rigidity measured measured measured measured measured measured [GPa] Poisson's Not Not Not Not Not Not 0.22 ratio measured measured measured measured measured measured Appearance Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 250 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 300 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 325 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 350 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 380 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 800 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 1200 nm  Not Not Not Not Not Not Not measured measured measured measured measured measured measured

TABLE 15 No. 51 No. 52 No. 53 No. 54 No. 55 No. 56 No. 57 Composition SiO₂ 65.20 65.0 65.3 64.6 65.8 65.1 64.8 [wt %] Al₂O₃ 21.8 21.8 21.9 21.5 22.1 21.8 21.7 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 P₂O₅ 1.38 1.38 1.39 1.37 1.41 1.39 1.38 Li₂O 3.66 3.65 3.66 3.63 3.70 3.66 3.64 Na₂O 0.85 0.39 0.39 0.40 0.40 0.39 0.39 K₂O 0.30 0.99 0.28 0.29 0.00 0.30 0.30 MgO 0.68 0.68 0.95 0.65 1.23 0.68 0.67 CaO 0.001 0.001 0.001 0.001 0.001 0.001 0.001 SrO 0.00 0.00 0.00 0.00 0.002 0.002 0.002 BaO 1.16 1.15 1.19 2.64 1.23 1.21 1.2300 ZnO 0.001 0.001 0.001 0.001 0.00 0.00 0.00 TiO₂ 0.0092 0.0113 0.0321 0.0140 0.0029 0.0201 0.0140 SnO₂ 1.36 1.39 1.36 1.37 1.27 1.85 2.24 ZrO₂ 3.70 3.64 3.71 3.64 2.98 3.68 3.71 Fe₂O₃ 0.0080 0.0075 0.0083 0.0081 0.0082 0.0078 0.0084 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Composition Pt 0.41 0.01 0.20 0.11 0.05 0.09 0.07 [ppm] RF 0.00 0.01 0.02 0.02 0.02 0.02 0.02 Pt + Rh 0.41 0.02 0.22 0.13 0.07 0.11 0.09 Sn/(P + B + 0.211 0.216 0.210 0.214 0.224 0.267 0.305 Zr + Ti + Sn) Al/(Zr + Sn) 4.31 4.33 4.31 4.29 5.20 3.94 3.65 (Mg + Zn)/Li 0.186 0.187 0.260 0.179 0.332 0.186 0.184 Sn/(Zr + Sn) 0.27 0.28 0.27 0.27 0.30 0.33 0.38 (Si + Al)/Li 23.77 23.78 23.83 23.72 23.76 23.74 23.76 (Si + Al)/Sn 63.97 62.45 63.98 62.85 69.21 46.97 38.62 (Li + Na + K)/Zr 1.30 1.38 1.17 1.19 1.38 1.18 1.17 Ti/Zr 0.0025 0.0031 0.0086 0.0038 0.0010 0.0055 0.0038 Ti/(Ti + Fe) 0.535 0.501 0.795 0.633 0.261 0.720 0.625 Na + K + Ca + 2.31 2.53 1.86 3.33 1.63 1.90 1.92 Sr + Ba (Mg + Cu + 0.50 0.50 0.58 0.90 0.83 0.51 0.51 Sr +Ba)/Zr (Mg + Ca + 0.38 0.36 0.49 0.76 0.50 0.44 0.44 Sr + Ba)/(Li + Na + K) Sb + As 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Before crystallization Transmittance 200 nm Not 69.1 73.0 72.4 78.3 65.1 59.6 [%] measured 3 mm 250 nm Not 20.7 21.8 21.1 23.3 20.2 18.8 thickness measured 300 nm Not 27.9 32.3 27.9 30.6 22.8 17.7 measured 325 nm Not 65.9 70.3 65.9 68.0 62.9 58.6 measured 350 nm Not 83.9 85.6 84.0 84.8 83.2 82.0 measured 380 nm Not 89.3 89.8 89.4 89.7 89.0 88.6 measured 800 nm Not 91.4 91.6 91.5 91.5 91.4 91.3 measured 1200 nm  Not 91.2 91.6 91.4 91.8 91.7 91.7 measured L* Not 96.6 96.6 96.6 96.6 96.5 96.5 measured a* Not −0.1 −0.1 −0.1 0.0 −0.1 −0.1 measured b* Not 0.4 0.3 0.4 0.3 0.4 0.5 measured Low Strain point 674 674 678 680 Not Not Not temperature [° C.] measured measured measured viscosity Annealing point 733 733 736 739 Not Not Not [° C.] measured measured measured Glass 733 730 732 733 724 726 728 transition point [° C.] High 10{circumflex over ( )}4[° C.] 1346 1346 1341 1345 1343 1348 1345 temperature 10{circumflex over ( )}3[° C.] 1526 1524 1518 1523 1523 1527 1524 viscosity 10{circumflex over ( )}2.5[° C.]   1641 1639 1630 1630 1636 1639 1638 10{circumflex over ( )}2[° C.] 1778 1777 1762 1762 1768 1769 1773 Liquidus Not Not 1493 Not Not Not Not temperature measured measured measured measured measured measured (° C.) Liquidus Not Not 3.1 Not Not Not Not viscosity measured measured measured measured measured measured [—] α[×10⁻⁷/° C.] 30-380° C. 42.2 42.4 40.7 41.7 39.6 39.4 39.7 Density 2.463 2.462 2.465 2.484 2.450 2.463 2.469 [g/cm3] β —OH[/mm] 0.14 0.14 0.14 0.14 0.14 0.14 0.14

TABLE 16 No. 51 No. 52 No. 53 No. 54 No. 55 No. 56 No. 57 After crystallization Crystallization 855° C.- 855° C.- 840° C.- 840° C.- 765° C.- 810° C.- 810° C.- condition 3 h 3 h 3 h 3 h 3 h 3 h 3 h 920° C.- 920° C.- 920° C.- 920° C.- 890° C.- 920° C.- 920° C.- 1 h 1 h 1 h 1 h 1 h 1 h 1 h Transmittance 200 nm Not Not Not Not Not 36.9 37.7 [%] measured measured measured measured measured 3 mm 250 nm Not 20.1 14.5 16.1 Not 14.6 13.2 thickness measured measured 300 nm Not 18.1 17.7 17.9 20.4 14.4 11.2 measured 325 nm Not 41.4 54.9 52.6 58.8 52.5 49.6 measured 350 nm Not Not Not Not 75.8 72.8 73.8 measured measured measured measured 380 nm Not Not Not Not 81.5 79.3 80.8 measured measured measured measured 800 nm Not Not Not Not 90.4 90.4 90.4 measured measured measured measured 1200 nm  Not Not Not Not 90.9 90.9 91.1 measured measured measured measured L* Not Not Not Not 95.2 94.9 95.1 measured measured measured measured a* Not Not Not Not 0.1 0.1 0.1 measured measured measured measured b* Not Not Not Not 1.8 2.4 2.1 measured measured measured measured Precipitated β-Q β-Q β-Q β-Q β-Q β-Q β-Q crystal Average 47 Not Not Not Not Not Not crystallite measured measured measured measured measured measured size [nm] α[×10⁻⁷/° C.] 30-380° C. 1.4 2.5 0.9 1.4 1.1 −0.9 −1.0 α[×10⁻⁷/° C.] 30-750° C. 3.4 4.7 2.5 3.2 1.9 0.6 0.5 Density 2.525 2.519 2.539 2.549 2.534 2.542 2.548 [g/cm3] Young's Not Not Not Not Not Not Not Modulus measured measured measured measured measured measured measured [GPa] Modulus Not Not Not Not Not Not Not of rigidity measured measured measured measured measured measured measured [GPa] Poisson's Not Not Not Not Not Not Not ratio measured measured measured measured measured measured measured Appearance Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm Not Not Not Not Not 43.3 36.8 measured measured measured measured measured 250 nm Not 2.7 33.6 23.9 Not 27.7 29.9 measured measured 300 nm Not 35.0 45.2 35.9 33.4 36.8 36.6 measured 325 nm Not 37.1 21.9 20.2 13.6 16.6 15.3 measured 350 nm Not Not Not Not 10.6 12.4 10.0 measured measured measured measured 380 nm Not Not Not Not 9.1 11.0 8.8 measured measured measured measured 800 nm Not Not Not Not 1.2 1.2 1.0 measured measured measured measured 1200 nm  Not Not Not Not 1.0 0.9 0.6 measured measured measured measured

TABLE 17 No. 58 No. 59 No. 60 No. 61 Composition SiO₂ 65.20 64.9 64.5 64.6 [wt %] Al₂O₃ 22.5 22.4 22.5 22.6 B₂O₃ 0.00 0.00 0.00 0.00 P₂O₅ 1.38 1.38 1.89 1.37 Li₂O 3.66 3.81 3.66 3.63 Na₂O 0.85 0.39 0.49 0.40 K₂O 0.35 0.79 0.28 0.29 MgO 1.08 0.68 0.85 0.85 CaO 0.001 0.001 0.001 0.001 SrO 0.00 0.00 0.00 0.00 BaO 1.16 1.15 1.19 2.60 ZnO 0.001 0.82 0.50 0.001 TiO₂ 0.0092 0.0113 0.0321 0.0140 SnO₂ 1.13 1.11 1.52 1.10 ZrO₂ 2.58 2.55 2.49 2.57 Fe₂O₃ 0.0080 0.0075 0.0083 0.0081 Sb₂O₃ 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 Composition Pt 0.09 0.01 0.07 0.05 [ppm] Rh 0.02 0.01 0.02 0.02 Pt + Rh 0.11 0.02 0.09 0.07 Sn/(P + B + Zr + Ti + Sn) 0.222 0.220 0.256 0.218 Al/(Zr + S) 6.06 6.12 5.61 6.16 (Mg + Zn)/Li 0.295 0.394 0.369 0.234 Sn/(Zr + Sn) 0.30 0.30 0.38 0.30 (Si + Al)/Li 23.96 22.91 23.77 24.02 (Si + Al)/Sn 77.61 78.65 57.24 79.27 (Li + Na + K)/Zr 1.88 1.96 1.78 1.68 Ti/Zr 0.0036 0.0044 0.0129 0.0054 Ti/(Ti + Fe) 0.536 0.601 0.795 0.633 Na + K + Ca + Sr + Ba 2.36 2.33 1.96 3.29 (Mg + Ca + Sr + Ba)/Zr 0.87 0.72 0.82 1.34 (Mg + Ca + Sr + Ba)/(Li + Na + K) 0.46 0.37 0.46 0.80 Sb + As 0.00 0.00 0.00 0.00 Before crystallization Transmittance [%]  200 nm Not measured Not measured Not measured Not measured 3 mm thickness  250 nm Not measured Not measured Not measured Not measured  300 nm Not measured Not measured Not measured Not measured  325 nm Not measured Not measured Not measured Not measured  350 nm Not measured Not measured Not measured Not measured  380 nm Not measured Not measured Not measured Not measured  800 nm Not measured Not measured Not measured Not measured 1200 nm Not measured Not measured Not measured Not measured L* Not measured Not measured Not measured Not measured a* Not measured Not measured Not measured Not measured b* Not measured Not measured Not measured Not measured Low temperature Strain point [° C.] 671 673 672 678 viscosity Annealing point [° C.] 730 732 734 736 Glass transition point [° C.] Not measured Not measured Not measured Not measured High temperature 10{circumflex over ( )}4[° C.] Not measured Not measured Not measured Not measured viscosity 10{circumflex over ( )}3[° C.] Not measured Not measured Not measured Not measured 10{circumflex over ( )}2.5[° C.] Not measured Not measured Not measured Not measured 10{circumflex over ( )}2[° C.] Not measured Not measured Not measured Not measured Liquidus temperature (° C.) 1399 1390 1379 1402 Liquidus viscosity [—] Not measured Not measured Not measured Not measured α[×10⁻⁷/° C.] 30-380° C. 43.0 43.3 42.4 41.7 Density [g/cm3] Not measured Not measured Not measured Not measured β-OH[/mm] 0.13 0.13 0.13 0.13

TABLE 18 No. 58 No. 59 No. 60 No. 61 After crystallization Crystallization condition 840° C.-5 h 855° C.-7 h 840° C.-3 h   840° C.-8 h 920° C.-1 h 920° C.-1 h 920° C.-1.5 h 920° C.-1 h Transmittance [%]  200 nm Not measured Not measured Not measured Not measured 3 mm thickness  250 nm Not measured Not measured Not measured Not measured  300 nm Not measured Not measured Not measured Not measured  325 nm Not measured Not measured Not measured Not measured  350 nm Not measured Not measured Not measured Not measured  380 nm Not measured Not measured Not measured Not measured  800 nm Not measured Not measured Not measured Not measured 1200 nm Not measured Not measured Not measured Not measured L* Not measured Not measured Not measured Not measured a* Not measured Not measured Not measured Not measured b* Not measured Not measured Not measured Not measured Precipitated crystal β-Q β-Q β-Q β-Q Average crystallite size [nm] Not measured Not measured Not measured Not measured α[×10⁻⁷/° C.] 30-380° C. Not measured Not measured Not measured Not measured α[×10⁻⁷/° C.] 30-750° C. Not measured Not measured Not measured Not measured Density [g/cm3] Not measured Not measured Not measured Not measured Young's Modulus [GPa] Not measured Not measured Not measured Not measured Modulus of rigidity [GPa] Not measured Not measured Not measured Not measured Poisson's ratio Not measured Not measured Not measured Not measured Appearance Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm Not measured Not measured Not measured Not measured 250 nm Not measured Not measured Not measured Not measured 300 nm Not measured Not measured Not measured Not measured 325 nm Not measured Not measured Not measured Not measured 350 nm Not measured Not measured Not measured Not measured 380 nm Not measured Not measured Not measured Not measured 800 nm Not measured Not measured Not measured Not measured 1200 nm  Not measured Not measured Not measured Not measured

TABLE 19 No. 62 No. 63 No. 64 No. 65 No 66 No. 67 No. 68 Composition SiO₂ 64.50 67.4 67.3 67.0 64.5 64.4 64.5 [wt %] Al₂O₃ 24.2 22.1 22.3 22.2 25.1 23.7 23.7 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 P₂O₅ 1.44 1.31 1.30 1.29 1.31 2.22 2.22 Li₂O 4.02 3.68 3.70 3.68 3.68 3.68 3.68 Na₂O 0.38 0.50 0.50 0.35 0.33 0.90 0.35 K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 MgO 1.34 1.23 1.14 1.22 1.22 1.22 1.22 CaO 0.018 0.017 0.018 0.014 0.015 0.014 0.014 SrO 0.00 0.00 0.00 0.00 0.00 0.00 0.00 BaO 0.00 0.00 0.00 0.58 0.00 0.00 0.58 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.0100 0.0100 0.0100 0.0100 0.0100 0.0100 0.0100 SnO₂ 1.23 1.12 1.08 1.07 1.13 1.14 1.13 ZrO₂ 2.88 2.65 2.66 2.60 2.62 2.62 2.61 Fe₂O₃ 0.0060 0.0060 0.0060 0.0040 0.0060 0.0060 0.0040 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Composition Pt 1.50 1.50 1.50 1.50 1.50 1.50 1.50 [ppm] RF 0.02 0.02 0.02 0.02 0.02 0.02 0.02 Pt + Rh 1.52 1.52 1.52 1.52 1.52 1.52 1.52 Sn/(P + B + 0.221 0.220 0.214 0.215 0.223 0.190 0.189 Zr + Ti + Sn) Al/(Zr + Sn) 5.89 5.86 5.96 6.05 6.69 6.30 6.34 (Mg + Zn)/Li 0.333 0.334 0.308 0.332 0.332 0.332 0.332 Sn/(Zr + Sn) 0.30 0.30 0.29 0.29 0.30 0.30 0.30 (Si + Al)/Li 22.06 24.32 24.22 24.24 24.35 23.94 23.97 (Si + Al)/Sn 72.11 79.91 82.96 83.36 79.29 77.28 78.05 (Li + Na + K)/Zr 1.53 1.58 1.58 1.55 1.53 1.75 1.54 Ti/Zr 0.0035 0.0038 0.0038 0.0038 0.0038 0.0038 0.0038 Ti/(Ti + Fe) 0.625 0.625 0.625 0.714 0.625 0.625 0.714 Na + K + Ca + 1.74 1.75 1.66 2.16 1.57 2.13 2.16 Sr + Ba (Mg + Cu + 0.47 0.47 0.44 0.70 0.47 0.47 0.70 Sr +Ba)/Zr (Mg + Ca + 0.31 0.30 0.28 0.45 0.31 0.27 0.45 Sr + Ba)/(Li + Na + K) Sb + As 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Before crystallization Transmittance 200 nm Not Not Not 78.7 78.7 77.2 81.2 [%] measured measured measured 3 mm 250 nm Not Not Not 23.6 23.0 23.0 23.9 thickness measured measured measured 300 nm Not Not Not 38.7 33.6 35.8 37.1 measured measured measured 325 nm Not Not Not 72.5 69.1 71.0 72.9 measured measured measured 350 nm Not Not Not 85.1 83.9 84.9 85.7 measured measured measured 380 nm Not Not Not 89.0 88.6 89.2 89.4 measured measured measured 800 nm Not Not Not 91.4 91.1 91.4 91.5 measured measured measured 1200 nm  Not Not Not 91.6 91.1 91.3 91.6 measured measured measured L* 96.6 96.6 96.7 96.4 96.3 96.5 96.5 a* 0.0 0.0 0.0 0.0 0.0 0.0 0.0 b* 0.4 0.3 0.3 0.5 0.5 0.4 0.4 Low Strain point Not Not Not Not Not Not Not temperature [° C.] measured measured measured measured measured measured measured viscosity Annealing point Not Not Not Not Not Not Not [° C.] measured measured measured measured measured measured measured Glass Not Not Not 741 738 732 736 transition measured measured measured point [° C.] High 10{circumflex over ( )}4[° C.] Not Not Not 1352 1325 1330 1334 temperature measured measured measured viscosity 10{circumflex over ( )}3[° C.] Not Not Not 1534 1500 1508 1512 measured measured measured 10{circumflex over ( )}2.5[° C.]   Not Not Not 1650 1611 1619 1622 measured measured measured 10{circumflex over ( )}2[° C.] Not Not Not 1793 1743 1749 1751 measured measured measured Liquidus Not Not Not Not Not Not Not temperature measured measured measured measured measured measured measured (° C.) Liquidus Not Not Not Not Not Not Not viscosity measured measured measured measured measured measured measured [—] α[×10⁻⁷/° C.] 30-380° C. Not Not Not 38.8 38.0 40.9 38.3 measured measured measured Density 2.447 2.425 2.425 2.437 2.447 2.438 2.446 [g/cm3] β —OH[/mm] 0.13 0.17 0.09 0.11 0.12 0.12 0.21

TABLE 20 No. 62 No. 63 No. 64 No. 65 No. 66 No. 67 No. 68 After crystallization Crystallization 780° C.- 780° C.- 780° C.- 780° C.- 810° C.- 780° C.- 780° C.- condition 3 h 3 h 3 h 3 h 3 h 3 h 3 h 890° C.- 890° C.- 920° C.- 890° C.- 890° C.- 920° C.- 920° C.- 1 h 1 h 1 h 1 h 1 h 1 h 1 h Transmittance 200 nm Not Not Not Not Not 49.8 Not [%] measured measured measured measured measured measured 3 mm 250 nm Not Not Not Not Not 20.8 Not thickness measured measured measured measured measured measured 300 nm Not Not Not Not Not 19.6 Not measured measured measured measured measured measured 325 nm Not Not Not Not Not 40.5 Not measured measured measured measured measured measured 350 nm Not Not Not Not Not 52.8 Not measured measured measured measured measured measured 380 nm Not Not Not Not Not 60.6 Not measured measured measured measured measured measured 800 nm Not Not Not Not Not 88.3 Not measured measured measured measured measured measured 1200 nm  Not Not Not Not Not 90.4 Not measured measured measured measured measured measured L* Not Not Not Not Not 94.5 Not measured measured measured measured measured measured a* Not Not Not Not Not 0.4 Not measured measured measured measured measured measured b* Not Not Not Not Not 6.8 Not measured measured measured measured measured measured Precipitated β-Q β-Q β-Q β-Q β-Q β-Q β-Q crystal Average Not Not Not Not Not Not Not crystallite measured measured measured measured measured measured measured size [nm] α[×10⁻⁷/° C.] 30-380° C. −1.5 −1.1 −2.1 Not Not Not Not measured measured measured measured α[×10⁻⁷/° C.] 30-750° C. −0.3 −0.3 −1.4 Not Not Not Not measured measured measured measured Density 2.514 2.507 2.508 2.519 2.514 2.499 2.520 [g/cm3] Young's Not Not Not Not Not Not Not Modulus measured measured measured measured measured measured measured [GPa] Modulus Not Not Not Not Not Not Not of rigidity measured measured measured measured measured measured measured [GPa] Poisson's Not Not Not Not Not Not Not ratio measured measured measured measured measured measured measured Appearance Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm Not Not Not Not Not 35.4 Not measured measured measured measured measured measured 250 nm Not Not Not Not Not 9.4 Not measured measured measured measured measured measured 300 nm Not Not Not Not Not 45.2 Not measured measured measured measured measured measured 325 nm Not Not Not Not Not 43.0 Not measured measured measured measured measured measured 350 nm Not Not Not Not Not 37.8 Not measured measured measured measured measured measured 380 nm Not Not Not Not Not 32.1 Not measured measured measured measured measured measured 800 nm Not Not Not Not Not 3.3 Not measured measured measured measured measured measured 1200 nm  Not Not Not Not Not 1.1 Not measured measured measured measured measured measured

TABLE 21 No. 69 No. 70 No. 71 No. 72 No. 73 No. 74 No. 75 Composition SiO₂ 64.50 64.6 64.5 65.9 67.2 67.5 64.7 [wt %] Al₂O₃ 23.7 24.6 24.6 22.2 22.2 22.2 23.6 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 P₂O₅ 2.23 1.91 2.84 1.31 0.00 0.00 1.31 Li₂O 3.68 3.68 3.68 3.68 3.68 3.68 3.68 Na₂O 0.34 0.35 0.35 0.33 0.33 0.07 0.08 K₂O 0.58 0.00 0.00 0.00 0.00 0.00 0.00 MgO 1.23 1.22 0.37 2.83 2.83 2.83 2.84 CaO 0.014 0.014 0.009 0.024 0.023 0.023 0.024 SrO 0.00 0.00 0.00 0.00 0.00 0.00 0.00 BaO 0.00 0.00 0.00 0.00 0.00 0.00 0.00 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.0100 0.0100 0.0100 0.0100 0.0100 0.0100 0.0100 SnO₂ 1.17 1.13 1.15 1.17 1.17 1.15 1.17 ZrO₂ 2.59 2.60 2.61 2.60 2.60 2.59 2.61 Fe₂O₃ 0.0040 0.0050 0.0050 0.0050 0.0050 0.0050 0.0050 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Composition Pt 1.50 1.50 1.50 1.50 1.50 1.50 1.50 [ppm] RF 0.02 0.02 0.02 0.02 0.02 0.02 0.02 Pt + Rh 1.52 1.52 1.52 1.52 1.52 1.52 1.52 Sn/(P + B + 0.195 0.200 0.17 0.230 0.310 0.307 0.229 Zr + Ti + Sn) Al/(Zr + Sn) 6.30 6.60 6.54 6.89 5.89 5.94 6.24 (Mg + Zn)/Li 0.334 0.332 0.101 0.769 0.769 0.769 0.772 Sn/(Zr + Sn) 0.31 0.30 0.31 0.31 0.31 0.31 0.31 (Si + Al)/Li 23.97 24.24 24.21 23.94 24.29 24.38 23.99 (Si + Al)/Sn 75.38 78.94 77.48 75.30 76.41 78.00 75.47 (Li + Na + K)/Zr 1.78 1.55 1.54 1.54 1.54 1.45 1.44 Ti/Zr 0.0039 0.0038 0.0038 0.0038 0.0038 0.0039 0.0038 Ti/(Ti + Fe) 0.714 0.667 0.667 0.667 0.667 0.667 0.667 Na + K + Ca + 2.16 1.58 0.73 3.18 3.18 2.92 2.94 Sr + Ba (Mg + Cu + 0.48 0.47 0.15 1.10 1.10 1.10 1.10 Sr +Ba)/Zr (Mg + Ca + 0.27 0.31 0.09 0.71 0.71 0.76 0.76 Sr + Ba)/(Li + Na + K) Sb + As 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Before crystallization Transmittance 200 nm 72.4 73.9 82.2 76.4 75.4 77.1 76.6 [%] 250 nm 23.1 23.5 24.1 23.7 23.4 24.0 23.8 3 mm 300 nm 38.6 37.1 34.5 37.2 35.7 34.5 36.2 thickness 325 nm 73.8 73.5 71.9 72.0 70.7 70.1 71.0 350 nm 86.5 86.6 86.1 85.2 84.8 84.5 84.6 380 nm 90.0 90.1 89.9 89.1 89.2 88.7 88.7 800 nm 91.6 91.7 91.7 91.1 91.3 90.9 90.9 1200 nm  91.8 91.7 91.8 91.4 91.4 91.2 91.1 L* 96.6 96.7 96.6 96.3 96.5 96.3 96.2 a* 0.0 0.0 0.0 0.0 0.1 0.0 0.0 b* 0.3 0.3 0.3 0.4 0.4 0.5 0.5 Low Strain point Not Not Not Not Not Not Not temperature [° C.] measured measured measured measured measured measured measured viscosity Annealing point Not Not Not Not Not Not Not [° C.] measured measured measured measured measured measured measured Glass 732 739 750 Not Not Not Not transition measured measured measured measured point [° C.] High 10{circumflex over ( )}4[° C.] 1334 1327 1350 Not 1309 Not Not temperature measured measured measured viscosity 10{circumflex over ( )}3[° C.] 1512 1502 1528 Not 1488 Not Not measured measured measured 10{circumflex over ( )}2.5[° C.]   1624 1612 1639 Not 1602 Not Not measured measured measured 10{circumflex over ( )}2[° C.] 1756 1741 1770 Not 1739 Not Not measured measured measured Liquidus Not Not Not Not Not Not Not temperature measured measured measured measured measured measured measured (° C.) Liquidus Not Not Not Not Not Not Not viscosity measured measured measured measured measured measured measured [—] α[×10⁻⁷/° C.] 30-380° C. 40.5 38.2 37.4 Not Not Not Not measured measured measured measured Density 2.437 2.442 2.423 2.450 2.451 2.450 2.458 [g/cm3] β —OH[/mm] 0.23 0.29 0.05 0.18 0.40 0.71 0.94

TABLE 22 No. 69 No. 70 No. 71 No. 72 No. 73 No. 74 No. 75 After crystallization Crystallization 780° C.- 780° C.- 810° C.- 810° C.- 780° C.- 780° C.- 810° C.- condition 3 h 3 h 3 h 3 h 3 h 3 h 3 h 920° C.- 920° C.- 890° C.- 890° C.- 920° C.- 860° C.- 920° C.- 1 h 1 h 1 h 1 h 1 h 1 h 1 h Transmittance 200 nm 48.6 Not 73.0 Not Not Not Not [%] measured measured measured measured measured 3 mm 250 nm 20.1 Not 30.3 Not Not Not Not thickness measured measured measured measured measured 300 nm 21.6 Not 20.1 Not Not Not Not measured measured measured measured measured 325 nm 45.6 Not 32.0 Not Not Not Not measured measured measured measured measured 350 nm 58.1 Not 42.3 Not Not Not Not measured measured measured measured measured 380 nm 65.2 Not 48.6 Not Not Not Not measured measured measured measured measured 800 nm 88.7 Not 76.6 Not Not Not Not measured measured measured measured measured 1200 nm  90.7 Not 86.6 Not Not Not Not measured measured measured measured measured L* 92.5 Not 83.3 Not Not Not Not measured measured measured measured measured a* −0.2 Not 1.4 Not Not Not Not measured measured measured measured measured b* 5.6 Not 7.1 Not Not Not Not measured measured measured measured measured Precipitated β-Q β-Q β-Q β-Q β-Q β-Q β-Q crystal Average Not Not Not Not Not Not Not crystallite measured measured measured measured measured measured measured size [nm] α[×10⁻⁷/° C.] 30-380° C. Not Not Not Not Not Not Not measured measured measured measured measured measured measured α[×10⁻⁷/° C.] 30-750° C. Not Not Not Not Not Not Not measured measured measured measured measured measured measured Density 2.498 2.522 2.499 2.514 2.526 2.519 2.510 [g/cm3] Young's Not Not Not Not Not Not Not Modulus measured measured measured measured measured measured measured [GPa] Modulus Not Not Not Not Not Not Not of rigidity measured measured measured measured measured measured measured [GPa] Poisson's Not Not Not Not Not Not Not ratio measured measured measured measured measured measured measured Appearance Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm Not Not Not Not Not 35.4 Not measured measured measured measured measured measured 250 nm Not Not Not Not Not 9.4 Not measured measured measured measured measured measured 300 nm Not Not Not Not Not 45.2 Not measured measured measured measured measured measured 325 nm Not Not Not Not Not 43.0 Not measured measured measured measured measured measured 350 nm Not Not Not Not Not 37.8 Not measured measured measured measured measured measured 380 nm Not Not Not Not Not 32.1 Not measured measured measured measured measured measured 800 nm Not Not Not Not Not 3.3 Not measured measured measured measured measured measured 1200 nm  Not Not Not Not Not 1.1 Not measured measured measured measured measured measured

TABLE 23 No. 76 No. 77 No. 78 No. 79 No. 80 No. 81 No. 82 Composition SiO₂ 64.30 64.4 64.4 64.5 67.4 68.1 58.5 [wt %] Al₂O₃ 23.7 23.6 23.7 24.5 22.2 22.2 22.2 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 P₂O₅ 1.81 1.31 0.81 1.30 1.35 0.81 0.40 Li₂O 3.68 3.68 3.68 3.68 3.65 3.66 3.68 Na₂O 0.36 0.36 0.36 0.35 0.35 0.35 0.35 K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 MgO 1.23 1.22 1.22 1.23 1.22 1.23 1.23 CaO 0.014 0.014 0.014 0.020 0.019 0.020 0.020 SrO 0.00 0.00 0.00 0.00 0.00 0.00 0.00 BaO 0.98 1.46 1.95 0.00 0.00 0.00 0.00 ZnO 0.000 0.000 0.000 0.000 0.00 0.00 0.00 TiO₂ 0.0100 0.0100 0.0100 0.0100 0.0100 0.0100 0.0100 SnO₂ 1.14 1.15 1.19 1.12 1.15 1.13 1.15 ZrO₂ 2.61 2.62 2.60 2.61 2.76 2.58 2.56 Fe₂O₃ 0.0050 0.0050 0.0040 0.0050 0.0040 0.0040 0.0050 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Composition Pt 1.50 1.50 1.50 1.50 1.50 1.50 1.50 [ppm] RF 0.02 0.02 0.02 0.02 0.02 0.02 0.02 Pt + Rh 1.52 1.52 1.52 1.52 1.52 1.52 1.52 Sn/(P + B + 0.205 0.226 0.258 0.222 0.218 0.249 0.279 Zr + Ti + Sn) Al/(Zr + Sn) 6.32 6.26 6.25 6.57 5.68 5.98 5.98 (Mg + Zn)/Li 0.334 0.332 0.332 0.334 0.334 0.336 0.334 Sn/(Zr + Sn) 0.30 0.31 0.31 0.30 0.29 0.30 0.31 (Si + Al)/Li 23.91 23.91 23.94 24.18 24.55 24.67 24.65 (Si + Al)/Sn 77.19 76.52 74.03 79.46 77.91 79.91 78.87 (Li + Na + K)/Zr 1.55 1.54 1.55 1.54 1.45 1.55 1.57 Ti/Zr 0.0038 0.0038 0.0038 0.0038 0.0036 0.0039 0.0039 Ti/(Ti + Fe) 0.667 0.667 0.714 0.667 0.714 0.714 0.667 Na + K + Ca + 2.58 3.05 3.54 1.60 1.59 1.60 1.60 Sr + Ba (Mg + Cu + 0.85 1.03 1.22 0.48 0.45 0.48 0.49 Sr +Ba)/Zr (Mg + Ca + 0.55 0.67 0.79 0.31 0.31 0.31 0.31 Sr + Ba)/(Li + Na + K) Sb + As 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Before crystallization Transmittance 200 nm 80.8 74.6 74.7 84.9 83.4 83.7 81.2 [%] 250 nm 23.5 23.1 23.1 24.5 24.1 24.4 23.9 3 mm 300 nm 38.5 37.3 35.9 37.2 36.2 37.0 34.6 thickness 325 nm 73.7 72.9 72.3 72.6 71.8 73.2 71.4 350 nm 86.4 86.1 85.9 85.7 85.5 86.4 85.7 380 nm 90.0 89.9 89.8 89.6 89.6 90.2 89.8 800 nm 91.7 91.7 91.6 91.5 91.7 91.8 91.6 1200 nm  91.6 91.7 91.6 91.5 91.6 91.7 91.6 L* 96.5 96.6 96.5 96.5 96.6 96.7 96.6 a* −0.1 −0.1 −0.1 0.0 0.0 0.0 0.0 b* 0.3 0.4 0.4 0.4 0.4 0.3 0.3 Low Strain point Not Not Not Not Not Not Not temperature [° C.] measured measured measured measured measured measured measured viscosity Annealing point Not Not Not Not Not Not Not [° C.] measured measured measured measured measured measured measured Glass Not Not Not Not 738 Not Not transition measured measured measured measured measured measured point [° C.] High 10{circumflex over ( )}4[° C.] Not Not Not Not 1354 1353 Not temperature measured measured measured measured measured viscosity 10{circumflex over ( )}3[° C.] Not Not Not Not 1538 1536 Not measured measured measured measured measured 10{circumflex over ( )}2.5[° C.]   Not Not Not Not 1652 1653 Not measured measured measured measured measured 10{circumflex over ( )}2[° C.] Not Not Not Not 1782 1792 Not measured measured measured measured measured Liquidus Not Not Not Not 1416 1399 1413 temperature measured measured measured measured (° C.) Liquidus Not Not Not Not 3.6 3.7 Not viscosity measured measured measured measured measured [—] α[×10⁻⁷/° C.] 30-380° C. Not Not Not Not 38.8 Not Not measured measured measured measured measured measured Density 2.455 2.464 2.476 2.454 2.428 2.427 2.427 [g/cm3] β —OH[/mm] 0.65 0.30 0.26 0.44 0.03 0.50 0.20

TABLE 24 No. 76 No. 77 No. 78 No. 79 No. 80 No. 81 No. 82 After crystallization Crystallization 780° C.- 810° C.- 765° C.- 780° C.- 780° C.- 780° C.- 780° C.- condition 3 h 3 h 3 h 3 h 3 h 3 h 3 h 860° C.- 920° C.- 860° C.- 890° C.- 890° C.- 890° C.- 890° C.- 1 h 1 h 1 h 1 h 1 h 1 h 1 h Transmittance 200 nm Not Not Not Not Not Not Not [%] measured measured measured measured measured measured measured 3 mm 250 nm Not Not Not Not Not Not Not thickness measured measured measured measured measured measured measured 300 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 325 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 350 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 380 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 800 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 1200 nm  Not Not Not Not Not Not Not measured measured measured measured measured measured measured L* Not Not Not Not Not Not Not measured measured measured measured measured measured measured a* Not Not Not Not Not Not Not measured measured measured measured measured measured measured b* Not Not Not Not Not Not Not measured measured measured measured measured measured measured Precipitated β-Q β-Q β-Q β-Q β-Q β-Q β-Q crystal Average Not Not Not Not Not Not Not crystallite measured measured measured measured measured measured measured size [nm] α[×10⁻⁷/° C.] 30-380° C. Not Not Not Not Not Not −2.5 measured measured measured measured measured measured α[×10⁻⁷/° C.] 30-750° C. Not Not Not Not Not Not −1.8 measured measured measured measured measured measured Density 2.519 2.510 2.530 2.530 2636 2.520 2.515 [g/cm3] Young's Not Not Not Not Not Not Not Modulus measured measured measured measured measured measured measured [GPa] Modulus Not Not Not Not Not Not Not of rigidity measured measured measured measured measured measured measured [GPa] Poisson's Not Not Not Not Not Not Not ratio measured measured measured measured measured measured measured Appearance Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 250 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 300 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 325 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 350 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 380 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 800 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 1200 nm  Not Not Not Not Not Not Not measured measured measured measured measured measured measured

TABLE 25 No. 83 No. 84 No. 85 No. 86 No. 87 No. 88 No. 89 Composition SiO₂ 68.9 65.7 66.1 66.5 65.2 67.9 67.9 [wt %] Al₂O₃ 22.2 24.5 24.5 24.5 24.5 22.3 22.3 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 P₂O₅ 0.00 0.81 0.40 0.00 1.31 0.40 0.40 Li₂O 3.68 3.68 3.68 3.68 3.68 3.68 3.68 Na₂O 0.35 0.36 0.35 0.36 0.39 0.67 0.67 K₂O 0.00 0.00 0.00 0.00 0.00 0.01 0.01 MgO 1.22 1.22 1.23 1.23 1.23 1.25 1.25 CaO 0.020 0.020 0.020 0.020 0.020 0.024 0.024 SrO 0.00 0.00 0.00 0.00 0.00 0.00 0.00 BaO 0.00 0.00 0.00 0.00 0.00 0.00 0.00 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.0100 0.0100 0.0100 0.0100 0.0100 0.0080 0.0200 SnO₂ 1.17 1.16 1.18 1.14 1.11 1.13 1.13 ZrO₂ 2.56 2.59 2.59 2.58 2.59 2.62 2.62 Fe₂O₃ 0.0050 0.0050 0.0050 0.0050 0.0050 0.0050 0.0090 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Composition Pt 1.50 1.50 1.50 1.50 1.50 1.50 0.02 [ppm] RF 0.02 0.02 0.02 0.02 0.02 0.02 0.01 Pt + Rh 1.52 1.52 1.52 1.52 1.52 1.52 0.03 Sn/(P + B + 0.313 0.254 0.282 0.306 0.221 0.272 0.271 Zr + Ti + Sn) Al/(Zr + Sn) 5.95 6.53 6.50 6.59 6.62 5.95 5.95 (Mg + Zn)/Li 0.332 0.332 0.334 0.334 0.334 0.340 0.340 Sn/(Zr + Sn) 0.31 0.31 0.31 0.31 0.30 0.30 0.30 (Si + Al)/Li 24.76 24.51 24.62 24.73 24.38 24.51 24.51 (Si + Al)/Sn 77.86 77.76 76.78 79.82 80.81 79.82 79.82 (Li + Na + K)/Zr 1.57 1.56 1.56 1.57 1.57 1.66 1.66 Ti/Zr 0.0039 0.0039 0.0039 0.0039 0.0039 0.0031 0.0076 Ti/(Ti + Fe) 0.667 0.667 0.667 0.667 0.667 0.615 0.690 Na + K + Ca + 1.59 1.60 1.60 1.61 1.64 1.95 1.95 Sr + Ba (Mg + Cu + 0.48 0.48 0.48 0.48 0.48 0.49 0.49 Sr +Ba)/Zr (Mg + Ca + 0.31 0.31 0.31 0.31 0.31 0.29 0.29 Sr + Ba)/(Li + Na + K) Sb + As 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Before crystallization Transmittance 200 nm 76.7 77.3 77.4 76.6 79.5 83.6 71.9 [%] 250 nm 23.4 23.6 23.7 23.6 24.0 24.1 20.9 3 mm 300 nm 34.1 35.2 35.5 35.8 37.5 37.6 28.5 thickness 325 nm 71.5 72.2 72.5 72.2 73.2 73.3 66.0 350 nm 85.9 86.1 86.2 86.1 86.4 86.5 84.0 380 nm 90.0 90.0 90.0 90.1 90.1 90.3 89.7 800 nm 91.7 91.7 91.7 91.6 91.7 91.8 91.5 1200 nm  91.6 91.6 91.6 91.6 91.6 91.9 91.3 L* 96.7 96.6 96.6 96.7 96.7 96.7 96.7 a* 0.0 0.0 0.0 0.0 −0.1 0.0 −0.1 b* 0.3 0.3 0.3 0.3 0.3 0.3 0.3 Low Strain point Not Not Not Not Not 678 Not temperature [° C.] measured measured measured measured measured measured viscosity Annealing point Not Not Not Not Not 737 Not [° C.] measured measured measured measured measured measured Glass Not Not Not Not Not 738 Not transition measured measured measured measured measured measured point [° C.] High 10{circumflex over ( )}4[° C.] Not Not 1331 Not Not 1354 Not temperature measured measured measured measured measured viscosity 10{circumflex over ( )}3[° C.] Not Not 1506 Not Not 1538 Not measured measured measured measured measured 10{circumflex over ( )}2.5[° C.]   Not Not 1616 Not Not 1654 Not measured measured measured measured measured 10{circumflex over ( )}2[° C.] Not Not 1744 Not Not 1793 Not measured measured measured measured measured Liquidus 1419 Not Not 1441 Not 1407 Not temperature measured measured (mullite) measured measured (° C.) Liquidus Not Not Not Not Not 3.7 Not viscosity measured measured measured measured measured measured [—] α[×10⁻⁷/° C.] 30-380° C. Not Not Not Not Not 39.6 Not measured measured measured measured measured measured Density 2.428 2.442 2.443 2.444 2.441 2.429 2.429 [g/cm3] β —OH[/mm] 0.83 0.07 0.15 0.18 0.22 0.12 0.54

TABLE 26 No. 83 No. 84 No. 85 No. 86 No. 87 No. 88 No. 89 After crystallization Crystallization 780° C.- 780° C.- 780° C.- 780° C.- 780° C.- 780° C.- 780° C.- condition 3 h 3 h 3 h 3 h 3 h 3 h 3 h 890° C.- 890° C.- 890° C.- 890° C.- 890° C.- 890° C.- 890° C.- 1 h 1 h 1 h 1 h 1 h 1 h 1 h Transmittance 200 nm Not Not Not Not Not Not Not [%] measured measured measured measured measured measured measured 3 mm 250 nm Not Not Not Not Not Not Not thickness measured measured measured measured measured measured measured 300 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 325 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 350 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 380 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 800 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 1200 nm  Not Not Not Not Not Not Not measured measured measured measured measured measured measured L* Not Not Not Not Not Not Not measured measured measured measured measured measured measured a* Not Not Not Not Not Not Not measured measured measured measured measured measured measured b* Not Not Not Not Not Not Not measured measured measured measured measured measured measured Precipitated β-Q β-Q β-Q β-Q β-Q β-Q β-Q crystal Average Not Not Not Not Not Not Not crystallite measured measured measured measured measured measured measured size [nm] α[×10⁻⁷/° C.] 30-380° C. −3.1 Not Not Not Not Not Not measured measured measured measured measured measured α[×10⁻⁷/° C.] 30-750° C. −2.2 Not Not Not Not Not Not measured measured measured measured measured measured Density 2.512 2.514 2.515 2.516 2.517 2.516 2.524 [g/cm3] Young's Not Not Not Not Not Not Not Modulus measured measured measured measured measured measured measured [GPa] Modulus Not Not Not Not Not Not Not of rigidity measured measured measured measured measured measured measured [GPa] Poisson's Not Not Not Not Not Not Not ratio measured measured measured measured measured measured measured Appearance Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 250 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 300 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 325 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 350 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 380 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 800 nm Not Not Not Not Not Not Not measured measured measured measured measured measured measured 1200 nm  Not Not Not Not Not Not Not measured measured measured measured measured measured measured

TABLE 27 No. 90 No. 91 No. 92 No. 93 No. 94 No. 95 Composition SiO₂ 67.90 67.9 67.9 67.8 68.5 68.2 [wt %] Al₂O₃ 22.3 22.3 22.3 22.5 21.9 22.0 B₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 P₂O₅ 0.40 0.40 0.40 0.40 0.40 0.45 Li₂O 3.68 3.68 3.68 3.68 3.68 3.68 Na₂O 0.67 0.67 0.67 0.58 0.58 0.68 K₂O 0.01 0.01 0.01 0.00 0.00 0.02 MgO 1.25 1.25 1.25 1.23 1.22 1.24 CaO 0.024 0.024 0.024 0.020 0.019 0.054 SrO 0.00 0.00 0.00 0.00 0.00 0.00 BaO 0.00 0.00 0.00 0.00 0.00 0.06 ZnO 0.00 0.00 0.00 0.00 0.00 0.00 TiO₂ 0.0200 0.0200 0.0200 0.0100 0.0100 0.1200 SnO₂ 1.13 1.13 1.13 1.18 1.18 1.04 ZrO₂ 2.62 2.62 2.62 2.60 2.58 2.51 Fe₂O₃ 0.0090 0.0090 0.0090 0.0050 0.0040 0.0140 Sb₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 As₂O₃ 0.00 0.00 0.00 0.00 0.00 0.00 Composition Pt 0.02 0.02 0.02 1.50 1.50 1.50 [ppm] RF 0.01 0.01 0.01 0.02 0.02 0.02 Pt + Rh 0.03 0.03 0.03 1.52 1.52 1.52 Sn/(P + B + 0.271 0.271 0.271 0.282 0.283 0.252 Zr + Ti + Sn) Al/(Zr + Sn) 5.95 5.95 5.95 5.95 5.82 6.20 (Mg + Zn)/Li 0.340 0.340 0.340 0.334 0.332 0.337 Sn/(Zr + Sn) 0.30 0.30 0.30 0.31 0.31 0.29 (Si + Al)/Li 24.51 24.51 24.51 24.54 24.57 24.51 (Si + Al)/Sn 79.82 79.82 79.82 76.53 76.61 86.73 (Li + Na + K)/Zr 1.66 1.66 1.66 1.64 1.65 1.74 Ti/Zr 0.0076 0.0076 0.0076 0.0038 0.0039 0.0478 Ti/(Ti + Fe) 0.690 0.690 0.690 0.667 0.714 0.896 Na + K + Ca + 1.95 1.95 1.95 1.83 1.82 2.05 Sr + Ba (Mg + Cu + 0.49 0.49 0.49 0.48 0.48 0.54 Sr +Ba)/Zr (Mg + Ca + 0.29 0.29 0.29 0.29 0.29 0.31 Sr + Ba)/(Li + Na + K) Sb + As 0.00 0.00 0.00 0.00 0.00 0.00 Before crystallization Transmittance 200 nm 71.9 71.9 71.9 84.1 86.3 Not [%] measured 3 mm 250 am 20.9 20.9 20.9 24.2 24.4 Not thickness measured 300 nm 28.5 28.5 28.5 36.5 37.4 Not measured 325 nm 66.0 66.0 66.0 72.7 73.6 Not measured 350 nm 84.0 84.0 84.0 86.2 86.7 Not measured 380 nm 89.7 89.7 89.7 90.2 90.3 Not measured 800 nm 91.5 91.5 91.5 91.6 91.8 Not measured 1200 nm  91.3 91.3 91.3 91.7 91.9 Not measured L* 96.7 96.7 96.7 96.7 96.7 96.6 a* −0.1 −0.1 −0.1 0.0 −0.1 −0.1 b* 0.3 0.3 0.3 0.3 0.3 0.4 Low Strain point Not Not Not Not Not Not temperature [° C.] measured measured measured measured measured measured viscosity Annealing point Not Not Not Not Not Not [° C.] measured measured measured measured measured measured Glass Not Not Not Not Not 733 transition measured measured measured measured measured point [° C.] High 10{circumflex over ( )}4[° C.] Not Not Not Not Not 1357 temperature measured measured measured measured measured viscosity 10{circumflex over ( )}3[° C.] Not Not Not Not Not 1542 measured measured measured measured measured 10{circumflex over ( )}2.5[° C.]   Not Not Not Not Not 1656 measured measured measured measured measured 10{circumflex over ( )}2[° C.] Not Not Not Not Not 1788 measured measured measured measured measured Liquidus Not Not Not Not Not 1400 temperature measured measured measured measured measured (° C.) Liquidus Not Not Not Not Not 3.8 viscosity measured measured measured measured measured [—] α[×10⁻⁷/° C.] 30-380° C. Not Not Not Not Not 39.2 measured measured measured measured measured Density 2.429 2.429 2.429 2.432 2.428 2.425 [g/cm3] β —OH[/mm] 0.28 0.16 0.19 0.25 0.32 0.47

TABLE 28 No. 90 No. 91 No. 92 No. 93 No. 94 No. 95 After crystallization Crystallization 780° C.- 780° C.- 780° C.- 780° C.- 810° C.- 780° C.- condition 3 h 3 h 3 h 1.5 h 0.75 h 3 h 890° C.- 890° C.- 890° C.- 920° C.- 920° C.- 890° C.- 1 h 1 h 0.25 h 0.5 h 0.25 h 1 h Transmittance 200 nm 30.9 33 35.2 35 40 37.8 [%] 250 nm 14.8 11.9 13.1 12.8 13 15.1 3 mm 300 nm 24.2 16.8 18.7 17.5 14.1 22.5 thickness 325 nm 63.5 59.4 59.4 54.8 51.7 61.2 350 nm 78.3 79 77.8 73 72.9 76.6 380 nm 83.4 86 85.1 81 82.3 82.0 800 nm 90.9 91 91.2 91 90.9 90.6 1200 nm  91.3 91 90.6 91 90.2 91.1 L* 95.6 96.2 96.1 95.56 95.7 95.3 a* 0.1 0.0 −0.1 −0.15 0.0 0.1 b* 1.5 0.8 1.0 1.82 1.5 1.8 Precipitated β-Q β-Q β-Q β-Q β-Q β-Q crystal Average 41 Not Not Not Not Not crystallite measured measured measured measured measured size [nm] α[×10⁻⁷/° C.] 30-380° C. −1.3 Not Not Not Not Not measured measured measured measured measured α[×10⁻⁷/° C.] 30-750° C. −0.2 Not Not Not Not Not measured measured measured measured measured Density 2.508 2.508 2.504 2.505 2.511 2.508 [g/cm3] Young's Not Not Not Not Not Not Modulus measured measured measured measured measured measured [GPa] Modulus Not Not Not Not Not Not of rigidity measured measured measured measured measured measured [GPa] Poisson's Not Not Not Not Not Not ratio measured measured measured measured measured measured Appearance Colorless and Colorless and Colorless and Colorless and Colorless and Colorless and transparent transparent transparent transparent transparent transparent Rate of change before and after crystallization [%] 200 nm 63.1 53.9 51.0 51.5 43.7 55.1 250 nm 38.7 43.2 37.6 38.9 36.1 37.7 300 nm 35.6 40.9 34.3 38.4 50.4 38.2 325 nm 13.4 10.0 10.0 17.0 21.7 15.8 350 nm 9.4 6.2 7.4 13.2 13.3 11.2 380 nm 7.6 3.9 5.1 9.5 8.2 9.1 800 nm 0.9 0.2 0.3 0.7 0.6 1.1 1200 nm  0.6 0.5 0.7 0.7 1.2 0.7

TABLE 29 No. 96 No. 97 No. 98 No. 99 Composition SiO₂ 67.3 67.3 67.2 65.7 [wt %] Al₂O₃ 22.3 22.3 22.3 22.2 B₂O₃ 0.00 0.00 0.00 0 P₂O₃ 0.40 0.40 0.40 1.4 Li₂O 3.68 3.68 3.68 3.7 NaO 0.67 0.67 0.67 0.4 K₂O 0.01 0.01 0.01 0.3 MgO 1.25 1.25 1.25 0.7 CaO 0.024 0.024 0.024 0 SrO 0.00 0.00 0.00 0 BaO 0.00 0.00 0.00 1.2 ZnO 0.00 0.00 0.00 0 TiO₂ 0.0080 0.0080 0.0080 2 SnO₂ 1.13 1.13 1.13 0.2 ZrO₂ 2.62 2.62 2.62 2.2 Fe₂O₃ 0.0050 0.0050 0.0050 0.015 Sb₂O₃ 0.65 0.00 0.30 0 As₂O₃ 0.00 0.65 0.38 0 Composition Pt 1.50 1.50 1.50 0.05 [ppm] Rh 0.02 0.02 0.02 0.05 Pt + Rh 1.52 1.52 1.52 0.1 Sn/(P + B + Zr + Ti + Sn) 0.272 0.272 0.272 0.034 Al/(Zr + Sn) 5.95 5.95 5.95 9.250 (Mg + Zn)/Li 0.340 0.340 0.340 0.189 Sn/(Zr + Sm) 0.30 0.30 0.30 0.08 (Si + Al)/Li 24.33 24.33 24.33 23.76 (Si + Al)/Sn 79.25 79.25 79.22 439.50 (Li + Na + K)/Zr 1.66 1.66 1.66 2.00 Ti/Zr 0.0031 0.0031 0.0031 0.909 Ti/(Ti + Fe) 0.615 0.615 0.615 0.993 Na + K + Ca + Sr + Ba 1.95 1.95 1.95 4.8 (Mg + Ca + Sr + Ba)/Zr 0.49 0.49 0.49 0.86 (Mg + Ca + Sr + Ba)/(Li + Na + K) 0.29 0.29 0.29 0.43 Sb + As 0.65 0.65 0.68 0 Before crystallization Transmittance  200 nm Not measured Not measured Not measured Not measured [%] 3 mm  250 nm Not measured Not measured Not measured Not measured thickness  300 nm Not measured Not measured Not measured Not measured  325 nm Not measured Not measured Not measured Not measured  350 nm Not measured Not measured Not measured Not measured  380 nm Not measured Not measured Not measured Not measured  800 nm Not measured Not measured Not measured Not measured 1200 nm Not measured Not measured Not measured Not measured L* Not measured Not measured Not measured Not measured a* Not measured Not measured Not measured Not measured b* Not measured Not measured Not measured Not measured Low temperature Strain point [° C.] Not measured Not measured Not measured Not measured viscosity Annealing point [° C.] Not measured Not measured Not measured Not measured Glass transition point [° C.] Not measured Not measured Not measured Not measured High 10{circumflex over ( )}4[° C.] Not measured Not measured Not measured Not measured temperature 10{circumflex over ( )}3[° C.] Not measured Not measured Not measured Not measured viscosity 10{circumflex over ( )}2.5[° C.] Not measured Not measured Not measured Not measured 10{circumflex over ( )}2[° C.] Not measured Not measured Not measured Not measured Liquidus temperature (° C.) Not measured Not measured Not measured Not measured Liquidus viscosity [—] Not measured Not measured Not measured Not measured α[×10⁻⁷/° C.] 30-380° C. Not measured Not measured Not measured Not measured Density [g/cm3] Not measured Not measured Not measured Not measured β-OH[/mm] 0.001 1.12 0.69 Not measured

TABLE 30 No. 96 No. 97 No. 98 No. 99 After crystallization Crystallization condition 780° C.-3 h 780° C.-3 h 780° C.-3 h 780° C.-3 h 890° C.-1 h 890° C.-1 h 890° C.-1 h 890° C.-1 h Transmittance  200 nm Not measured Not measured Not measured Not measured [%] 3 mm  250 nm Not measured Not measured Not measured Not measured thickness  300 nm Not measured Not measured Not measured Not measured  325 nm Not measured Not measured Not measured Not measured  350 nm Not measured Not measured Not measured Not measured  380 nm Not measured Not measured Not measured Not measured  800 nm Not measured Not measured Not measured Not measured 1200 nm Not measured Not measured Not measured Not measured L* Not measured Not measured Not measured 88.0  a* Not measured Not measured Not measured 0.0 b* Not measured Not measured Not measured 6.2 Precipitated crystal β-Q β-Q β-Q β-Q Average crystallite size [nm] Not measured Not measured Not measured Not measured α[×10⁻⁷/° C.] 30-380° C. Not measured Not measured Not measured Not measured α[×10⁻⁷/° C.] 30-750° C. Not measured Not measured Not measured Not measured Density [g/cm3] Not measured Not measured Not measured Not measured Young's Modulus [GPa] Not measured Not measured Not measured Not measured Modulus of rigidity [GPa] Not measured Not measured Not measured Not measured Poisson's ratio Not measured Not measured Not measured Not measured Appearance Colorless and Colorless and Colorless and Yellow transparent transparent transparent Rate of change before and after crystallization [%] 200 nm Not measured Not measured Not measured Not measured 250 nm Not measured Not measured Not measured Not measured 300 nm Not measured Not measured Not measured Not measured 325 nm Not measured Not measured Not measured Not measured 350 nm Not measured Not measured Not measured Not measured 380 nm Not measured Not measured Not measured Not measured 800 nm Not measured Not measured Not measured Not measured 1200 nm  Not measured Not measured Not measured Not measured Manufacture and Evaluation of Li₂O—Al₂O₃—SiO₂-Based Crystallized Glass Sheet

Firstly, in order that the glass has the composition shown in each table, each raw material was mixed in the form of an oxide, a hydroxide, a carbonate, a nitrates, and the like to obtain a glass batch (composition shown in each table is an analytical value of an actually-prepared glass). The obtained glass batch was placed in a crucible containing platinum and rhodium, a strengthened platinum crucible containing no rhodium, a refractory crucible, or a quartz crucible, the glass batch was melted at 1600° C. for 4 to 100 hours, and then, the temperature was raised to 1650 to 1680° C. to melt the glass batch for 0.5 to 20 hours, the melted glass batch was formed into a roll having a thickness of 5 mm, the resultant glass roll was further subject to heat treatment at 700° C. for 30 minutes using an annealing furnace, and the temperature of the annealing furnace was decreased to room temperature at 100° C./h to obtain a crystallizable glass. Note that the melting was performed by an electro-melting method used broadly for the development of glass materials.

The contents of Pt and Rh of the sample were analyzed using ICP-MS equipment (Agilent 8800 manufactured by Agilent Technologies, Inc.). Firstly, after the produced glass sample was pulverized and wetted with pure water, perchloric acid, nitric acid, sulfuric acid, hydrofluoric acid, and the like were added, and the sample was melted. Thereafter, the contents of Pt and Rh of the sample were measured by ICP-MS. Based on a calibration curve prepared by using solutions containing Pt and Rh at known concentrations, which were prepared in advance, the contents of Pt and Rh of each measurement sample were evaluated. The measurement mode was He gas/HMI (low mode) for Pt and HEHe gas/HMI (medium mode) for Rh, and the mass numbers were 198 for Pt and 103 for Rh. Note that the content of Li₂O of the prepared sample was analyzed by using an atomic absorption spectrometer (ContrAA600, manufactured by Analytik Jena GmbH). Including a flow of melting the glass sample and the use of calibration curves, the analysis was performed basically in much the same way as in the analysis of Pt and Rh. The contents of other components were measured by using ICP-MS or atomic absorption spectrometry in much the same way as Pt, Rh, Li₂O, or by creating a calibration curve on an XRF analyzer (ZSX Primus IV manufactured by Rigaku Corporation) by using, as a calibration curve sample, a glass sample with a known concentration determined in advance using ICP-MS or an atomic absorption spectrometer, and, based on the calibration curve, evaluating an actual content of each component from an XRF analysis value of the measurement sample. During the XRF analysis, a tube voltage, a tube current, an exposure time, and the like were adjusted in accordance with the components to be analyzed.

The crystallizable glass described in each table was subjected to heat treatment for nucleation at from 750 to 900° C. for 0.75 to 60 hours, and then, a heat treatment at from 800 to 1000° C. for 0.25 to 3 hours was further performed for crystallization. Thereafter, heat treatment was performed at 700° C. for 30 minutes, and the temperature was decreased to room temperature by 100° C./h. The obtained crystallized glass was evaluated in terms of transmittance, diffuse transmittance, lightness, chromaticity, precipitated crystal, average crystallite size, thermal expansion coefficient, density, Young's modulus, modulus of rigidity, Poisson's ratio, and appearance. For the crystallizable glass before crystallization, the transmittance, the lightness, the chromaticity, and the like were measured in much the same way as in the crystallized glass. The crystallizable glass was further evaluated in terms of a β-OH value, a viscosity, and a liquidus temperature.

The transmittance, the lightness, and the chromaticity were evaluated by measurement by using a spectrophotometer for a crystallized glass sheet with both surfaces being optically polished to have 3 mm thick. A spectrophotometer V-670 manufactured by JASCO Corporation was used for the measurement. Note that V-670 is attached with “ISN-723”, which is an integrating sphere unit, and the transmittance measured corresponds to a total light transmittance. A measurement wavelength range was set from 200 to 1500 nm, a scan speed was set to 200 nm/min, a sampling pitch was set to 1 nm, a bandwidth was set to 5 nm for a wavelength range from 200 to 800 nm, and was set to 20 nm for other wavelength ranges. Baseline correction (100% adjustment) and dark measurement (0% adjustment) were performed before the measurement. During the dark measurement, a barium sulfate plate that came along with ISN-723 was removed. The measured transmittance was used to calculate tristimulus values XYZ according to JISZ8781-42013 and the corresponding international standards, and the lightness and the chromaticity were calculated from each stimulus value (light source C/10°). When the diffuse transmittance of the crystallized glass was measured, the same model as above was used, and the sample to be measured was placed and the measurement was performed while a barium sulfate plate that came along with ISN-723 was removed.

The precipitated crystal was evaluated by using an X-ray diffractometer (fully automatic multi-purpose horizontal X-ray diffractometer Smart Lab, manufactured by Rigaku Corporation). The scanning mode was set to 2θ/θ measurement, scan type was continuous scan, scattering and divergence slit width were 10, light receiving slit width was 0.2°, a measuring range was from 10 to 60°, a measurement step was 0.1°, a scanning speed was 5°/min, and an analysis software packaged with the instrument was used to evaluate a main crystal and a crystal grain size. As a precipitation crystal seed identified as the main crystal, a β-quartz solid solution is indicated in the table as “0-Q”. The average crystallite size of the main crystals was calculated by using the measured X-ray diffraction peak, based on the ebeye-Scherrer method. Note that in the measurement for calculating the average crystallite size, the scanning speed was set to 1°/min.

The thermal expansion coefficient was evaluated by using a crystallized glass sample processed to have a length of 20 mm and a diameter of 3.8 mm, and as an average linear thermal expansion coefficient measured in the temperature ranges from 30 to 380° C. and from 30 to 750° C. A Dilatometer manufactured by NETZSCH was used for the measurement. Further, the same measuring instrument was used to measure the thermal expansion curve for the temperature range from 30 to 750° C. and the inflection point of the curve was calculated to evaluate the glass transition point of the crystallizable glass before crystallization.

The Young's modulus, the modulus of rigidity, and the Poisson's ratio was measured at room temperature by using a plate-shaped sample (40 mm×20 mm×20 mm) whose surface was polished with a polishing liquid in which 1200 mesh alumina powder was dispersed, and by using a free resonance type elastic modulus measuring device (JE-RT3 manufactured by Nihon Techno-Plus Co. Ltd.)

The density was evaluated by an Archimedes's method.

The strain point and the annealing point were evaluated by a fiber elongation method. Note that a fiber sample was prepared by subjecting the crystallizable glass to hand-drawing.

An FT-IR Frontier (PerkinElmer Inc.) was used to measure the transmittance of the glass to evaluate the β-OH value according to the following formula. Note that the scanning speed was set to 100 μm/min, and the sampling pitch was set to 1 cm⁻¹, and the number of times of scans was set to 10 times per measurement.

β-OH value=(1/X)log 10(T ₁ /T ₂)

-   -   X: Glass thickness (mm)     -   T₁: Transmittance (%) at a reference wavelength of 3846 cm⁻¹     -   T₂: Minimum transmittance (%) near an absorption wavelength of         hydroxyl groups of 3600 cm⁻¹

The high temperature viscosity was evaluated by a platinum ball pulling-up method. For the evaluation, a lumpy glass sample was crushed into appropriate sizes, and fed into an alumina crucible while inclusion of air bubbles was avoided as much as possible. Then, the alumina crucible was heated to melt the sample, and the viscosity of the glass was measured at a plurality of temperatures. The constant of the Vogel-Fulcher equation was calculated, a viscosity curve was created, and the temperature at each viscosity was calculated.

The liquidus temperature was evaluated by the following method. Firstly, a platinum boat of about 120×20×10 mm was filled with a glass powder having a uniform size from 300 to 500 micrometers, placed in an electric furnace, and melted at 1600° C. for 30 minutes. Thereafter, the platinum boat was placed in an electric furnace having a linear temperature gradient, left to stand for 20 hours, and the devitrification was precipitated. After air cooling of the measurement sample to room temperature, the devitrification precipitated at an interface between the platinum boat and the glass was observed. A temperature of a part where devitrification was precipitated was calculated from a temperature gradient graph of the electric furnace, and was recorded as the liquidus temperature. The obtained liquidus temperature was interpolated into a high-temperature viscosity curve of the glass, and the viscosity corresponding to the liquidus temperature was recorded as the liquidus viscosity. Note that it was found from results of X-ray diffraction, composition analysis, and the like (scanning electron microscope S3400N TyPE2 manufactured by Hitachi, Ltd., and EMAX ENERGY EX250X manufactured by HORIBA, Ltd.) that a primary phase of the glasses listed in each table was mainly ZrO₂.

Appearance was evaluated by visually observing the color tone of the crystallized glass. Note that the visual observation was performed on a white background and a black background under indoor light and sunlight, respectively (performed at 8:00, 12:00, and 16:00 on clear and cloudy days in January, April, July, and October). The color tone was determined comprehensively from each visual result.

Manufacture and Evaluation of Glass Article

Firstly, 29.9 parts by mass of a silicone resin (resin solid content), 35.2 parts by mass of a white TiO₂ powder pigment (average particle size: 0.2 μm), and 11.7 parts by mass of talc (average particle size: 20 μm) as an extender pigment were mixed, and 23.2 parts by mass of an organic solvent was added to the mixture to produce a paste. Next, onto the entire surface of the thus-produced Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet, the paste was applied by using screen printing so as to have a thickness of 10 μm. Thereafter, the paste was dried for 10 minutes at 70° C., and then subjected to firing for 15 minutes at 320° C. to form a white colored layer. As a result, a glass article was obtained.

The resultant glass articles were evaluated in terms of color tone. For Sample Nos. 1 to 98, which were Examples, white color equivalent to the color of the colored layer were obtained. In contrast, for Sample No. 99, which was Comparative Example, more yellowish color than the color of the colored layer was observed and the color tone of the colored layer was impaired.

FIG. 2 shows measurement results of reflection chromaticity, for a glass article prepared by forming a white colored layer on Sample No. 89 (3 mm thick), and a glass article prepared by forming a white colored layer on an existing Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet commercially available in the top plate market (3 mm thick, with chromaticity b* of greater than 5 as measured by the method described above) (the reflection chromaticity was measured using CM-600d manufactured by Konica Minolta, Inc.). As is obvious from FIG. 2 , there was no difference in reflection chromaticity between Sample No. 89 and the colored layer, and, for Sample No. 89, the color tone equivalent to that of the colored layer could be observed. In contrast, there was a significant difference in reflection chromaticity between the existing Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet and the colored layer, and, for that existing crystallized glass sheet, the color tone equivalent to that of the colored layer could not be observed. Note that the effects of the present invention were also confirmed for the colored layers in red, pink, blue, silver, and green, for example.

REFERENCE SIGNS LIST

-   -   1. Glass article     -   2. Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet     -   2 a. Cooking surface     -   2 b. Back surface     -   3. Colored layer 

1: A glass article comprising: a Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet having lightness L* of 70 or greater, chromaticity a* of within 5, and chromaticity b* of within ±5 at a thickness of 3 mm; and a colored layer formed on a back surface of the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet. 2: The glass article according to claim 1, wherein the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet includes, in mass %, SiO₂ from 40 to 90%, Al₂O₃ from 5 to 30%, Li₂O from 1 to 10%, TiO₂ 0 to less than 2%, SnO₂ from 0 to 20%, ZrO₂ from 1 to 20%, MgO from 0 to 10%, P₂O₅ from 0 to 10%, and Sb₂O₃+As₂O₃ from 0 to less than 2%. 3: The glass article according to claim 1, wherein appearance of the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet is colorless and transparent. 4: The glass article according to claim 1, wherein the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet has a transmittance of 10% or greater at a thickness of 3 mm and a wavelength of 300 nm. 5: The glass article according to claim 1, wherein the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet has a thermal expansion coefficient of 30×10⁻⁷/° C. or less at 30 to 380° C. 6: The glass article according to claim 1, wherein the Li₂O—Al₂O₃—SiO₂-based crystallized glass sheet has a thermal expansion coefficient of 30×10⁻⁷/° C. or less at 30 to 750° C. 7: A top plate for a cooker comprising the glass article according to claim
 1. 